Volume 2012 (2012), Article ID 574321, 9 pages
Inhibitory Mechanism of Carbon Steel Corrosion in Sea Water by an Aqueous Extract of Henna Leaves
1PG and Research Department of Chemistry, GTN Arts College, Tamil Nadu, Dindigul 624005, India
2Department of Chemistry, RVS School of Engineering and Technology, Dindigul 624005, India
3Department of Chemistry, Shanmuganathan Engineering College, Arasampatti 622507, India
Received 19 September 2012; Accepted 27 October 2012
Academic Editors: A. A. Franco and E. Stupnisek-Lisac
Copyright © 2012 V. Johnsirani et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.
The inhibition efficiency (IE) of an aqueous extract of henna leaves in controlling corrosion of carbon steel in seawater has been evaluated by weight-loss method. The weight loss study reveals that the formulation consisting of 8 mL of henna extract (HE) and 25 ppm of Zn2+ has 94% inhibition efficiency in controlling corrosion of carbon steel in sea water. Polarization study reveals that HE and Zn2+ system functions as mixed type inhibitor. AC impedance spectra reveal that protective film is formed on the metal surface. The nature of the metal surface has been analysed by FTIR spectra, SEM, and AFM analysis.
Sea water is one of the most corroded and most abundant naturally occurring electrolytes. The corrosive behaviour of seawater is reflected by the fact that most of the common structural metals and alloys are attacked by this liquid or its surrounding environments. The sea water environments can be divided into five zones, namely, subsoil, continuously submerged, tidal, splash zone above high tidal, and atmospheric zone . The corrosion behaviour of metals and alloys differs from one zone to another. In splash zone the stainless steels have usually satisfactory performance while the carbon and low alloy steels do not. Anderson and Ross had found that the austenitic grades performed much better than martensitic and ferritic grades . The Ni, Cu, and P alloyed steels were found to be much more resistant than carbon steel in splash zone . Also, it was found that Mn, P, and Al had measurable influence on corrosion rates of low carbon steels under tidal exposure. After 5-year exposure test, it was found that the rate of attack in splash zone was much higher than the atmospheric and deep submerged zones .
Metals and alloys are often exposed to the action of acids and alkalis in industrial processes thereby prompting their deterioration . One of the most effective means of protecting metals and alloys surfaces from corrosion in acid and alkaline environments is the use of corrosion inhibitors . Corrosion inhibitors are usually added to the acid/alkaline solution to reduce the metal loss. Recently, studies on the use of drugs have been reported by several researchers [7, 8]. Some of these corrosion inhibitors are, however, toxic to the environment. This has prompted the search for green corrosion inhibitors that are nontoxic and ecofriendly for metals and alloys in acidic and alkaline solutions . These green corrosion inhibitors have been found to have centre for -electrons and functional groups (such as –C=C–, –OR, –OH, –NR2, –NH2, and –SR) which provide electrons that facilitate the adsorption of the inhibitor on the metal/alloy surface.
Before the 1960s, inorganic inhibitors such as zinc, chromate, polyphosphate, and nitrites were used as inhibitors. However, discharge of such material has become unacceptable due to environmental hazards . The recent trend is towards environmental friendly inhibitors. Increasing awareness of health and ecological risk has drawn attention to finding more suitable inhibitors, which are nontoxic. Accordingly, greater research efforts have been directed towards formulating environmentally acceptable inhibitors. The extracts from plant leaves, roots, and seeds have been studied and found to be cheap, environmental friendly, and good corrosion inhibitors. The plant leave extracts studied include Opuntia extract , Carica papaya (CP) and Azadirachta indica (AI) , Vernonia amygdalina , Telfairia occidentalis , Phyllanthus amarus , fenugreek leaves , olive leaves , Euphorbia hirta, and Dialium guineense . The roots studied include ginseng root , Beet root extract , Kopsia singaporensis extract , and Murraya koenighii . The present work is undertaken.(1)To evaluate the inhibition efficiency (IE) of henna extract (HE)- system in controlling corrosion of carbon steel immersed in sea water in the absence and presence of by weight-loss method.(2)To study the mechanism of corrosion inhibition by polarization study and AC impedance spectra.(3)To analyse the protective film by FTIR spectra, scanning electron microscope (SEM), and atomic force microscope.(4)To propose the mechanism of corrosion inhibition based on the above results.
2.1. Preparation of Plant Extract
The leaves of henna were dried and ground to powder and 10 gm of the powdered leaves weighed and boiled with double-distilled water, filtering the suspending impurities and making up to 100 mL. The extract was used as corrosion inhibitor in the present study.
2.2. Preparation of the Specimens
Carbon steel specimens (0.026% S, 0.06% P, 0.4% Mn, 0.1% C and rest iron) of the dimensions 1.0 × 4.0 × 0.2 cm were polished to a mirror finish, degreased with trichloroethylene, and used for the weight-loss method and surface examination studies.
2.3. Weight-Loss Method
2.3.1. Determination of Surface Area of the Specimens
The length, breadth, and the thickness of carbon steel specimens and the radius of the holes were determined with the help of vernier calipers of high precision, and the surface areas of the specimens were calculated.
2.3.2. Weighing the Specimens before and after Corrosion
All the weighing of the carbon steel specimens before and after corrosion was carried out using Shimadzu Balance-AY62.
2.3.3. Determination of Corrosion Rate
The weighed specimens in triplicate were suspended by means of glass hooks in 100 mL beakers containing 100 mL various test solutions, and after 24 hours of immersion, the specimens were taken out, washed in running water, dried, and weighed. From the change in weights of the specimens, corrosion rates were calculated using the following relationship: where = weight-loss in milligrams, = density of specimen g/cm3, = area of specimen in square cm, and = exposure time in hours.
Corrosion inhibition efficiency (IE) was then calculated using the equation where = corrosion rate in the absence of inhibitor and = corrosion rate in the presence of inhibitor.
2.4. Surface Examination Study
The carbon steel specimens were immersed in various test solutions for a period of one day. After one day, the specimens were taken out and dried. The nature of the film formed on the surface of metal specimen was analyzed by various surface analysis techniques.
2.5. Potentiodynamic Polarization
Polarization studies were carried out in a CHI electrochemical workstation with impedance model 660 A. It was provided with IR compensation facility. A three-electrode cell assembly was used. The working electrode was carbon steel. A SCE was the reference electrode. Platinum was the counter electrode. From polarization study, corrosion parameters such as corrosion potential (), corrosion current (), Tafel slopes anodic = , and cathodic = were calculated, and linear polarization study (LPR) was done. The scan rate () was 0.01. Hold time at () was zero and quiet time (s) was two.
2.6. AC Impedance Spectra
The instrument used for polarization study was used to record AC impedance spectra also. The cell set up was also the same. The real part () and imaginary part () of the cell impedance were measured in ohms at various frequencies. Values of charge transfer resistance () and the double layer capacitance () were calculated.
2.7. Fourier Transform Infrared Spectra
These spectra were recorded in a Perkin-Elmer-1600 spectrophotometer using KBr pellet. The FTIR spectrum of the protective film was recorded by carefully removing the film, mixing it with KBr and making the pellet.
2.8. Scanning Electron Microscopic Studies (SEM)
The carbon steel immersed in blank solution and in the inhibitor solution for a period of one day was removed, rinsed with double-distilled water, dried, and observed in a scanning electron microscope to examine the surface morphology. The surface morphology measurements of carbon steel were examined using JEOL MODEL6390 computer-controlled scanning electron microscope.
2.9. Atomic Force Microscopy Characterization (AFM)
The carbon steel specimens immersed in blank and in the inhibitor solution for a period of one day were removed, rinsed with double-distilled water, dried, and subjected to the surface examination. Atomic force microscopy (Veeco dinnova model) was used to observe the samples’ surface in tapping mode, using cantilever with linear tips. The scanning area in the images was 5 μm × 5 μm, and the scan rate was 0.6 HZ/second.
3. Results and Discussions
3.1. Weight-Loss Study
The physicochemical parameters of sea water are given in Table 1.
The calculated inhibition efficiencies (IEs) of henna extract in controlling the corrosion of carbon steel immersed in sea water both in the absence and presence of zinc ion have been tabulated in Table 2. The calculated values indicate the ability of henna extract to be a good corrosion inhibitor. The inhibition efficiency is found to be enhanced in the presence of zinc ion. The formulation consisting of 8 mL of HE and 25 ppm of offers 94% inhibition efficiency. This mixture of inhibitors shows better IE than the individual inhibitors .
3.1.1. Synergism Parameter ()
Synergism parameters are indications of synergistic effect existing between inhibitors [24, 25]. value is found to be greater than one indicating the synergistic effect existing between of concentrations 25 ppm and 50 ppm with various concentrations of HE. The results are given in Table 3.
In Table 3 synergism parameters were calculated using the relation where where = surface coverage of inhibitor (HE) and = surface coverage of inhibitor () and where
3.1.2. Analysis of Variance (-Test)
-test is used to investigate if the synergistic effect existing between two inhibitors is statistically significant or not [26, 27]. If -value is above 5.32 for 1, 8 degrees of freedom, the synergistic effect proves to be statistically significant. If it is below 5.32 for 1, 8 degrees of freedom indicating that it is statistically insignificant at a 0.05 level of significance. The results are given in Table 4.
The obtained -value 0.56 for 25 ppm is not statistically significant, since it is less than the critical -value 5.32 for 1, 8 degrees of freedom at 0.05 level of significance. Therefore it is concluded that the influence of 25 ppm on the inhibition efficiencies of various concentrations of HE is not statistically significant. The obtained -value 3.82 for 50 ppm is not statistically significant, since it is less than the critical -value 5.32 for 1, 8 degrees of freedom at 0.05 level of significance. Therefore it is concluded that the influence of 50 ppm on the inhibition efficiencies of various concentrations of HE is not statistically significant.
3.2. Analysis of Polarization Curves
Polarization study has been used to detect the formation of protective film on the metal surface. When a protective film is formed on the metal surface, the linear polarization resistance (LPR) increases and the corrosion current () decreases. The potentiodynamic polarization curves of carbon steel immersed in various test solutions are shown in Figure 1. The corrosion parameters, namely, corrosion potential (), Tafel slopes ( = cathodic; = anodic), linear polarization resistance (LPR), and corrosion current () are given in Table 5. When carbon steel is immersed in sea water, the corrosion potential is −816 mV versus SCE. The formulation consisting of 8 mL of HE solution and 25 ppm of shifts the corrosion potential to −808 mV versus SCE. The corrosion potential shift is very small. This suggests that the HE- formulation functions as a mixed inhibitor controlling the anodic reaction and cathodic reaction, to the same extent. The corrosion current value and LPR value for sea water are A/cm2 and ohm cm2. For the formulation of HE (8 mL) and (25 ppm), the corrosion current value is decreased to A/cm2, and the LPR value is increased to ohm cm2. This indicates that a protective film is formed on the metal surface. When a protective film is formed on the metal surface, LPR value increases and corrosion current value decreases .
3.3. Analysis of AC Impedance Spectra
AC impedance spectra have been studied to detect the formation of film on the metal surface. If a protective film is formed, the charge transfer resistance increases and double-layer capacitance value decreases [29, 30]. The AC impedance spectra of carbon steel immersed in various solutions are shown in Figure 2. The AC impedance parameters, namely, charge transfer resistance () and double-layer capacitance (), (derived from Nyquist plot) are given in Table 6.
The AC impedance parameters, namely, charge transfer resistance () and double-layer capacitance (), are given in Table 6. When carbon steel is immersed in sea water, value is 101.10 ohm cm2 and value is F/cm2. When HE and are added to sea water, value increases from 101.10 ohm cm2 to 123.68 ohm cm2 and the decreases from F/cm2 to F/cm2. This suggests that a protective film is formed on the surface of the metal. This is further supported by the increase in impedance value [log (z/ohm)] from 2.060 to 2.132 (Figure 3). This accounts for the very high IE of HE- system.
In electrochemical studies, instantaneous corrosion rate is measured. But in weight-loss method, corrosion rate is measured after a longer period in the present study after one day. After a longer period, the protective film becomes more compact and stable. This accounts for the discrepancy in IE, obtained from AC impedance spectra and from weight-loss method (Figure 4).
3.4. Analysis of FTIR Spectra
The active principle in an aqueous extract of henna extract is Lawsone. The red-orange colour of the extract is due to Lawsone (see Scheme 1).
A few drops of an aqueous extract of henna were dried on a glass plate. A solid mass was obtained. Its FTIR spectrum of pure HE is shown in Figure 5(a). The phenolic O–H stretch appeared at 3414 cm−1. The C=O stretching frequency appeared at 1632 cm−1. Thus Lawsone was characterized by IR spectroscopy 
The FTIR spectrum of the protective film formed on the metal after immersion in the sea water for one day containing 8 mL of HE and 25 ppm of is shown in Figure 5(b). It is found that the phenolic O–H stretch has shifted from 3414 cm−1 to 3415 cm−1. The C=O stretching frequency has shifted from 1632 cm−1 to 1613 cm−1. It was inferred that Lawsone has coordinate with through the phenolic oxygen, aromatic ring, and C=O group of the p-benzo quinone resulting in the formation of -Lawsone complex on the anodic sites of the metal surface. The band at 1362 cm−1 due to the Zn(OH)2 formed on the cathodic sites of the metal surface. Thus FTIR spectral study leads to the conclusion that the protective film consists of -Lawsone complex and Zn(OH)2 [32–35].
3.5. SEM Analysis of Metal Surface
The SEM images of magnification (×500) of carbon steel specimens immersed in sea water for one day in the absence and presence of inhibitor system are shown in Figure 6 image (b) and image (c), respectively.
The SEM micrographs of polished carbon steel surface (control) in Figure 6 image (a) show the smooth surface of the metal. This shows the absence of any corrosion products formed on the metal surface. The SEM micrographs of carbon steel surface immersed in sea water in Figure 6 image (b) show the roughness of the metal surface which indicates the corrosion of carbon steel in sea water. Figure 6 image (c) indicates that in presence of 8 mL of HE- (25 ppm) mixture in sea water, the surface coverage increases which in turn results in the formation of insoluble complex on the surface of the metal (HE- inhibitor complex), and the surface is covered by a thin layer of inhibitors which control the dissolution of carbon steel. Such results have been earlier .
3.6. Atomic Force Microscopy Characterization
AFM is a powerful technique to investigate the surface morphology at nano- to microscale and has become a new choice to study the influence of inhibitor on the generation and the progress of the corrosion at the metal/solution interface [36–38]. The three-dimensional (3D) AFM morphologies and the AFM cross-sectional profile for polished carbon steel surface (reference sample), carbon steel surface immersed in sea water (blank sample), and carbon steel surface immersed in sea water containing the formulation of 8 mL of HE and 25 ppm of are shown in Figure 7 images (a, d, g), (b, e, h), (c, f, i), respectively.
3.6.1. Root Mean Square Roughness, Average and Roughness and Peak-to-Valley Value
AFM image analysis is performed to obtain the average roughness, (the average deviation of all points roughness profile from a mean line over the evaluation length), root-mean-square roughness, (the average of the measured height deviations taken within the evolution length and measured from the mean line), and the maximum peak-to-valley (p-v) height values (largest single peak-to-valley height in five adjoining sampling heights) . Table 7 is a summary of (), (), (P-V) value for carbon steel surface immersed in different environment.
Figure 7 (a, d, g) displays the surface topography of uncorroded metal surface. The values of , , and p-v height for the polished carbon steel surface (reference sample) are 4.3 nm, 3.4 nm, and 35.28 nm, respectively. The slight roughness observed on the polished carbon steel surface is due to atmospheric corrosion.
Figure 7 (b, e, h) displays the corroded metal surface with few pits in the absence of the inhibitor immersed in sea water. The (), (), (p-v) height values for the carbon steel surface are 17.10 nm, 13.58 nm, and 92.28 nm, respectively.
These data suggest that carbon steel surface immersed in sea water has a greater surface roughness than the polished metal surface, which shows that the unprotected carbon steel surface is rougher and is due to the corrosion of the carbon steel in sea water environment.
Figure 7 (c, f, i) displays the surface after immersion in sea water containing 8 mL of . The (), () (p-v) height values for the carbon steel surface are 11.84 nm, 7.65 nm, and 27.47 nm, respectively. The (), () (p-v) height values are considerably less in the inhibited environment compared to the uninhibited environment. These parameters confirm that the surface is smoother. The smoothness of the surface is due to the formation of a compact protective film of -HE complex and Zn(oH)2 on the metal surface thereby inhibiting the corrosion of carbon steel .
3.7. Mechanism of Corrosion Inhibition
Weight-loss method reveals that the formulation consisting of 8 mL of HE and 25 ppm of offers 94% IE to carbon steel immersed in sea water. A synergistic effect exists between HE and . Polarization study reveals that HE- system functions as a mixed inhibitor. AC impedance spectra reveal that a protective film is formed on the metal surface. FTIR spectra reveal that the protective film consists of -Lawsone complex and Zn(OH)2.
In order to explain the Previous facts in a holistic way, the following mechanism of corrosion inhibition is proposed. When the formulation consisting of sea water, henna extract, and is prepared, there is formation of -Lawsone complex in solution.(i)When carbon steel is immersed in the solution, the -Lawsone complex diffuses from the bulk of the solution towards the metal surface.(ii)On the metal surface, -Lawsone complex is converted into -Lawsone complex. is released (iii)The released combines with OH− to form Zn(OH)2 on the cathodic sites: (iv)Thus the protective film consists of -Lawsone complex and Zn(OH)2. This accounts for the synergistic effect.
The present study leads to the following conclusions.(1)The formulation consisting of 8 mL HE and 25 ppm has 94% inhibition efficiency to carbon steel immersed in sea water.(2)Polarization study reveals that HE- system functions as a mixed inhibitor.(3)AC impedance spectra reveal that a protective film is formed on the metal surface.(4)FTIR spectra reveal that the protective film consists of -Lawsone complex and Zn(OH)2.
The authors are thankful to their respective management and Defence Research and Development Organisation, New Delhi.
- F. L. LaQue, Marine Corrosion and Prevention, John Wiley & Sons, New York, NY, USA, 1975.
- D. B. Anderson and R. W. Ross Jr., “Proection of steel pilling in marine splash and spray zone-Metallic sheathing concept,” pp. 461–473, Proceeding of the 4th International Congress on Marine Corrosion and Fouling, Juan-les-Pins, France, 1976.
- C. P. Larrabee, “Corrosion resistance of high strength low alloy steel as influenced by composition and environment,” Corrosion, vol. 9, pp. 259–371, 1953.
- A. A. Humbles, “The cathodic protection of steel in seawater,” Corrosion, September 1949.
- O. K. Abola and A. O. James, “The effects of Aloe vera extract on corrosion and kinetics of corrosion process of zinc in HCl solution,” Corrosion Science, vol. 52, no. 2, pp. 661–664, 2010.
- E. E. Ebenso, T. Arslan, F. Kandemirli, N. Caner, and I. Love, “Quantum chemical studies of some rhodanine azosulpha drugs as corrosion inhibitors for mild steel in acidic medium,” International Journal of Quantum Chemistry, vol. 110, no. 5, pp. 1003–1018, 2010.
- N. O. Eddy, U. J. Ibok, E. E. Ebenso, A. Nemr, and E. S. H. El Ashry, “Quantum chemical study of the inhibition of the corrosion of mild steel in H2SO4 by some antibiotics,” Journal of Molecular Modeling, vol. 15, no. 9, pp. 1085–1092, 2009.
- A. I. Onen, B. T. Nwufo, E. E. Ebenso, and R. M. Hlophe, “Titanium (IV) oxide as corrosion inhibitor for aluminium and mild steel in acidic medium,” International Journal of Electrochemical Science, vol. 5, pp. 1563–1573, 2010.
- E. E. Oguzie, “Corrosion inhibition of aluminium in acidic and alkaline media by Sansevieria trifasciata extract,” Corrosion Science, vol. 49, no. 3, pp. 1527–1539, 2007.
- A. Sharmila, A. A. Prema, and P. A. Sahayaraj, “Influence of Murraya koenigii (curry leaves) extract on the corrosion inhibition of carbon steel in HCL solution,” Rasayan Journal of Chemistry, vol. 3, no. 1, pp. 74–81, 2010.
- A. Y. El-Etre, “Inhibition of aluminum corrosion using Opuntia extract,” Corrosion Science, vol. 45, no. 11, pp. 2485–2495, 2003.
- E. E. Ebenso, U. J. Ibok, U. J. Ekpe et al., “Corrosion inhibition studies of some plant extracts on aluminium in acidic medium,” Transactions of the SAEST, vol. 39, no. 4, pp. 117–123, 2004.
- A. D. Odiongenyi, S. A. Odoemelam, and N. O. Eddy, “Corrosion inhibition and adsorption properties of ethanol extract of Vernonia amygdalina for the corrosion of mild steel in H2SO4,” Portugaliae Electrochimica Acta, vol. 27, no. 1, pp. 33–45, 2009.
- E. E. Oguzie, “Inhibition of acid corrosion of mild steel by Telfaria occidentalis extract,” Pigment and Resin Technology, vol. 34, no. 6, pp. 321–326, 2005.
- P. C. Okafor, M. E. Ikpi, I. E. Uwah, E. E. Ebenso, U. J. Ekpe, and S. A. Umoren, “Inhibitory action of Phyllanthus amarus extracts on the corrosion of mild steel in acidic media,” Corrosion Science, vol. 50, no. 8, pp. 2310–2317, 2008.
- E. A. Noor, “Temperature effects on the corrosion inhibition of mild steel in acidic solutions by aqueous extract of fenugreek leaves,” International Journal of Electrochemical Science, vol. 2, pp. 996–1017, 2007.
- A. Y. El-Etre, “Inhibition of acid corrosion of carbon steel using aqueous extract of olive leaves,” Journal of Colloid and Interface Science, vol. 314, no. 2, pp. 578–583, 2007.
- U. Anozie, C. S. Akoma, and L. A. Nnanna, “Corrosion inhibition of aluminium alloy in acidic medium by Euphorbia hirta and Dialum guineense extracts,” International Journal of Pure and Applied Sciences and Technology, vol. 6, no. 2, pp. 79–88, 2011.
- I. B. Obot and N. O. Obi-Egbedi, “Ginseng root: a new efficient and effective eco-friendly corrosion inhibitor for aluminium alloy of type AA 1060 in hydrochloric acid solution,” International Journal of Electrochemical Science, vol. 4, no. 9, pp. 1277–1288, 2009.
- S. J. Arockia, S. Rajendran, S. V. Ganga, A. J. Amalraj, and B. Naranyansamy, “Corrosion inhibition by beet root extract,” Portugaliae Electrochemica Acta, vol. 27, no. 1, pp. 1–11, 2009.
- P. B. Raja, A. A. Rahim, H. Osman, and K. Awang, “Inhibitory effect of Kopsia singapurensis extract on the corrosion behavior of mild steel in acid media,” Acta Physico-Chimica Sinica, vol. 26, no. 8, pp. 2171–2176, 2010.
- K. S. Beenakumari, “Inhibitory effects of Murraya koenigii (Curry leaf) leaf extracts on the corrosion of mild steel in 1 M Hcl,” Green Chemistry Letters and Reviews, vol. 4, no. 2, pp. 117–120, 2011.
- T. Umamathi, J. A. Selvi, S. A. Kanimozhi, S. Rajendran, and A. J. Amalraj, “Effect of Na3PO4 on the corrosion inhibition efficiency of EDTA—Zn2+ system for carbon steel in aqueous solution,” Indian Journal of Chemical Technology, vol. 15, no. 6, pp. 560–565, 2008.
- S. Rajendran, S. Shanmugapriya, T. Rajalakshmi, and A. J. A. Raj, “Corrosion inhibition by an aqueous extract of rhizome powder,” Corrosion, vol. 61, no. 7, pp. 685–692, 2005.
- K. Anuradha, R. Vimala, B. Narayanaswamy, J. A. Selvi, and S. Raji, “Corrosion inhibition of carbon steel in low chloride media by an aqueous extract of Hibiscus rosa-sinensis linn,” Chemical Engineering Communications, vol. 195, no. 3, pp. 352–366, 2008.
- S. Rajendran, A. Raji, J. A. Selvi, A. Rosaly, and S. Thangasamy, “Evaluation of gender bias in use of modular instruction and concepts of organic chemistry Nomenclature,” Journals of Material Education, vol. 29, pp. 245–258, 2007.
- S. Rajendran, A. Raji, J. A. Selvi, A. Rosaly, and S. Thangasamy, “Parents' education and achievement scores in chemistry,” Edutracks, vol. 6, pp. 30–33, 2007.
- F. R. Selvarani, S. Santhamadharasi, J. W. Sahayaraj, A. J. Amalraj, and S. Rajendran, “Synergistic effect of succinic acid and Zn2+ in controlling corrosion of carbon steel,” Bulletin of Electrochemistry, vol. 20, no. 12, pp. 561–566, 2004.
- J. Sathiabama, S. Rajendran, and J. A. Selvi, “Erilchrome Black-T as corrosion inhibition for carbon steel in well water,” Bulletin of Electrochemistry, vol. 22, pp. 363–370, 2006.
- S. Rajendran, M. Manivannan, J. W. Sahayaraj et al., “Corrosion behavior of aluminium in methyl orange solution at pH 11,” Transactions of the SAEST, vol. 41, no. 2, pp. 63–67, 2006.
- R. M. Silverstein, G. C. Bassler, and T. C. Morrill, Spectrometric, Identification of Organic Compounds, John Wiley & Sons, New York, NY, USA, 1986.
- I. Sekine and Y. Hirakawa, “Effect of 1-hydroxyethylidene-1, 1-diphosphonic acid on the corrosion of SS 41 steel in 0. 3% sodium chloride solution,” Corrosion, vol. 42, no. 5, pp. 272–277, 1986.
- S. Rajendran, S. P. Sridevi, N. Anthony, A. J. Amalraj, and M. Sundaravadivelu, “Corrosion behaviour of carbon steel in polyvinyl alcohol,” Anti-Corrosion Methods and Materials, vol. 52, no. 2, pp. 102–107, 2005.
- S. Rajendran, M. Agasta, R. Bama Devi, B. Shyamala Devi, K. Rajam, and J. Jayasundari, “Corrosion inhibition of aqueous extract of Henna leaves,” Zastita Materijala, vol. 50, no. 2, pp. 77–84, 2009.
- R. M. Silverstein and F. X. Webster, Spectrometric Identification of Organic Compounds, John Wiley & Sons, New York, NY, USA, 6th edition, 2007.
- B. Sherine, A. J. Abdul Nasser, and S. Rajendran, “Inhibitive action of hydroquinone—Zn2+ system in controlling the corrosion of carbon steel in well water,” International Journal of Engineering Science and Technology, vol. 2, no. 4, pp. 341–357, 2010.
- A. K. Singh and M. A. Quraishi, “Investigation of the effect of disulfiram on corrosion of mild steel in hydrochloric acid solution,” Corrosion Science, vol. 53, no. 4, pp. 1288–1297, 2011.
- B. Wang, M. Du, J. Zhang, and C. J. Gao, “Electrochemical and surface analysis studies on corrosion inhibition of Q235 steel by imidazoline derivative against CO2 corrosion,” Corrosion Science, vol. 53, no. 1, pp. 353–361, 2011.