Volume 2013 (2013), Article ID 191723, 6 pages
Aluminising of Mild Steel Plates
Department of Metallurgical and Materials Engineering, NITK, Surathkal 575025, India
Received 29 November 2012; Accepted 16 January 2013
Academic Editors: Y. Yamabe-Mitarai and T. Yue
Copyright © 2013 Udaya Bhat Kuruveri et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.
Hot dip aluminising of low carbon steel was done at temperatures 690°C and 750°C for dipping time ranging from 300 to 2400 seconds. During aluminising a mixture of ZnCl2 and NH4Cl was used as flux. During aluminising components of the flux decomposed and zinc formed interacted with the Fe and Al. The aluminised samples were characterised for iron-aluminium intermetallic layer formation, morphology, and local composition. It was observed that intermetallic layer was predominantly Fe2Al5 and FeAl3 at 690°C and at 750°C coating consisted of FeAl3 layer and a layer with Al/Fe ratio greater than 3.26. For both temperatures, coating thickness increased with increase in time. For a given dipping time, deposition was less at higher temperature and this is attributed to changes in the kinetics of growth of individual layers due to dissolved zinc in the aluminium, at 750°C. Also, spalling of intermetallic layers was observed at elevated temperatures and longer dipping times.
Steel remains the material of choice for numerous applications, largely because of its low cost and wide variety of properties available through alloy design, heat treatment, and amenability for forming operations . The oxide layer forming on the steel substrate is a noncompact one and due to this conventional mild steel exhibits poor oxidation and corrosion resistance properties. To improve corrosion properties, the steel can be alloyed with various elements such as chromium and nickel, but this increases material cost and limits width of the processing window . Alternate route is to modify the surface of the steel appropriately, so that it can replace expensive alloy steel material . During surface modification, the surface of the steel material is modified over a relatively shallow depth, using an appropriate method. When a suitable technique is selected and correctly done, the following properties of the steel can be increased: resistance to wear, chemical resistance, mechanical resistance, and oxidation resistance [3, 4]. Among various surface modification methods available for steel, the hot dipping process has drawn much attention because it is an effective and inexpensive process. In this context, use of aluminium as a coating material is highly relevant because, aluminium, when applied to steel provides corrosion resistance layer . Also, aluminium bearing steels can be easily nitrided and nitrided steel has better wear and fatigue properties. Continuous alumina layer is highly resistant to oxidation, sulfidation, and degradation in chloride containing aqueous solutions . Hence, hot dip aluminising is widely used for coating of steel with aluminium to increase corrosion, oxidation, and hardness of the steel components [5, 7].
Fe–Al is a complex system and its phase diagram is shown in Figure 1. It shows five types of intermetallic compounds, namely, Fe3Al, FeAl, FeAl2, Fe2Al5, and FeAl3. Beneficial application of aluminising depends on minimising detrimental brittle phases and promoting growth of relatively ductile phases. There are investigations on the formation and growth kinetics of the intermetallic phases, under both isothermal and nonisothermal conditions. Shatynski et al.  modelled the formation of intermetallic phases from purely diffusional perspective. They found that growth of intermetallics follows parabolic relation. In the case of Cr–Ni stainless steel, Dybkov  experimentally proved that the intermetallics follows paralinear (initially linear followed by parabolic) growth kinetics. Eggeler et al.  have studied interaction between pure solid steel with liquid aluminium and observed that near aluminium side FeAl3 forms and near iron side Fe2Al5 intermetallic forms. Heumann and Dittrich  tried to explain the tongue like morphology of F2Al5 layer. Bouayad et al.  studied the kinetics of various intermetallic layer formation in pure solid iron and pure liquid aluminium and found that FeAl3 follows linear growth kinetics and Fe2Al5 follows parabolic kinetics. They did experiments at temperatures 700, 800, and 900°C. Naoi and Kajihara  did Al/Fe interdiffusion experiments over temperature range 550–640°C and found that only Fe2Al5 forms at the interface. They did experiments for fairly long time (120 hours) before arriving at this conclusion. Springer et al.  concluded that Fe2Al5 grows faster at lower temperature. They covered a temperature range of 600–675°C to cover solid-solid and solid-liquid diffusion couples. Maki et al.  have observed alloying reaction in aluminised steel when it was exposed for long durations at 600°C. Kobayashi and Yakou  have done experiments with a view to control intermetallic layers at interface between medium carbon steel and aluminium during diffusion experiments over the temperature range from 700 to 900°C for 300 s. They observed that interface is exclusively of Fe2Al5. It is stated that the growth of intermetallic layers depends on the diffusion of Fe atoms into the Al rich intermetallic layers . It is also stated that intermetallic compounds with high Al content (namely, FeAl2, Fe2Al5, and FeAl3) are not desirable due to their brittleness. Hwang et al.  investigated the role of carbon in the dissolution of the substrate and formation of intermetallics. They concluded that carbon effectively lowers the rate of intermetallic layer formation.
Aluminum is a highly reactive metal and gets oxidised very fast, especially, when it is molten. Shielding molten aluminium is very essential. Also, the steel surface has to be cleaned for effective aluminisation of the surface. Mixture of zinc chloride and ammonium chloride is a promising one. It is a violent flux used in galvanisation , but its use in aluminising is less explored. Here an effort was made to understand the effectiveness of the zinc chloride and ammonium chloride as the flux and its role on the formation of Fe–Al based intermetallic layers.
2. Materials and Experimental Methods
The substrate material used in this investigation was low carbon steel, purchased in the form of a rolled strip. The composition of the strip is given in Table 1. The strip was cut into coupons of 3 cm length and 1 cm wide. Coupons were annealed at 900°C for two hours to remove the effect of prior work. Coupon surfaces were ground and polished. The coupons were precleaned using 10% HCl, washed in distilled water, and dried just before they were dipped in liquid aluminium.
Aluminium melt for hot dipping was prepared by heating aluminium ingot in a clay crucible heated by resistance heating. The aluminium was melted and the set temperature was attained. Fluxing was done using a eutectic mixture of ammonium chloride and zinc chloride. Fluxing treatment was done in order to enhance the wetting and dissolution of the oxide coating on the steel, in the molten aluminium bath. Fluxing was done by maintaining a layer on the top of the Al bath. Steel coupons were dipped in aluminium melt maintained at 690°C and 750°C for the time intervals of 300, 600, 900, 1500, and 2400 seconds.
The specimens were cut across the cross-section, metallographically polished, and etched using 3% nital solution. Microstructures were observed in scanning electron microscope (SEM) and coating morphology was studied. Intermetallic layer thickness was measured. Local composition was measured using EDS (energy dispersive spectroscopy) attached to SEM.
3. Results and Discussion
Figure 2 shows the microstructure of the low carbon steel used in the experiment. Microstructure consists of proeutectoid ferrite and eutectoid pearlite. The area fractions of these features confirm that the substrate used is a low carbon steel. Figures 3 and 4 show the microstructure of the aluminised steel, aluminised at 690°C for 300 s and 2400 s, respectively. We see a layer of intermetallic phases (I.M.) between steel and aluminium. Intermetallic layer has a characteristic morphology, which is referred to in the literature as “tongue” like morphology. Intermetallic layer is continuous but its thickness is not constant. The interface between the Al and intermetallic layer is not smooth but the unevenness is on a smaller length scale. On the contrast, the interface between steel and intermetallic layer is more uneven and appears like wave or tongue like. Wave or tongue like morphology for intermetallic layers during aluminising is reported in the literature [15, 17]. Thickness was measured over a length of 1 mm. For 300 s exposure time, the interface thickness was in the range of 95 to 120 m with an average value of 112 micrometers. Intermetallic layer was showing predominantly single contrast, but periodic EDS measurements on this layer showed two distinct regions A and B, whose chemistry was matching with Fe2Al5 and FeAl3, respectively.
There exists another layer C (Figures 3(b) and 4(b)) where the Al/Fe ratio was much higher than 3.26 which is the upper limit of the atomic ratio for the phase, FeAl3 . When the dipping time was large, a thin layer D at Fe/Fe2Al5 interface is clearly visible (inset in Figure 4(b)). EDS analysis on it at selected places indicates Fe/Al ratio as 1 : 2 indicating it most probably as FeAl2 compound. It may be mentioned that Fe2Al5 and FeAl3 are not line phases (refer to phase diagram shown in Figure 1), indicating the possibility of different Fe/Al ratios at different locations. This is also observed during EDS analysis.
Figure 5 shows microstructural features under the conditions of 750°C and 300 seconds. We see two distinct regions corresponding to FeAl3 and another layer with Al : Fe ratio greater than 3.26 : 1. Both show dissolved zinc of various scales. There is no layer corresponding to Fe2Al5 which is distinctly clear in 690°C. Figures 6(a) and 6(b) show microstructures in the case of 750°C bath temperature and holding time of 2400 seconds. Here also no layer corresponding to Fe2Al5 is visible. A layer corresponding to solid solution of Al in iron is clearly visible. All layers show dissolved zinc in them.
We see many polyhedric crystals peeled off from the intermetallic layers in the aluminium matrix. This is due to decrease in the iron solubility in aluminium during cooling. The occurrence of these crystals is more favoured when the cooling rate is increased and the interaction time is long (Figures 4(a) and 5(a)). These crystals have a composition close to that existing in the intermetallic layer close to Al side. Such peeling off is reported by Bouayad et al. .
Formation of various phases in the intermetallic layer under different conditions is explained as follows. In the initial stages of dipping, the intermetallic layer forms are FeAl3 and Fe2Al5 . The FeAl3 layer is initially formed at the interface between the aluminium and steel substrate by the diffusion of iron atoms into aluminium layer and the Fe2Al5 layer is then formed at the interface between the FeAl3 layer and steel substrate. Formation of this layer depends on the relative values of diffusivities (iron into aluminium and aluminium into iron). Under normal conditions, diffusion of iron towards aluminium is larger . It favours Fe2Al5 formation at Fe-FeAl3 interface. This is happening at lower temperature. At higher temperature, the zinc increased the activity of Al in the bath (for details refer to the next paragraph). Increased activity leads to increased diffusion of Al towards iron-FeAl3 interface. This reduced the chances of Fe2Al5 and increased the chances of FeAl3 layer as well as a layer with Al/Fe ratio greater than 3.2 : 1.
Higher dipping temperature means higher amount of ZnCl2 from the flux mixture reacts with metal oxides or oxygen in the environment. It gives ZnO which gets reduced by Al into Zn. This explains higher levels of Zn in the intermetallic layer formed at elevated temperatures. Higher levels of dissolved zinc in Al favour formation of FeAl3 intermetallic than Fe2Al5. The two-phase equilibrium of Fe2Al5 and FeAl3 cannot appear in this study as it involves diffusion of species under chemical potential gradient. Presence of Zn in the bath increases activity of Al, leading to a layer with more Al concentration. Such observations are also reported in the literature . This explains the observation of FeAl3 and higher Al concentration layers. The eutectic reaction at 655°C in Fe–Al system  is bypassed during experimental investigation. Another aspect is liquid aluminium-iron layer on the surface is rapidly cooled giving metastable phases. Skinner et al.  have reported possibility of a number of metastable phases, namely, Al6Fe, Al5Fe, and Al9Fe2 under rapid cooling conditions. All these metastable phases have Al concentration more than that in FeAl3. In our experiments also, the condition at the surface is rapid cooling leading to metastable phases.
Figure 7 shows variation of thickness as a function of dipping time. It shows an increase in the deposit thickness as a function of time. To explore the parabolic relationship between intermetallic layer thickness and dipping time, a plot of thickness versus square root of dipping time is drawn (Figure 8). A straight line relationship is observed indicating that total intermetallic layer follows parabolic growth behaviour. At 690°C, increase in thickness is mainly from thickness of Fe2Al5 and FeAl3. Though FeAl2 layer is visible during longer dipping times, its thickness is negligible compared to overall deposition thickness. Amongst Fe2Al5 and FeAl3, Fe2Al5 undergoes parabolic growth behaviour and FeAl3 follows quasilinear behaviour . Gibbs free energy for formation of FeAl3 is lower than Fe2Al5 and due to this FeAl3 forms instantaneously during dipping. But from kinetics point of view Fe2Al5 is more favoured . Diffusion of Al and Fe takes place across the FeAl3 layer, promoting formation of Fe2Al5 . Due to this, for lower dipping times, FeAl3 and for longer dipping times, Fe2Al5 are major constituents. Because of this, thickness seems to be nonzero even at the start of the dipping. Such observations are also reported by Cheng and Wang  and Li et al. . It is also to be mentioned the smallest experimental duration during our experiments is 300 seconds. It is reported that by this time all the transient nature associated with this reactive diffusion is crossed .
At 750°C, the deposit consists of FeAl3 and another layer where is a positive decimal number. These individual layers have different growth kinetics and hence at 750°C the overall thickness is less compared to that at 690°C. At long interaction times and high temperatures, the spalling of the intermetallic layer takes place and it affects the measurement of the layer thickness .
The experimental investigations lead to the following conclusions. Use of a mixture of ZnCl2 and NH4Cl as a flux for aluminizing leads to some amount of dissolved zinc in the Al bath, especially when bath temperature is high.
At 690°C, the intermetallic layer consisted of predominantly, Fe2Al5, and FeAl3 and at 750°C, the intermetallic layer consists of FeAl3, and a layer with higher levels of Al concentration (Al/Fe ratio more than 3.26) forming due to rapid cooling conditions. This change is attributed to increased Al activity due to dissolved zinc.
The growth of Fe2Al5 layer and total intermetallic layer follows parabolic growth behaviour with respect to dipping time.
- G. Krauss, Properties and Selection: Iron, Steel and High Performance Slloys, vol. 1 of ASM Metals Hand Book, Materials Park, Ohio, USA, 1990.
- J. R. Davis, Surface Engineering, vol. 5 of ASM Metals Hand Book, Materials Park, Ohio, USA, 1990.
- Z. Ahmad, Principles of Corrosion Engineering and Corrosion Control, Elsevier, London, UK, 2006.
- T. Burakowski and T. Weirzchok, Surface engineering of Metals-Principles, Equipments, Technologies, CRC Press, London, UK, 2000.
- D. Wang and Z. Shi, “Aluminizing and oxidation treatment of 1Cr18Ni9 stainless steel,” Applied Surface Science, vol. 227, no. 1–4, pp. 255–260, 2004.
- K. Murakami, N. Nishida, K. Osamura, and Y. Tomota, “Aluminization of high purity iron by powder liquid coating,” Acta Materialia, vol. 52, no. 5, pp. 1271–1281, 2004.
- A. Bahadur and O. N. Mohanty, “Structural studies of hot dip aluminized coatings on mild steel,” Materials Transactions, JIM, vol. 32, no. 11, pp. 1053–1061, 1991.
- N.Y. Tang, “Determination of liquid phase boundaries in Zn-Fe-Mx systems,” Journal of Phase Equilibria, vol. 21, no. 1, pp. 167–176, 2000.
- S. R. Shatynski, J. P. Hirth, and R. A. Rapp, “A theory of multiphase binary diffusion,” Acta Metallurgica, vol. 24, no. 12, pp. 1071–1078, 1976.
- V. I. Dybkov, “Reaction diffusion in heterogeneous binary systems—part 1 Growth of the chemical compound layers at the interface between two elementary substances: one compound layer,” Journal of Materials Science, vol. 21, no. 9, pp. 3078–3084, 1986.
- G. Eggeler, W. Auer, and H. Kaesche, “On the influence of silicon on the growth of the alloy layer during hot dip aluminizing,” Journal of Materials Science, vol. 21, no. 9, pp. 3348–3350, 1986.
- T. Heumann and S. Dittrich, “Uber die Kinetic der Reaction von Festemund Flussigem Aluminum mit Eisen,” Zeit fi Afetallkunde, vol. 10, pp. 617–624, 1959.
- A. Bouayad, C. Gerometta, A. Belkebir, and A. Ambari, “Kinetic interactions between solid iron and molten aluminium,” Materials Science and Engineering A, vol. 363, no. 1-2, pp. 53–61, 2003.
- D. Naoi and M. Kajihara, “Growth behavior of Fe2Al5 during reactive diffusion between Fe and Al at solid-state temperatures,” Materials Science and Engineering A, vol. 459, no. 1-2, pp. 375–382, 2007.
- H. Springer, A. Kostka, E. J. Payton, D. Raabe, A. Kaysser-Pyzalla, and G. Eggeler, “On the formation and growth of intermetallic phases during interdiffusion between low-carbon steel and aluminum alloys,” Acta Materialia, vol. 59, no. 4, pp. 1586–1600, 2011.
- J. Maki, M. Suehiro, and Y. Ikematsu, “Alloying reaction of aluminized steel sheet,” ISIJ International, vol. 50, no. 8, pp. 1205–1210, 2010.
- S. Kobayashi and T. Yakou, “Control of intermetallic compound layers at interface between steel and aluminium by diffusion treatment,” Materials Science and Engineering A, vol. 338, pp. 44–53, 2002.
- S. H. Hwang, J. H. Song, and Y. S. Kim, “Effects of carbon content of carbon steel on its dissolution in to molten aluminium alloy,” Materials Science and Engineering A, vol. 390, pp. 437–443, 2005.
- M. Gilles, D. Leychkis, Y. Grot, and R. Pankert, “Preparation of steel surfaces for single dip aluminium rich zinc galvanising,” US Patent no. 7160581, January 2007.
- G. Neumann and A. D. Le Claire, Diffusion in Solid Metals and Alloys, Numerical Data and Functional Relationships in Science and Technology, vol. 26, Springer, 1990.
- M. V. Akdeniz and A. O. Mekhrabov, “The effect of substitutional impurities on the evolution of Fe-Al diffusion layer,” Acta Materialia, vol. 46, no. 4, pp. 1185–1192, 1998.
- D. J. Skinner, K. Okazaki, and C. M. Adam, “Physical metallurgy and mechanical properties of Al alloys containing 8 to 12%Fe rapidly solidified powder alumium alloys,” in Rapidly Solidified Powder Aluminum Alloys, M. E. Fine and E. A. Starke, Eds., ASTM STP 890, pp. 211–236, American Society for Testing and Materials, Philedelphia, Pa, USA, 1986.
- W.-J. Cheng and C.-J. Wang, “Characterisation of intermetallic layer formation in aluminde/nickel duplex coating on mild steel,” Materials Characterisation, vol. 69, pp. 63–70, 2012.
- K. Bouché, F. Barbier, and A. Coulet, “Intermetallic compound layer growth between solid iron and molten aluminium,” Materials Science and Engineering A, vol. 249, no. 1-2, pp. 167–175, 1998.
- Y. J. Li, J. Wang, and X. Holly, “X-ray diffraction and TEM analysis of Fe-Al alloy layer in coating of new hot dip aluminised steel,” Materials Science and Technology, vol. 19, no. 5, pp. 657–660, 2003.