Review Article
Viscosity and Glass Transition in Amorphous Oxides
Table 4
Thermodynamic parameters of configurons.
| Amorphous material | / kJ mol−1 | , kJ mol−1 | | | |
| Silica (SiO2) | 237 | 522 | 17.54 | 11.37 | 1.54 | SLS
(mass %): 70SiO2 | 331 | 293 | 44.03 | 24.40 | 1.8 | 21CaO 9Na2O | 80SiO2 20Na2O | 155 | 207 | 17.98 | 7.79 | 2.31 | 66.7SiO2 33.3PbO | 197 | 274 | 25.40 | 7.3 | 3.48 | 65SiO2 35PbO | 231 | 257 | 30.32 | 8.53 | 3.55 | 59.9SiO2 40.1PbO | 236 | 258 | 31.12 | 6.55 | 4.6 | B2O3 | 258 | 113 | 44.2 | 9.21 | 4.8 | 65SiO2 35Na2O | 300 | 186 | 40.71 | 7.59 | 5.36 | 70SiO2 30Na2O | 258 | 205 | 34.84 | 5.22 | 5.87 | 75.9SiO2 24.1PbO | 262 | 234 | 36.25 | 5.44 | 6.66 | Germania (GeO2) | 129 | 272 | 17.77 | 2.49 | 7.14 | 75SiO2 25Na2O | 233 | 203 | 30.62 | 4.22 | 7.26 | Anorthite
(CaAl2Si2O8) | 884 | 251 | 79.55 | 0.374 | 213 | 52SiO2 30Li2O 18B2O3 | 420 | 194 | 52.06 | 0.227 | 229 | Salol
| 145 | 118 | 68.13 | 0.114 | 598 | (HOC6H4COOC6H5) | α–phenyl–o–cresol | 172 | 103 | 83.84 | 0.134 | 626 | Diopside
(CaMgSi2O6) | 834 | 240 | 88.71 | 0.044 | 2016 |
|
|