Heterostructures for Realizing Magnon-Induced Spin Transfer Torque
Figure 7
(a) Current in plane magnetoresistance measurements on Fe3O4(500 Å)/Cr(57 Å)/Fe3O4(1000 Å) spin valves. The black (red) data are measurements with increasing (decreasing) fields. (b) Change of GMR as a function of Cr spacer layer thickness; the line is a fit to an exponential decay, with a decay constant of 33 Å.