Tin-Doped Indium Oxide-Titania Core-Shell Nanostructures for Dye-Sensitized Solar Cells
Table 1
Photovoltaic properties of devices when the TiO2 shell was annealed between 350 and 600°Ca.
| | | (V) | (mA⋅cm−2) | FF (%) | (%) | Dye loading (×10−8 mol⋅cm−2) |
| | 350°C | 0.46 ± 0.03 | 7.05 ± 0.07 | 50.7 ± 1.0 | 1.65 ± 0.07 | 2.16 | | 400°C | 0.49 ± 0.06 | 9.90 ± 0.08 | 50.6 ± 0.9 | 2.45 ± 0.08 | 1.80 | | 500°C | 0.53 ± 0.03 | 12.61 ± 0.05 | 50.7 ± 0.6 | 3.39 ± 0.05 | 1.32 | | 600°C | 0.56 ± 0.04 | 9.75 ± 0.05 | 50.5 ± 0.9 | 2.76 ± 0.07 | 1.01 |
|
|
Average values and standard deviations are based on 3-4 devices.
|