Pressure Induced Suppression to the Valence Change Transition in EuPdAs
Figure 1
Powder X-ray diffraction patterns and the Rietveld refinement profile of the EuPdAs sample at room temperature. All main diffraction peaks can be indexed well by the P63/mmc space group (hexagonal structure) with Å and Å with Eu5As3 and Pd2As as the impurity phases. The ratio between EuPdAs and the impurities is found to be 90 : 10.