Morphologic and Chemical Properties of PMMA/ATH Layers with Enhanced Abrasion Resistance Realised by Cold Plasma Spraying at Atmospheric Pressure

Table 1

Summary of coating parameters (subscript w stands for wood and g for glass) [20].

Sample number	Deposited material	Process/carrier gas; (flow rate)	Carrier gas pressure in MPa	Working distance in mm	Powder feed rate in cm^3/h	Substrate displacement in mm/s
	PMMA/ATH	Compressed air (40 L/min)	0.15	13	72	20
	PMMA/ATH	Forming gas; (35 L/min)	0.1	25	121	100
	PMMA/ATH (90%); PF (10%)	Compressed air (40 L/min)	0.16	16	121	20