Precipitation and Growth Kinetics in Mechanically Alloyed Ni–Al
Table 1
Dislocation density and grain size of as-fabricated specimens produced by mechanical alloying and arc-melting.
| | Dislocation density (1/m2) | Grain size |
| Ni–15at%Al (MA) | 3.65 × 1016 | 91 nm | Ni–15at%Al–0.6at%Y2O3 (MA) | 5.18 × 1016 | 66 nm | Ni–15at%Al (arc) | 8.50 × 1013 | 3 mm |
|
|