The Influence of Prior Natural Aging on the Subsequent Artificial Aging Response of Aluminium Alloy A356 with Respective Globular and Dendritic Microstructures

<table>T6 (540°C-1 h, 0 or 120 h NA, 180°C-4 h) hardness values as a function of the Mg-content of A356 produced using different casting techniques.</table>

Advances in Materials Science and Engineering

fig6

Figure 6

Figure 6: The Influence of Prior Natural Aging on the Subsequent Artificial Aging Response of Aluminium Alloy A356 with Respective Globular and Dendritic Microstructures 

Figure 6 | The Influence of Prior Natural Aging on the Subsequent Artificial Aging Response of Aluminium Alloy A356 with Respective Globular and Dendritic Microstructures 