Direct Laser Cladding of Cobalt on Ti-6Al-4V with a Compositionally Graded Interface
Figure 2
Wear profiles of (1) Ti substrate and Co clad Ti lased with laser power density, P of 0.212 kW/mm2 and scan speed, v of 14.3 mm/s for (2) without Cu interlayer and with Cu interlayer with thickness of (3) 30 μm at 1 kg load.