Stress Corrosion Cracking of Steel and Aluminum in Sodium Hydroxide: Field Failure and Laboratory Test

<table>Crack depth as a function of applied stress.</table>

Advances in Materials Science and Engineering

Figure 5: Stress Corrosion Cracking of Steel and Aluminum in Sodium Hydroxide: Field Failure and Laboratory Test 