Crystallisation Kinetics of a 𝜷-Spodumene-Based Glass Ceramic

Table 2

Properties of the investigated LZSA glass ceramic (sintered at 850°C for 10 min).

d50, μm	2.34
𝜌, g·cm^−3
Parent glass	2.622 ± 0.004
Glass ceramic	2.711 ± 0.003
𝛼, 10^6∘C^−1	2.38
tan 𝛿	0.029 ± 0.011
𝜀r	9.97 ± 0.84
Tg, °C	580
Tc, °C	794
Tc−Tg, °C	214