Contribution of Process Annealing on the Development of Microstructure and Texture of Cu-30Zn Brass

Table 2

Texture trend of final cold rolled gauge (from R1 to R3).

Texture orientation	Texture trend
Cube, Bs, G, CG	Strength gradually decreases from R1 to R3.
S, R, C	Strength gradually increases from R1 to R3.
Cu, Taylor, Z	Strengths constant in R1 and R2 with the increase in R3.
H, CH	Highest strength in R1 and decrease and constant in R2 and R3.
L	First increases and then decreases. Highest strength in R2