Influence of Annealing Temperature on the Magnetic Properties of Rapidly Quenched (Nd,Pr)<sub><b>2</b></sub>-(Fe,Co,Ga,Ti,C)<sub><b>14</b></sub>B/<b><i>α</i></b>-Fe Nanocomposite Ribbons

<table>FESEM morphologies of Nd<sub>9.4</sub>Pr<sub>0.6</sub>Fe<sub>74.5</sub>Co<sub>6</sub>B<sub>6</sub>Ga<sub>0.5</sub>Ti<sub>1.5</sub>C<sub>1.5</sub> at (a) 600°C, (b) 650°C,  (c) 700°C, and (d) 750°C annealed ribbons for 10 minutes.</table>

Advances in Materials Science and Engineering

fig4

Figure 4

Figure 4: Influence of Annealing Temperature on the Magnetic Properties of Rapidly Quenched (Nd,Pr)<sub><b>2</b></sub>-(Fe,Co,Ga,Ti,C)<sub><b>14</b></sub>B/<b><i>α</i></b>-Fe Nanocomposite Ribbons 

Advances in Materials Science and Engineering

Influence of Annealing Temperature on the Magnetic Properties of Rapidly Quenched (Nd,Pr)2-(Fe,Co,Ga,Ti,C)14B/α-Fe Nanocomposite Ribbons

Figure 4

Influence of Annealing Temperature on the Magnetic Properties of Rapidly Quenched (Nd,Pr)₂-(Fe,Co,Ga,Ti,C)₁₄B/α-Fe Nanocomposite Ribbons