Effect of Cooling Rate on the Microstructure of Al-Zn Alloys with Addition of Silicon as Nanocomposite
Table 2
EDXS microanalysis of the Al-Zn-1.5Si (wt%) modified alloy solidified at different cooling rates.
|
Phase morphology |
Sample condition |
Average chemical composition (wt%) | dT/dt (°C s−1) | Si (wt%) | Al | Zn | Si |
| Dendritic region | 11.7 | 1.53 | 80.7 | 19.3 | — | 31.5 | 1.53 | 78.0 | 22.0 | — | 50.1 | 1.53 | 85.0 | 15.0 | — |
| Interdendritic region | 11.7 | 1.53 | 10.3 | 89.7 | — | 31.5 | 1.53 | 23.8 | 76.2 | — | 50.1 | 1.53 | 20.1 | 79.9 | — |
| Al-Zn-Si Eutectic (blocky) | 11.7 | 1.53 | 13.5 | 31.6 | 54.9 | 31.5 | 1.53 | 20.8 | 23.4 | 55.8 | 50.1 | 1.53 | 8.1 | 34.5 | 57.4 |
|
|