Parameters Controlling the Oxide Reduction during Sintering of Chromium Prealloyed Steel
Figure 11
Microstructure of the AstCrM + 0.5% C components sintered at 1200°C for 30 min (a) prevalent upper bainitic when cooled at 10°C/min and upper/lower bainite mixture when cooled at 50°C/min.