Surface Hardening of Ti-15V-3Al-3Cr-3Sn Alloy after Cyclic Hydrogenation and Subsequent Solution Treatment

Table 4

The magnitude of angular shift and (/) the FWHM in degree of peaks 𝛽(110), 𝛽(200), and 𝛽(211) for some treated specimens corresponding to A0, B0, and C0 ones, respectively.

Specimen	𝛽(110)	𝛽(200)	𝛽(211)
A0	39.47 (—/0.19)	56.83 (—/0.30)	71.43 (—/0.23)
AT3	39.61 (0.14/0.20)	57.03 (0.20/0.32)	71.75 (0.32/0.32)
AT3L4	38.69 (−0.78/0.14)	55.73 (−1.10/0.30)	69.79 (−1.64/0.24)
B0	39.31 (—/0.29)	57.09 (—/0.23)	71.67 (—/0.21)
BT3	39.41 (0.10/0.16)	57.21 (0.12/0.27)	71.81 (0.14/0.29)
BT3L4	38.55 (−0.76/0.12)	55.77 (−1.32/0.23)	69.67 (−2.00/0.23)
C0	39.49 (—/0.22)	57.11 (—/0.34)	71.65 (—/0.25)
CT3	39.60 (0.11/0.14)	57.21 (0.10/0.20)	71.77 (0.12/0.19)
CT3L4	38.29 (−1.20/0.11)	55.39 (−1.82/0.14)	69.17 (−2.48/0.16)