Surface Hardening of Ti-15V-3Al-3Cr-3Sn Alloy after Cyclic Hydrogenation and Subsequent Solution Treatment
Table 5
Variations in lattice constant and volume expansion rate between typical treatments.
| Treatment | Variation | Lattice constant () | Lattice expansion | Volume expansion |
| A0 | 3.234 | — | — | AT3 (versus A0) | 3.233 | −0.031% | −0.093% | AT3L4 (versus A0) | 3.275 | 1.30% | 3.90% | B0 (versus A0) | 3.232 | −0.062% | −0.186% | BT3 (versus B0) | 3.231 | −0.031% | −0.093% | BT3L4 (versus B0) | 3.253 | 0.68% | 2.04% | C0 (versus A0) | 3.230 | −0.124% | −0.372% | CT3 (versus C0) | 3.229 | −0.031% | −0.093% | CT3L4 (versus C0) | 3.288 | 1.80% | 5.40% |
|
|