Surface Hardening of Ti-15V-3Al-3Cr-3Sn Alloy after Cyclic Hydrogenation and Subsequent Solution Treatment
Table 6
,
, and
for typical specimens (Vickers hardness measured at the load of 50 gw).
| Process designation | | (m) | | 50 | 100 | 150 | 200 | 250 | 300 | 350 | 400 | 450 | (500) |
| A0 | 236.9 | | 241.2 | | 226.3 | | 230.4 | | 231.7 | | 234.6 | AT3 | 264.5 | | | | | | | | | | | | AT3L4 | 409.3 | 376.2 | 387.6 | 378.6 | 371.4 | 380.0 | 356.6 | 346.5 | 336.9 | 345.6 | 346.1 | AT4 | 301.1 | | 257.2 | | 260.5 | | 250.3 | | 254.2 | | 253.1 |
| B0 | 179.5 | | 185.3 | | 177.2 | | 164.7 | | 174.3 | | 169.8 | BT3 | 277.9 | | | | | | | | | | | | BT3L4 | 344.7 | 364.1 | 364.7 | 364.0 | 357.0 | 355.6 | 347.3 | 338.7 | 330.4 | 336.9 | 331.2 | BT4 | 288.2 | | 219.6 | | 221.2 | | 217.7 | | 213.8 | | 219.8 |
| C0 | 314.7 | | 318.6 | | 317.4 | | 310.6 | | 317.9 | | 318.2 | CT3 | 330.7 | | | | | | | | | | | | CT3L4 | 491.1 | 476.3 | 467.2 | 436.8 | 443.1 | 438.7 | 436.5 | 429.8 | 432.7 | 427.3 | 423.8 | CT4 | 348.1 | | 327.9 | | 322.6 | | 317.4 | | 338.1 | | 326.7 |
|
|