Toughness Calculation of Postfire Normal Concrete

Table 1

The experimental results of fracture parameters.

Specimen	Temperature	𝑃ini/kN	𝑃max/kN	CMOD𝑐/mm	CTOD𝑐/mm	𝐸; GPa	𝐺𝐹; N/m	𝐾^ini𝐼; MPa·m^1/2	𝐾𝐼^𝐶−𝐴; MPa·m^1/2	𝐾^un𝐼^−𝐸; MPa·m^1/2	𝐾^un𝐼^−𝐴; MPa·m^1/2
WS6	65°C	6.98	11.31	0.195	0.078	21.73	425.91	0.550	1.007	1.594	1.557
WS7		3.88	8.23	0.163	0.100	24.79	482.62	0.303	1.63	1.664	1.933
WS8		6.88	10.41	0.212	0.087	19.43	487.75	0.557	1.006	1.518	1.563
WS9		7.94	10.71	0.164	0.087	23.25	480.51	0.511	1.174	1.685	1.685
WS10		6.32	11.67	0.229	0.086	16.60	522.36	0.562	0.903	1.507	1.465
Average		6.42	10.47	0.193	0.088	21.16	479.83	0.480	1.161	1.594	1.641
WS16	200°C	—	—	—	—	—	—	—	—	—	—
WS17		4.22	6.60	0.317	0.143	11.58	282.51	0.211	0.803	1.206	1.014
WS18		3.97	6.15	0.213	0.138	6.98	215.14	0.353	0.485	0.863	0.838
WS19		2.41	5.33	0.213	0.138	9.17	235.91	0.215	0.72	0.924	0.935
WS20		3.32	5.24	0.458	0.211	7.00	368.94	0.245	0.796	1.022	1.041
Average		3.50	5.72	0.352	0.157	8.68	376.95	0.256	0.688	1.044	0.957
WS31	400°C	1.55	3.61	1.032	0.492	2.56	532.09	0.138	0.572	0.795	0.710
WS32		1.78	3.19	1.218	0.548	1.42	396.93	0.158	0.333	0.574	0.491
WS33		2.37	3.27	0.768	0.299	2.12	434.89	0.174	0.236	0.621	0.410
WS34		2.36	4.53	0.736	0.302	1.71	598.93	0.125	0.356	0.468	0.494
WS35		—	—	—	—	—	—	—	—	—	—
Average		2.01	3.78	0.901	0.410	1.95	490.71	0.152	0.374	0.615	0.526
WS46	600°C	0.76	1.13	1.482	0.684	0.47	228.23	0.067	0.174	0.221	0.231
WS47		0.53	1.48	2.082	0.684	0.48	395.06	0.063	0.209	0.277	0.284
WS48		0.81	1.65	1.908	0.813	1.14	539.22	0.072	0.478	0.550	0.550
WS49		0.58	1.14	1.687	0.973	0.38	331.99	0.052	0.188	0.225	0.225
WS50		0.62	1.48	2.082	0.727	0.38	273.07	0.068	0.155	0.213	0.213
Average		0.62	1.38	1.848	0.799	0.57	353.51	0.064	0.241	0.297	0.301