Effects of Rolling Reduction and Strength of Composed Layers on Bond Strength of Pure Copper and Aluminium Alloy Clad Sheets Fabricated by Cold Roll Bonding

<table>Rolling reduction dependence on the ultimate tensile stress of (a) the Cu/Al clad sheet and the composed layer, (b) the Cu/AA5052 clad sheet and the composed layers, and (c) the Cu/AA5083 clad sheet and the composed layers.</table>

Advances in Materials Science and Engineering

fig5

Figure 5

Figure 5: Effects of Rolling Reduction and Strength of Composed Layers on Bond Strength of Pure Copper and Aluminium Alloy Clad Sheets Fabricated by Cold Roll Bonding 

Figure 5 | Effects of Rolling Reduction and Strength of Composed Layers on Bond Strength of Pure Copper and Aluminium Alloy Clad Sheets Fabricated by Cold Roll Bonding 