Fatigue Properties of Layered Double Hydroxides Modified Asphalt and Its Mixture

<table class="table-group" id="tab3"><tr><td><table class="table"><tr><td class="thead-hr" colspan="4"><hr/></td></tr><tr class="thead"><td align="left">Temperature</td><td align="center">UV strength</td><td align="center">Film thickness</td><td align="center">Aging time</td></tr><tr><td class="thead-hr" colspan="4"><hr/></td></tr><tr><td align="left">50°C</td><td align="center">10,000 <i>μ</i>W/cm<sup>2</sup></td><td align="center">1250 <i>μ</i>m</td><td align="center">8 days</td></tr><tr class="table-tr"><td colspan="4"><hr class="tbody-hr"/></td></tr></table></td></tr></table>

UV aging test conditions for bitumen binder.

Advances in Materials Science and Engineering

tab3

Table 3

Table 3: Fatigue Properties of Layered Double Hydroxides Modified Asphalt and Its Mixture 