Nanocrystalline 6061 Al Powder Fabricated by Cryogenic Milling and Consolidated via High Frequency Induction Heat Sintering
Table 3
Properties of the consolidated samples.
| Sintering parameters | Grain size (nm) | Percentage of full density (%) | Hardness HV |
| 500°C–400°C/min–1.5 min. | 125 | 92 | 56 | 550°C–400°C/min–1.5 min. | 150 | 98 | 59 |
|
|