Corrosion Behavior of Pure Cr, Ni, and Fe Exposed to Molten Salts at High Temperature

<table>Electron image of the metal-scale interface and X-ray mappings of Cr, O, and V when pure metal chromium was exposed to NaVO<sub>3</sub> at 700°C during 100 hours.</table>

Advances in Materials Science and Engineering

fig2

Figure 2

Figure 2: Corrosion Behavior of Pure Cr, Ni, and Fe Exposed to Molten Salts at High Temperature 