Conductivity and Dielectric Studies of Lithium Trifluoromethanesulfonate Doped Polyethylene Oxide-Graphene Oxide Blend Based Electrolytes

<div>The frequency dependence of dielectric loss, <svg height="9.25202pt" id="M37" style="vertical-align:-3.29111pt" version="1.1" viewbox="-0.0498162 -5.96091 8.17908 9.25202" width="8.17908pt" xmlns="http://www.w3.org/2000/svg" xmlns:xlink="http://www.w3.org/1999/xlink"><g transform="matrix(.013,0,0,-0.013,0,0)"><path d="M387 375C387 402 357 448 257 448C172 448 82 404 82 326C82 289 108 255 156 241V239C85 223 23 181 23 116C23 39 89 -12 182 -12C265 -12 336 31 378 91L361 114C320 73 269 47 216 47C157 47 115 82 115 137C115 191 160 219 218 219C243 219 262 218 272 217L304 259L302 266C295 265 281 264 255 264C195 264 163 294 163 335C163 377 200 416 249 416C293 416 321 389 329 342C331 332 335 329 341 329C355 329 387 352 387 375Z" id="g113-247"></path><glyph.data ascent="3473" descent="-2876" horiz-adv-x="410" vert-adv-y="410"></glyph.data></g><g transform="matrix(.0091,0,0,-0.0091,5.005,3.132)"><path d="M250 606C250 634 233 656 203 656C168 656 146 618 146 593C146 564 169 545 192 545C227 545 250 573 250 606ZM227 95L212 119C187 98 152 71 135 71C129 71 128 78 134 102L207 373C219 418 217 451 194 451C165 451 92 411 30 351L44 326C77 353 106 371 114 371C124 371 121 357 117 341L55 97C32 5 46 -12 70 -12C108 -12 191 51 227 95Z" id="g50-106"></path><glyph.data ascent="3443" descent="-2856" horiz-adv-x="280" vert-adv-y="280"></glyph.data></g></svg>, at room temperature: (a) salted system and (b) plasticized system for selected sample.</div>

Advances in Materials Science and Engineering

fig8

Figure 8

Figure 8: Conductivity and Dielectric Studies of Lithium Trifluoromethanesulfonate Doped Polyethylene Oxide-Graphene Oxide Blend Based Electrolytes 