Effect of Cu Addition on the Electrochemical Corrosion Performance of Ni3Al in 1.0 M H2SO4
Table 1
Electrochemical parameters of the tested materials in a 1.0 M H2SO4 solution at 25°C.
Material
(mV)
(mV/Dec)
(mV/Dec)
(A/cm2)
(mV)
(A/cm2)
(mV)
(mA/cm2)
Ni3Al
−279
40
124
9.1 ± 0.05
−105
15000 ± 0.05
—
—
Ni3Al-1Cu
−279
49
90
2.8 ± 0.05
104
17000 ± 0.05
—
—
Ni3Al-3Cu
−272
65
140
3.8 ± 0.05
190
55000 ± 0.05
—
—
Ni3Al-5Cu
−249
90
157
4.5 ± 0.05
73
15000 ± 0.05
164 ± 0.00005
18
Ni
−297
71
122
31.2 ± 0.05
−70
16000 ± 0.05
498 ± 0.00005
450 ± 0.00005
Cu
−121
81
437
2.5 ± 0.05
—
—
—
—
Al
−682
274
136
56.0 ± 0.05
—
—
—
—
and indicate the primary passivation potential and primary passivation current density. and indicate the repassivation potential and current density, respectively.