Research Article
Specimen Test of Large-Heat-Input Fusion Welding Method for Use of SM570TMCP
Table 6
Results of tensile test in large-heat-input welding test (SM570TMCP).
| Steel type | Plate thickness (mm) | Preheat tem. (°C) | Interlayer tem. (°C) | Welding method | Input heat (kJ/cm) | Yield strength (0.2%, MPa) | Tensile strength (MPa) | Elongation (%) | Fracture part |
| SM570TMC | 35 | None | None | ESW | 80 | 445 460 | 610 624 | 25.2 26.5 | Weld Metal Weld Metal | 120 | 456 466 | 616 625 | 22.4 24.5 | Weld Metal Weld Metal | 40 | 50°C | Max. 250°C | SAW | 70 | 579 583 | 660 655 | 22.6 24.2 | Weld Metal Weld Metal | 100 | 567 530 | 652 648 | 19.3 22.7 | Weld Metal Weld Metal | FCAW | 60 | 535 531 | 606 407 | 19.1 15.9 | Weld Metal Weld Metal | 80 | 50°C | Max. 250°C | SAW | 70 | 452 455 | 611 627 | 29.8 34.0 | Base Metal Base Metal | FCAW | 60 | 532 529 | 604 589 | 25.5 29.7 | Weld Metal Weld Metal | 100 | 50°C | Max. 250°C | SAW | 70 | 554 561 | 627 639 | 23.3 36.0 | Weld Metal Base Metal | FCAW | 60 | 499 502 | 597 596 | 22.7 22.5 | Weld Metal Weld Metal |
|
|