Magnetron Sputtering a New Fabrication Method of Iron Based Biodegradable Implant Materials

<div>Exemplary Tafel-curves of s-Fe annealed at different temperatures for two hours. With increasing annealing temperatures a shift of <svg height="11.927pt" id="M48" style="vertical-align:-3.291101pt" version="1.1" viewbox="-0.0498162 -8.6359 12.9901 11.927" width="12.9901pt" xmlns="http://www.w3.org/2000/svg" xmlns:xlink="http://www.w3.org/1999/xlink"><g transform="matrix(.013,0,0,-0.013,0,0)"><path d="M715 650H476L470 622C550 619 562 610 562 570C562 536 553 481 535 384L523 321C485 121 408 37 283 37C178 37 99 109 134 297L178 532C193 612 199 616 278 622L284 650H29L23 622C105 616 109 609 94 532L48 291C23 160 51 83 98 40C143 -1 202 -16 260 -16C321 -16 387 3 439 49C509 111 542 204 563 312L577 384C595 479 608 533 619 569C629 603 637 620 709 622L715 650Z" id="g113-86"></path><glyph.data ascent="3473" descent="-2876" horiz-adv-x="727" vert-adv-y="727"></glyph.data></g><g transform="matrix(.0091,0,0,-0.0091,8.606,3.132)"><path d="M387 400C387 425 348 451 303 451C247 451 176 414 132 376C69 322 24 228 24 148C24 43 74 -12 147 -12C211 -12 301 33 363 103L346 128C319 99 249 51 193 51C148 51 112 84 112 165C112 230 130 287 154 330C170 359 199 400 243 400C277 400 304 383 326 354C333 345 343 343 354 348C378 360 387 382 387 400Z" id="g50-100"></path><glyph.data ascent="3443" descent="-2856" horiz-adv-x="411" vert-adv-y="411"></glyph.data></g></svg> to more negative values and slight increase of <svg height="12.0653pt" id="M49" style="vertical-align:-3.4294pt" version="1.1" viewbox="-0.0498162 -8.6359 9.54526 12.0653" width="9.54526pt" xmlns="http://www.w3.org/2000/svg" xmlns:xlink="http://www.w3.org/1999/xlink"><g transform="matrix(.013,0,0,-0.013,0,0)"><path d="M394 607C394 634 378 655 350 655C315 655 294 620 294 594C294 564 314 546 339 546C372 546 394 574 394 607ZM360 349C373 414 374 448 351 448C321 448 249 404 183 338L197 313C223 336 265 367 276 367C285 367 283 355 275 313C241 129 220 23 189 -102C175 -158 153 -197 124 -197C106 -197 85 -187 70 -177C64 -173 51 -177 44 -183C34 -193 23 -209 23 -228C23 -244 46 -261 67 -261C86 -261 127 -245 181 -197C237 -147 279 -52 303 66L360 349Z" id="g113-107"></path><glyph.data ascent="3473" descent="-2876" horiz-adv-x="423" vert-adv-y="423"></glyph.data></g><g transform="matrix(.0091,0,0,-0.0091,5.174,3.132)"><path d="M387 400C387 425 348 451 303 451C247 451 176 414 132 376C69 322 24 228 24 148C24 43 74 -12 147 -12C211 -12 301 33 363 103L346 128C319 99 249 51 193 51C148 51 112 84 112 165C112 230 130 287 154 330C170 359 199 400 243 400C277 400 304 383 326 354C333 345 343 343 354 348C378 360 387 382 387 400Z" id="g50-100"></path><glyph.data ascent="3443" descent="-2856" horiz-adv-x="411" vert-adv-y="411"></glyph.data></g></svg> is observed.</div>

Advances in Materials Science and Engineering

fig9

Figure 9

Figure 9: Magnetron Sputtering a New Fabrication Method of Iron Based Biodegradable Implant Materials 