Studying the Effect of ZnO on Physical and Elastic Properties of (ZnO)_x(P₂O₅)_1−x Glasses Using Nondestructive Ultrasonic Method

Table 1

The values of density, molar volume, sound velocities, elastic moduli, Poisson’s ratio, and Debye temperature.

Glass sample ()	(kg m^−3)	(cm^3 mol^−1)	(m/s)	(m/s)	(GPa)	(GPa)	(GPa)	(GPa)		(K)
0.1	2420	56.2	3887	2406	36.6	14.0	17.9	33.3	0.189	257
0.2	2590	50.1	3986	2424	41.2	15.2	20.9	36.8	0.207	265
0.3	2745	45.1	4087	2446	45.8	16.4	24.0	40.1	0.221	276
0.4	2937	40.1	4158	2462	50.8	17.8	27.0	43.8	0.230	283
0.5	3105	36.0	4275	2486	56.7	19.2	31.2	47.8	0.245	293
0.6	3281	32.2	4376	2506	62.8	20.6	35.4	51.8	0.256	303