| Specimen | Tensile strength (MPa) | Elastic modulus (MPa) | Measured | Mean (S.D.) | Ratio | Measured | Mean (S.D.) | Ratio |
| D19HD0 | 1,218 | 1,193 (54) | 100% | 53,520 | 55,073 (1,502) | 100% | 1,229 | 55,180 | 1,131 | 56,519 |
| D19HD6 | 1,016 | 1,091 (55) | 91.4% | 59,276 | 56,917 (1,464) | 103.3% | 1,147 | 55,623 | 1,106 | 56,681 | 1,131 | 57,229 | 1,029 | 55,190 | 1,117 | 57,505 |
| D19HD8 | — | 877 (26) | 73.5% | — | 51,439 (2,163) | 93.4% | 863 | 52,641 | 898 | 49,577 | 873 | 50,036 | 908 | 50,267 | 843 | 54,674 |
| D19HD10 | 746 | 736 (9) | 61.7% | 49,664 | 46,252 (2,003) | 84.0% | 741 | 45,073 | — | — | 722 | 46,453 | 736 | 44,988 | 738 | 45,080 |
| D19HD12 | 684 | 686 (37) | 57.5% | 38,819 | 35,439 (2,233) | 64.3% | 731 | 35,442 | 640 | 34,792 | 730 | 33,410 | 666 | 37,175 | 667 | 32,999 |
|
|