TiC0.5N0.5-Based Cermets with Varied Amounts of Si3N4 Nanopowders Prepared by Spark Plasma Sintering
Table 3
Typical atomic content of each element in Particle A.
| Samples | C | N | Ti | V | Ni | Mo | W |
| TiCN-0 wt.% Si3N4 | 52.60 | 4.03 | 16.55 | 0.22 | 8.21 | 8.73 | 9.66 | TiCN-2 wt.% Si3N4 | 53.61 | 8.52 | 17.91 | 0.47 | 1.83 | 5.19 | 12.45 | TiCN-5 wt.% Si3N4 | 54.51 | 11.43 | 10.72 | 0.21 | 8.40 | 4.01 | 10.72 |
|
|