TiC0.5N0.5-Based Cermets with Varied Amounts of Si3N4 Nanopowders Prepared by Spark Plasma Sintering
Table 4
Typical atomic content of each element in Particle B.
| Samples | C | N | Si | Ti | V | Ni | Mo | W |
| TiCN-0 wt.% Si3N4 | 41.05 | 13.17 | 0 | 42.53 | 0.16 | 0.45 | 1.89 | 0.75 | TiCN-2 wt.% Si3N4 | 39.03 | 19.52 | 0.15 | 35.51 | 0.01 | 1.88 | 2.99 | 0.91 | TiCN-5 wt.% Si3N4 | 34.91 | 25.91 | 0.29 | 34.11 | 0.15 | 2.10 | 1.77 | 0.76 |
|
|