Deposition-Parameter-Determined Resistive Switching Characteristics in TiOx/Pb(Zr0.52Ti0.48)O3 Bilayers
Figure 2
curves of Pt/PZT/LSMO (a), Pt//PZT/LSMO in which the layer is deposited at 30 (b), 80 (c), 150 (d), and 300°C (e) in 2.0 Pa oxygen pressure and Pt//LSMO in which the layer is deposited at 30°C in 2.0 Pa oxygen pressure (f). The arrows indicate the voltage sweeping directions. The inset in (b) shows the curves measured after the PZT layer is poled to opposite directions.
(a) PZT |
(b) (2.0 Pa, 30°C)/PZT |
(c) (2.0 Pa, 80°C)/PZT |
(d) (2.0 Pa, 150°C)/PZT |
(e) (2.0 Pa, 300°C)/PZT |
(f) (2.0 Pa, 30°C) |