A Cell-Based Smoothed XFEM for Fracture in Piezoelectric Materials
Table 4
Comparison of XFEM results and analytical solutions for electromechanical Griffith crack (shear load).
| Loading | Analytical solution | Mesh (I) | Mesh (II) | | CS-XFEM | XFEM | CS-XFEM | XFEM | /(MNm−3/2) | /(Cm−3/2) | /(MNm−3/2) | /(Cm−3/2) | /(MNm−3/2) | /(Cm−3/2) | /(MNm−3/2) | /(Cm−3/2) | /(MNm−3/2) | /(Cm−3/2) |
| Mechanical | 1.7724 × 10−1 | 0 | 1.7452 × 10−1 | 0 | 1.7315 × 10−1 | 0 | 1.7441 × 10−1 | 0 | 1.7295 × 10−1 | 0 | Electrical | 0 | 1.7724 × 10−4 | 0 | 1.7534 × 10−4 | 0 | 1.7392 × 10−4 | 0 | 1.7513 × 10−4 | 0 | 1.7372 × 10−4 | Mechanical + electrical | 1.7724 × 10−1 | 1.7724 × 10−4 | 1.7452 × 10−1 | 1.7534 × 10−4 | 1.7315 × 10−1 | 1.7392 × 10−4 | 1.7441 × 10−1 | 1.7513 × 10−4 | 1.7295 × 10−1 | 1.7372 × 10−4 |
|
|