Advances in Materials Science and Engineering / 2016 / Article / Tab 4 / Research Article
Effects of La and Ce Addition on the Modification of Al-Si Based Alloys Table 4 (a) Effect of La on recalescence observed in 356 alloy. (b) Effect of Ce on recalescence observed in 356 alloy. (c) Effect of La and Ce on recalescence observed in 356 alloy.
(a)
Alloy code Composition Recalescence of eutectic solidification Aimed Actual Te 1 Te 2 ΔTe te 1 te 2 Δte La (wt%) Ce (wt%) La (wt%) Ce (wt%) T10 0.2 0 0.17 0 570.0 570.0 0 0 0 0 T1 0.5 0 0.36 0 565.2 566.4 1.3 239.8 260.2 20.4 T3 1.5 0 1.25 0 560.9 563.2 2.0 257.0 281.2 24.2
(b) Alloy code Composition Recalescence of eutectic solidification Aimed Actual Te 1 Te 2 ΔTe te 1 te 2 Δte La (wt%) Ce (wt%) La (wt%) Ce (wt%) T11 0 0.2 0 0.08 562.1 562.8 0.7 326.8 367.0 40.2 T4 0 0.5 0 0.39 566.8 567.5 0.7 257.4 280.4 23.0 T5 0 1.0 0 0.82 566.2 566.8 0.6 255.0 277.2 22.2
(c) Alloy code Composition Recalescence of eutectic solidification Aimed Actual Te 1 Te 2 ΔTe te 1 te 2 Δte La (wt%) Ce (wt%) La (wt%) Ce (wt%) T7 0.5 0.5 0.44 0.382 567.0 567.0 0 0 0 0 T8 1.0 1.0 0.78 0.77 562.72 563.78 1.05 296.0 321.6 25.6 T9 1.5 1.5 1.27 1.531 558.45 561.08 2.61 321.4 355.2 33.8