Multiobjective Optimization of Turning Cutting Parameters for J-Steel Material
Table 3
Listing of undominated samples from full-factorial matrix.
| Pareto ID | ID # among 125 samples | (m/min) | (mm) | (mm/rev) | (µm) | (min/cm3) |
| P1 | 56 | 200 | 0.15 | 0.050 | 0.264 | 0.66667 | P2 | 36 | 175 | 0.20 | 0.050 | 0.296 | 0.57143 | P3 | 66 | 200 | 0.30 | 0.050 | 0.309 | 0.33333 | P4 | 47 | 175 | 0.40 | 0.075 | 0.381 | 0.19048 | P5 | 121 | 300 | 0.40 | 0.050 | 0.504 | 0.16667 | P6 | 98 | 250 | 0.40 | 0.100 | 0.518 | 0.10000 | P7 | 123 | 300 | 0.40 | 0.100 | 0.801 | 0.08333 | P8 | 99 | 250 | 0.40 | 0.150 | 1.222 | 0.06667 | P9 | 124 | 300 | 0.40 | 0.150 | 1.963 | 0.05556 | P10 | 125 | 300 | 0.40 | 0.200 | 2.861 | 0.04167 |
|
|
Sample is within the “knee-cap” zone of the Pareto frontier.
|