Multiobjective Optimization of Turning Cutting Parameters for J-Steel Material
Table 5
Listing of undominated samples from m-EGO.
| Pareto ID | (m/min) | (mm) | (mm/rev) | (µm) | (min/cm3) |
| E1 | 200 | 0.30 | 0.050 | 0.309 | 0.33333 | E2 | 223 | 0.31 | 0.050 | 0.374 | 0.28695 | E3 | 200 | 0.40 | 0.050 | 0.434 | 0.25000 | E4 | 259 | 0.40 | 0.050 | 0.443 | 0.19279 | E5 | 300 | 0.40 | 0.050 | 0.504 | 0.16667 | E6 | 250 | 0.40 | 0.100 | 0.518 | 0.10000 | E7 | 300 | 0.40 | 0.100 | 0.801 | 0.08333 | E8 | 250 | 0.40 | 0.150 | 1.222 | 0.06667 | E9 | 300 | 0.40 | 0.150 | 1.963 | 0.05556 | E10 | 300 | 0.40 | 0.200 | 2.861 | 0.04167 |
|
|
Sample is within the “knee-cap” zone of the Pareto frontier.
|