Potential of New-Generation Electron Beam Technology in Interface Modification of Cold and HVOF Sprayed MCrAlY Bond Coats

Table 1

Properties of as-sprayed and EB treated samples.

Sample	Thickness; (m)	Young’s modulus; (GPa)	Instrumented hardness; (GPa)	Porosity; (%)	Roughness; (, m)
CS-A	756	8008 ± 285	171 ± 14	0.13	11.7
CS-B	1197	5114 ± 239	190 ± 5	0.05	2.7
CS-C	924	5416 ± 266	206 ± 6	0.02	2.1
HVOF-A	40	8175 ± 325	174 ± 8	5.81	6.1
HVOF-B	37	6821 ± 434	184 ± 11	4.15	5.7
HVOF-C	43	4641 ± 57	186 ± 7	1.67	3.5