Synthesis and Thermomechanical Characterization of Nylon 6/Cu Nanocomposites Produced by an Ultrasound-Assisted Extrusion Method
Table 2
Mechanical properties and standard deviation of Nylon 6 and the nanocomposites.
| Nylon 6/nano-Cu | Tensile strength (MPa) | Tensile modulus (MPa) | Tensile elongation at break (%) |
| Nylon 6 | 65.13 ± 1.70 | 464.22 ± 10.12 | 3.00 ± 0.09 | 99.09/0.01 | 66.42 ± 1.42 | 475.08 ± 8.85 | 2.54 ± 0.06 | 99.05/0.05 | 69.39 ± 1.05 | 534.27 ± 11.26 | 2.11 ± 0.05 | 99.90/0.10 | 70.95 ± 1.30 | 582.13 ± 7.34 | 1.14 ± 0.03 | 99.95/0.50 | 64.05 ± 0.73 | 555.82 ± 12.41 | 1.38 ± 0.04 |
|
|
The total weight of each sample is of 100 g. Values shown with a ± symbol belong to the standard deviation. |