Improvements in the Rheological Properties, Impact Strength, and the Biodegradability of PLA/PCL Blend Compatibilized by Electron-Beam Irradiation in the Presence of a Reactive Agent

<div>Complex viscosities (measured at 190°C) of pure PLA (▲), pure PCL (△), uncompatibilized PLA/PCL (90/10) (○), and compatibilized PLA/PCL (90/10) blends irradiated at 5 kGy (◇), 10 kGy (◆), 20 kGy (•), 50 kGy (□), 100 kGy (■), and 200 kGy (╋).</div>