Additive Manufacturing of Cobalt-Based Dental Alloys: Analysis of Microstructure and Physicomechanical Properties
Table 1
Tensile properties of Co-Cr-Mo and Co-Cr-W.
| Alloy, condition, and inclination (Φ) | Young’s modulus E (GPa) | Yield strength RP0.2 (MPa) | Elongation at failure At (%) | Ultimate tensile strength Rm (MPa) | Mean | SD | Mean | SD | Mean | SD | Mean | SD |
| Co-Cr-Mo 0°_AB | 98.38 | 17.01 | 702 | 15.4 | 5.7 | 1.04 | 923 | 32.4 | Co-Cr-Mo 0°_HT | 156.48 | 19.50 | 819 | 29.1 | 13.3 | 2.32 | 1097 | 21.6 |
| Co-Cr-Mo 30°_AB | 105.32 | 19.39 | 783 | 23.7 | 6.7 | 1.94 | 1102 | 45.2 | Co-Cr-Mo 30°_HT | 149.73 | 6.29 | 1002 | 41.1 | 8.3 | 0.81 | 1262 | 14.1 |
| Co-Cr-Mo 60°_AB | 112.11 | 58.51 | 696 | 34.3 | 7.5 | 2.10 | 1012 | 24.0 | Co-Cr-Mo 60°_HT | 105.67 | 13.18 | 808 | 37.8 | 9.4 | 1.32 | 1054 | 20.9 |
| Co-Cr-Mo 90°_AB | 100.21 | 6.95 | 674 | 9.0 | 14.8 | 1.62 | 1033 | 12.4 | Co-Cr-Mo 90°_HT | 164.54 | 15.10 | 757 | 7.2 | 16.7 | 1.51 | 1052 | 6.3 |
| Co-Cr-W 0°_AB | 183.44 | 15.58 | 917 | 9.9 | 11.1 | 1.14 | 1263 | 8.6 | Co-Cr-W 0°_HT | 216.32 | 21.99 | 655 | 26.6 | 15.0 | 1.54 | 1111 | 8.9 |
| Co-Cr-W 30°_AB | 147.50 | 20.57 | 965 | 5.9 | 10.4 | 1.31 | 1272 | 10.3 | Co-Cr-W 30°_HT | 186.96 | 7.90 | 651 | 4.9 | 15.5 | 1.04 | 1127 | 12.3 |
| Co-Cr-W 60°_AB | 167.17 | 26.23 | 845 | 11.1 | 17.1 | 1.35 | 1247 | 6.1 | Co-Cr-W 60°_HT | 214.51 | 29.25 | 669 | 20.0 | 18.0 | 2.90 | 1162 | 13.4 |
| Co-Cr-W 90°_AB | 138.55 | 6.93 | 755 | 8.7 | 24.3 | 0.70 | 1188 | 6.3 | Co-Cr-W 90°_HT | 202.35 | 22.08 | 658 | 7.1 | 16.9 | 1.51 | 1108 | 10.9 |
|
|