Oxygen Defect-Mediated Magnetism in Fe-C Codoped TiO<sub>2</sub>

Zou, Zhaorui; Zhou, Zhongpo; Wang, Haiying; Du, Meng

doi:https://doi.org/10.1155/2016/6270129

Advances in Materials Science and Engineering

On this page

Abstract Introduction Calculations Results Conclusions Acknowledgments References Copyright Related Articles

Research Article | Open Access

Volume 2016 | Article ID 6270129 | https://doi.org/10.1155/2016/6270129

Oxygen Defect-Mediated Magnetism in Fe-C Codoped TiO₂

Zhaorui Zou,^1,2Zhongpo Zhou ,^1,2,3Haiying Wang ,^1,2and Meng Du^1,2

Academic Editor: Pavel Lejcek

Received11 Jun 2016

Revised15 Aug 2016

Accepted24 Aug 2016

Published20 Sept 2016

Abstract

The magnetic properties of the C doped and C-Fe codoped TiO₂ films fabricated by sol-gel and spin coating have been investigated combining experiments and first-principles calculations. All the samples exhibit the anatase crystal phase and the room temperature ferromagnetism. The values of the saturation magnetizations are in the order of Fe-C codoped TiO₂ > Fe-C codoped TiO₂ (annealed in O₂) > C doped TiO₂ > C doped TiO₂ (annealed in O₂). The calculated net moment values are in the order of Fe-C codoped TiO₂ > C doped TiO₂ with oxygen vacancies existing, in accord with the experimental results. The hybridization of Fe 3d, C 2p, and O 2p (nearest to the Fe defect) led to the spin split of Fe 3d, C 2p, and O 2p which contributed to the ferromagnetism.

1. Introduction

Diluted magnetic semiconductors (DMSs) are promising candidates for the spin-polarized devices such as magnetooptical, nonvolatile storage and other spin logical devices [1]. However, most of these DMSs have relatively low Curie temperatures (), reducing their practical usefulness. In the recent decades, oxide diluted magnetic semiconductors such as ZnO [2], SnO₂ [3], and TiO₂ [4] doped with magnetic transition metal elements have attracted considerable attention, due to the discovery of room temperature (RT) ferromagnetism (FM) in these systems. Several theoretical investigations have been reported, most of which focus on the cation vacancies in TiO₂ bulk materials [5–10]. However, recent studies showed that the unexpected RT FM is closely related to the oxygen vacancies (Vos) instead of the cation vacancies [11–17]. Vo is a type of defects in TiO₂ which can be manipulated relatively easily during the synthesis processing [17]. Near the surface or in the bulk, Vos can lead to ferromagnetism enabling a possible application for TiO₂ as a magnetic semiconductor in spintronics [18].

In TiO₂ based DMSs, it is concluded that there are four factors related to the observed ferromagnetism: the Vos, cation vacancies, transition metal dopants, and the change of titanium oxidation state (Ti³⁺) [16]. On the one hand, the Vos can cause an obvious change in the band structure and make a significant contribution to the FM. On the other hand, the transition metal elements which have unpaired d-electrons can provide magnetic moment to the DMSs. In this paper, we have investigated the electronic and magnetic properties of transition metal (Fe), nonmetal C, and Vos codoped anatase TiO₂ (Ti₃₁FeO₆₂C) combining the experiments and the first-principles calculations based on the density-functional theory (DFT). The experimental results are consistent with the first-principles calculations. The magnetism induced by the Fe and C (Fe-C) codoping is investigated being associated with the defect electrons. The connections between doped Fe ions, C ions, and Vos are discussed to explain the ferromagnetism observed in these materials.

2. Experiments and Calculations

The C doped TiO₂ films, C doped TiO₂ films (annealed in O₂), Fe-C codoped TiO₂ films, and Fe-C codoped TiO₂ films (annealed in O₂) were prepared by sol-gel and spin-coating methods. A clear solution was prepared by reacting tetrabutyl titanate (C₁₆H₃₆O₄Ti) and nanotube carbon (C) with a mixture of water and hydrochloric acid (HCl) in an ethanol (C₂H₅OH) diluted medium. The C doped TiO₂ films were spin-coated on the fluorine doped tin oxide (FTO) substrates with the mentioned solution. After the prebaking at 70°C for 30 min, these films were annealed at 450°C for 2 h in O₂ gas and in air to obtain the C doped and the Vos-decreased C doped TiO₂ films, respectively. To get the Fe-C codoped samples, iron nitrate hydrate was added into deionized water; and the C doped TiO₂ films were immersed in the solution for 1 hour. Following the same procedure as that for the C doped and the Vos-decreased C doped TiO₂ samples, the Fe-C codoped and the Vos-decreased Fe-C codoped samples were prepared.

The crystal structures were characterized by X-ray diffraction (XRD, Bruker D8 Discover) with Cu Kα radiation (λ = 1.54 Å). The electronic structures were measured by the X-ray photoelectron spectroscopy (XPS) and the binding energy of the XPS spectra was calibrated with reference to the C 1s peak at 284.6 eV. The optical absorption spectra in the wavelength range of 200–800 nm were measured by using ultraviolet-visible near infrared spectrophotometer (CARY5000, Varian) at RT under the diffuse reflection mode with the integrating sphere. The photoluminescence (PL) spectra were conducted by using the 325 nm He–Cd laser (20 MW) as an excitation light source. The magnetic properties were studied using a vibrating-sample magnetometer (VSM) equipped in the physical property measurement system (PPMS, Quantum Deign). The magnetization loops were recorded with the magnetic field from −1 T to 1 T (T is the abbreviation of Tesla) applied parallel to the samples surfaces.

First-principles calculations based on spin-polarized density-functional theory and projector augmented wave (PAW) pseudopotential technique are performed as implemented within the Vienna Ab-Initio Simulation Package (VASP) [19, 20]. The generalized gradient approximation (GGA-PBE) for the wave functions is used with a cutoff of 400 eV to model the exchange and correlation functional [21]. The calculations have been carried out for three cases: (1) one oxygen (O) atom is substituted by a Vo (Ti₃₂O₆₃); (2) two O atoms are substituted by a Vo and a C atom (Ti₃₂O₆₂C); (3) a titanium (Ti) atom and two O atoms are substituted by an Fe atom, a , and a C atom (Ti₃₁FeO₆₂C). The Monkhorst-Pack scheme -points grid sampling was set to be 2 × 2 × 5 for the 95-atom anatase supercell. The valence electrons configurations for the O, C, Ti, and Fe are 2s² 2p⁴, 2s² 2p², 3s² 3p⁶ 3d² 4s², and 3d³ 4s², respectively. All the atomic positions are fully optimized until the atom forces drop below the value 0.02 eV/Å.

3. Results and Discussions

Figure 1 exhibits the XRD patterns of the C doped TiO₂ films, C doped TiO₂ films (annealed in O₂), Fe-C codoped TiO₂ films, and Fe-C codoped TiO₂ films (annealed in O₂). It can be seen that the XRD diffraction peaks of the undoped TiO₂ film appearing around 25.3°, 36.9°, 37.8°, 38.5°, 48.0°, 53.9°, 55.0°, 62.1°, 62.6°, 68.7°, 70.2°, and 75.0° are indexed to (101), (103), (004), (112), (200), (105), (211), (213), (204), (116), (220), and (215) of the anatase phase (JCPDS, number 21-1272); and the XRD diffraction peaks at 26.7°, 34.0°, 51.7°, and 65.8° are referred to as FTO (110), (101), (211), and (301). No signals of impurities such as rutile, FeTiO₃, or Fe cluster are detected. In addition, for the C doped TiO₂ films (annealed in O₂) and Fe-C codoped TiO₂ films (annealed in O₂), the XRD diffraction peaks show a relative lower intensity and a wider full width at half maximum (FWHM) comparing with the XRD data of C doped TiO₂ films and Fe-C codoped TiO₂ films. The average particle sizes of all the films were calculated and estimated using Scherrer equation choosing the Brag angle at (101), (004), and (200) diffraction peak. It is shown that the values of average particle size are 24.5 nm and 26.8 nm, for the C doped TiO₂ films and Fe-C codoped TiO₂ films, respectively. After the sample was annealed in O₂ gas, the values of average particle size decreased to 18.2 nm and 23.6 nm for the C doped TiO₂ films and Fe-C codoped TiO₂ films. The variation of the particle size originates from the difference of the doped element (Fe or C) and annealing gas (O₂).

Figure 2 demonstrates the XPS core levels for O-1s, C-1s, and Fe-2p of the Fe-C codoped TiO₂ films. As it is shown in Figure 2(a), the core level spectrum of O-1s is fitted with two peaks at 530.14 eV and 531.70 eV, attributed to O 1s in Ti-O linkages and Ti-O-C bonds of TiO₂, respectively. Figure 2(b) shows the core level spectrum of C-1s which can be fitted by four peaks at 284.84 eV, 286.71 eV, 283.6 eV, and 288.60 eV, respectively. The peak of 284.84 eV clearly arises from adventitious element carbon which also exists in the case of pure TiO₂ samples. The peaks at 286.71 eV, 283.6 eV, and 288.60 eV are attributed to C-O and C-Ti and COOH binding, respectively. Therefore, multiple carbon species, namely, substitutional and interstitial carbon atoms and carbonate species, coexist in the lattice of TiO₂. Figure 2(c) reveals the Fe 2p core level XPS spectrum. Apparently, there are two main peaks of Fe 2p_3/2 and Fe 2p_1/2 located at 710.71 eV and 724.52 eV, respectively, close to the binding energy of Fe³⁺ ion which indicates the existence of Fe³⁺ [22]. It is noticed that there is no weak peak at binding energy around 709 eV introduced by the contribution of Fe²⁺ ion in the spectrum.

(a)

(b)

(c)

Figure 3(a) illustrates the UV-Vis absorption spectra for these samples, which exhibit the characteristic spectrum of TiO₂ with its fundamental absorption edge around 384 nm (3.2 eV of band-gap energy). The absorption edges of the C doped TiO₂ films, C doped TiO₂ films (annealed in O₂), Fe-C codoped TiO₂ films, and Fe-C codoped TiO₂ films (annealed in O₂) are 387 nm, 370 nm, 399 nm, and 392 nm, with calculated band-gap energy of 3.20 eV, 3.35 eV, 3.11 eV, and 3.16 eV, respectively, similar to those reported in [23, 24]. Comparing with the samples annealed in O₂ atmosphere, the absorption edges of the C doped and Fe-C codoped TiO₂ films both shifted slightly toward the visible light range. The values of the band gap are in the following order: Fe-C codoped TiO₂ > Fe-C codoped TiO₂ (annealing in O₂) > C doped TiO₂ > C doped TiO₂ (annealing in O₂). The spectrum of Fe-C codoped sample yields the largest red shift which indicates the doping of Fe or C element may narrow the band gap.

(a)

(b)

Figure 3(b) presents the PL spectra of C doped TiO₂ films, C doped TiO₂ films (annealing in O₂), Fe-C codoped TiO₂ films, and Fe-C codoped TiO₂ films (annealing in O₂) at RT. The PL spectra are very sensitive to the stoichiometry and surface states for materials, which can provide information on electronic and optical properties [25, 26]. All the PL spectra of the specimens show two strong emission peaks at 468 nm and 480 nm, which are attributed to the Vos [27, 28]. The emission peaks corresponding to the defects are largely enhanced after annealing in O₂ gas.

Figure 4 shows the plots of magnetization () versus applied magnetic field () which demonstrate hysteresis behaviour in all samples measured by a VSM with the magnetic field from −1 to 1 T at RT. The values of the saturation magnetization () are in the following order: the C doped TiO₂ (annealed in O₂) < C doped TiO₂ < Fe-C codoped TiO₂ (annealed in O₂) < Fe-C codoped TiO₂.

In order to understand the origin of RT FM in the Fe-C codoped TiO₂ films, the first-principles calculations are performed. The positions of , Ti, Fe, C, and O for -Fe-C codoped TiO₂ are the same as those of the doped TiO₂ and the -C codoped TiO₂. Firstly, when there exists only one Vo in the supercell, each Vo is assumed to donate two electrons. The result indicates that the two electrons created by one Vo are shared by three equivalent Ti³⁺ ions with up-spin of three different directions, which is similar to the results reported by Yang et al. [29]. The calculated net magnetic moment of the system is about 0.533 , which is related to the denoted two electrons that occupy the three neighboring Ti sites. The second and the third scenarios are -C codoped TiO₂ (Ti₃₂O₆₂C) and -Fe-C codoped TiO₂ (Ti₃₁FeO₆₂C), respectively.

Figure 5 shows the TDOS and PDOS of Vo-C codoped TiO₂ and Vo-Fe-C codoped TiO₂, respectively. The calculated band gaps using the GGA functional are about 2.09 eV for the Vo-C codoped TiO₂ and Vo-Fe-C codoped TiO₂, which is lower than the experimental value of 3.20 eV. However, the reduced band gap has nearly no influence on the magnetic state of C doped anatase TiO₂ and Fe-C codoped TiO₂.

(a)

(b)

Figure 5(a) shows the TDOS and PDOS of C 2p electrons for Vo-C codoped TiO₂ samples. It can be seen from Figure 5(a)I that there is no spin splitting around the Fermi level, which illustrates that the Vo-C codoped TiO₂ samples have no magnetic property. For the PDOS of C 2p electrons (in Figure 5(a)II) nearest to the Vo, there are also no exchange splitting around the Fermi level between the spin-up and spin-down states, lying within the band gap. With respect to the local Cartesian coordinate, the up-spin and down-spin of C , C , and C states are all occupied. This indicates that the two electrons, created by one Vo, were trapped by the doped C atom. As a result, the valence electrons configuration for doped C atom is 1s² 2p⁶, which produces 0 net magnetic moment.

Figure 5(b)I exhibits the TDOS for Vo-Fe-C codoped TiO₂ sample. It can be seen that a part splitting between the spin-up and spin-down states around the Fermi level is shown illustrating the existence of magnetism. For the PDOS of Fe 3d electrons (in Figure 5(b)II), the Fe 3d states are spin-polarized and lie within the band gap of Vo-Fe-C codoped TiO₂. With respect to the local Cartesian coordinate, the spin-up and spin-down states of Fe are occupied, while for Fe , Fe , and Fe the spin-up states are occupied; for Fe 3d_xy, only a few spin-down states are occupied. Noticeably, there are no spin-up and spin-down states of Fe occupied. This indicates that each doped Fe atom at the Ti site produces the net magnetic moments of 2.538 , and its electron configuration can be resembled as Fe³⁺ (3d⁵). For the PDOS of C 2p electrons (in Figure 5(b)III), the C 2p states are spin-polarized and lie within the band gap of Vo-Fe-C codoped TiO₂. With respect to the local Cartesian coordinate, the spin-up and spin-down states of C and C are all occupied, while, for C , the spin-down C states are occupied and partly spin-up states are not; as a result, the valence electrons configuration for the doped C atom is 1s² 2p⁵. This indicates that each doped C atom at the O site produces −0.025 net magnetic moments. For the PDOS of O 2p electrons (in Figure 5(b)IV), the C 2p states are partly spin-polarized and lie within the band gap of Vo-Fe-C codoped TiO₂. With respect to the local Cartesian coordinate, the spin-up and spin-down states of O , O , and C are all occupied, but the slightly spin-up states of O appear around Fermi level energy; as a result, the valence electrons configuration for O atom is 1s² 2p⁶. The calculated net magnetic moment of O atom nearest to doped Fe atom is 0.075 .

To analyze the spin polarization induced by the doped Fe atom and C atom, we calculated the spin density distribution Fe and C atom. The calculated results are that the magnetic moment is mainly delocalized around the Fe atom, namely, about 2.538 on the Fe atom, about −0.025 on the C atom, about 0.079 on the nearest-neighbor O atom, and about 0.029 on the second-neighbor O atom. The calculated result indicates that the magnetic orbital describing the doped Fe, Vo, and C center extends to the second-nearest-neighbor O atoms. One of the two electrons created by the Vo is trapped by the doped C atom, and the other one is shared by Fe, C, and O atoms surrounding it. The total magnetic moment is 3.216 for the Vo-Fe-C codoped TiO₂.

Combining all the results presented above, we introduced a defect electron based model for the observed ferromagnetism. The magnetic moment is associated with a Vo, C^2-/Vo/Ti⁴⁺, and C^2-/Fe³⁺/Vo complex for Vo-C codoped TiO₂ and Vo-Fe-C codoped TiO₂, respectively. The magnetic orbitals extend to nearest neighbor and second neighbor around the complex. In the two models, the two electrons denoted by Vo mediate the coupling of C^2-/Vo/Ti⁴⁺ and C^2-/Fe³⁺/Vo complex, possessing the characteristics of 3d electrons of Ti⁴⁺ and Fe³⁺, occupying C 2p site, partly O 2p sites, and Fe³⁺ site. This is the original signal of the C^2- and Fe³⁺, which also can be used to explain the reason that there is only Ti⁴⁺ signal appearing in XPS spectra. The value of total magnetic moment for Vo-Fe-C codoped TiO₂ and Vo-C doped TiO₂ is in the same order of for Fe-C codoped TiO₂ and C doped TiO₂.

4. Conclusions

In summary, the RT FM properties of the C doped TiO₂ films and Fe-C codoped TiO₂ films have been investigated. The values of the saturation magnetizations are in the order of Fe-C codoped TiO₂ > Fe-C codoped TiO₂ (annealed in O₂) > C doped TiO₂ > C doped TiO₂ films (annealed in O₂). The calculated net moment values are in the order of Fe-C codoped TiO₂ > C doped TiO₂ with Vos existing, which are in accord with the experimental results. These calculations suggest the key factor for the formation of ferromagnetic ordering is the Vo which contributes two electrons to the doped C atom and neighboring O sites. The hybridization of Fe 3d, C 2p (nearest to the Fe atom), and O 2p (nearest to the Fe defect) led to the spin splitting of Fe 3d, C 2p, and O 2p which contributed to the magnetism. The unique characteristic of the defect electrons denoted by a Vo in Fe-C codoped TiO₂ and C doped TiO₂ is that they provide the means for the percolation of the magnetic complexes to achieve magnetization in the Fe-C codoped samples.

Competing Interests

The authors declare that there is no conflict of interests regarding the publication of this paper.

Acknowledgments

This work is supported by the NSFC nos. 11404100, 11175135, 10904116, and 11304083, the Key Scientific and Technological Project of Henan Province no. 102102210186, the Postdoctoral Research Foundation of Henan Normal University no. 01026500204, and the Scientific Research Foundation for Ph.D. of Henan Normal University nos. 01026500257 and 01026500121. This work is also supported by the High Performance Computing Center of Henan Normal University.

References

B. Pal and P. K. Giri, “High temperature ferromagnetism and optical properties of Co doped ZnO nanoparticles,” Journal of Applied Physics, vol. 108, no. 8, Article ID 084322, 2010.
View at: Publisher Site | Google Scholar
K. Ueda, H. Tabata, and T. Kawai, “Magnetic and electric properties of transition-metal-doped ZnO films,” Applied Physics Letters, vol. 79, no. 7, pp. 988–990, 2001.
View at: Publisher Site | Google Scholar
X. Liu, J. Iqbal, Z. Wu, B. He, and R. Yu, “Structure and room-temperature ferromagnetism of Zn-doped SnO₂ nanorods prepared by solvothermal method,” The Journal of Physical Chemistry C, vol. 114, no. 11, pp. 4790–4796, 2010.
View at: Publisher Site | Google Scholar
R. K. Singhal, A. Samariya, S. Kumar et al., “Study of defect-induced ferromagnetism in hydrogenated anatase TiO₂:Co,” Journal of Applied Physics, vol. 107, no. 11, Article ID 113916, 2010.
View at: Google Scholar
Y. Bai and Q. Chen, “First principle study of the cation vacancy in anatase TiO₂,” Physica Status Solidi—Rapid Research Letters, vol. 2, no. 1, pp. 25–27, 2008.
View at: Publisher Site | Google Scholar
H. Peng, J. Li, S.-S. Li, and J.-B. Xia, “Possible origin of ferromagnetism in undoped anatase TiO₂,” Physical Review B—Condensed Matter and Materials Physics, vol. 79, no. 9, Article ID 092411, 4 pages, 2009.
View at: Publisher Site | Google Scholar
N. Yu and J. W. Halley, “Electronic structure of point defects in rutile TiO₂,” Physical Review B, vol. 51, no. 8, pp. 4768–4776, 1995.
View at: Publisher Site | Google Scholar
E. Cho, S. Han, H.-S. Ahn, K.-R. Lee, S. K. Kim, and C. S. Hwang, “First-principles study of point defects in rutile TiO_2−x,” Physical Review B, vol. 73, no. 19, Article ID 193202, 2006.
View at: Publisher Site | Google Scholar
S.-G. Park, B. Magyari-Köpe, and Y. Nishi, “Electronic correlation effects in reduced rutile TiO₂ within the LDA + U method,” Physical Review B, vol. 82, no. 11, Article ID 115109, 2010.
View at: Publisher Site | Google Scholar
M. Setvin, C. Franchini, X. Hao et al., “Direct view at excess electrons in TiO₂ rutile and anatase,” Physical Review Letters, vol. 113, no. 8, Article ID 086402, 5 pages, 2014.
View at: Publisher Site | Google Scholar
M. Wang, M. Feng, and X. Zuo, “First principles study of the electronic structure and magnetism of oxygen-deficient anatase TiO₂ (0 0 1) surface,” Applied Surface Science, vol. 292, no. 4, pp. 475–479, 2014.
View at: Publisher Site | Google Scholar
Z. Zhou, H. Wang, and Z. Yang, “Intrinsic defect-mediated magnetism in Fe-N codoped TiO₂,” Journal of Alloys and Compounds, vol. 657, pp. 372–378, 2016.
View at: Publisher Site | Google Scholar
A. T. Brant, N. C. Giles, S. Yang et al., “Ground state of the singly ionized oxygen vacancy in rutile TiO₂,” Journal of Applied Physics, vol. 114, no. 11, Article ID 113702, 2013.
View at: Publisher Site | Google Scholar
A. M. M. Navarro, C. E. R. Torres, V. Bilovol, A. F. Cabrera, L. A. Errico, and M. Weissmann, “Study of the relation between oxygen vacancies and ferromagnetism in Fe-doped TiO₂ nano-powders,” Journal of Applied Physics, vol. 115, no. 22, Article ID 223908, 2014.
View at: Publisher Site | Google Scholar
B. Shao, Y.-F. He, M. Feng, Y. Lu, and X. Zuo, “Unexpected magnetic anisotropy induced by oxygen vacancy in anatase TiO₂: a first-principles study,” Journal of Applied Physics, vol. 115, no. 17, Article ID 17A915, 2014.
View at: Publisher Site | Google Scholar
X. J. Wang, Y. L. Song, L. L. Tao et al., “Origin of ferromagnetism in aluminum-doped TiO₂ thin films: theory and experiments,” Applied Physics Letters, vol. 105, no. 26, Article ID 262402, 2014.
View at: Publisher Site | Google Scholar
C. Lin, D. Shin, and A. A. Demkov, “Localized states induced by an oxygen vacancy in rutile TiO₂,” Journal of Applied Physics, vol. 117, no. 22, Article ID 225703, 2015.
View at: Publisher Site | Google Scholar
R. Janisch, P. Gopal, and N. A. Spaldin, “Transition metal-doped TiO₂ and ZnO—present status of the field,” Journal of Physics: Condensed Matter, vol. 17, no. 27, pp. R657–R689, 2005.
View at: Publisher Site | Google Scholar
G. Kresse and D. Joubert, “From ultrasoft pseudopotentials to the projector augmented-wave method,” Physical Review B, vol. 59, no. 3, pp. 1758–1775, 1999.
View at: Publisher Site | Google Scholar
G. Kresse and J. Furthmüller, “Efficient iterative schemes for ab initio total-energy calculations using a plane-wave basis set,” Physical Review B-Condensed Matter and Materials Physics, vol. 54, no. 16, pp. 11169–11186, 1996.
View at: Publisher Site | Google Scholar
J. P. Perdew, K. Burke, and M. Ernzerhof, “Generalized gradient approximation made simple,” Physical Review Letters, vol. 77, no. 18, pp. 3865–3868, 1996.
View at: Publisher Site | Google Scholar
C. D. Wagner, W. M. Riggs, L. E. Davis, and J. F. Moulder, G.E. Muilenberg, editor, Perkin Elmer Corporation (Physical Electronics Division), Eden Prairie, Minn, USA, 1979.
J. Yu, Q. Xiang, and M. Zhou, “Preparation, characterization and visible-light-driven photocatalytic activity of Fe-doped titania nanorods and first-principles study for electronic structures,” Applied Catalysis B: Environmental, vol. 90, no. 3-4, pp. 595–602, 2009.
View at: Publisher Site | Google Scholar
W. Choi, A. Termin, and M. R. Hoffmann, “The role of metal-ion dopants in quantum-sized TiO₂: correlation between photoreactivity and charge-carrier recombination dynamics,” Journal of Physical Chemistry, vol. 98, no. 51, pp. 13669–13679, 1994.
View at: Publisher Site | Google Scholar
Y. Lei, L. D. Zhang, G. W. Meng et al., “Preparation and photoluminescence of highly ordered TiO₂ nanowire arrays,” Applied Physics Letters, vol. 78, no. 8, pp. 1125–1127, 2001.
View at: Publisher Site | Google Scholar
C. Huang, X. Liu, L. Kong, W. Lan, Q. Su, and Y. Wang, “The structural and magnetic properties of Co-doped titanate nanotubes synthesized under hydrothermal conditions,” Applied Physics A: Materials Science and Processing, vol. 87, no. 4, pp. 781–786, 2007.
View at: Publisher Site | Google Scholar
J. H. Cho, B. Y. Kim, H. D. Kim et al., “Enhanced ferromagnetism in Co-doped TiO₂ powders,” Physica Status Solidi B: Basic Research, vol. 241, no. 7, pp. 1537–1540, 2004.
View at: Publisher Site | Google Scholar
P. M. Kumar, S. Badrinarayanan, and M. Sastry, “Nanocrystalline TiO₂ studied by optical, FTIR and X-ray photoelectron spectroscopy: correlation to presence of surface states,” Thin Solid Films, vol. 358, no. 1-2, pp. 122–130, 2000.
View at: Publisher Site | Google Scholar
K. Yang, Y. Dai, B. Huang, and Y. P. Feng, “Density-functional characterization of antiferromagnetism in oxygen-deficient anatase and rutile TiO₂,” Physical Review B-Condensed Matter and Materials Physics, vol. 81, no. 3, Article ID 033202, 2010.
View at: Publisher Site | Google Scholar

Copyright

Copyright © 2016 Zhaorui Zou et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

PDF Download Citation

Download other formats

Order printed copies

Views

807

Downloads

759

Citations

Advances in Materials Science and Engineering

Oxygen Defect-Mediated Magnetism in Fe-C Codoped TiO2

Abstract

1. Introduction

2. Experiments and Calculations

3. Results and Discussions

4. Conclusions

Competing Interests

Acknowledgments

References

Copyright

Oxygen Defect-Mediated Magnetism in Fe-C Codoped TiO₂