The Effect of Interaction between Nanofillers and Epoxy on Mechanical and Thermal Properties of Nanocomposites: Theoretical Prediction and Experimental Analysis

Table 3

Tensile strength properties of block specimens: neat, MMT, and CNT epoxy composites.

Content	Neat Epoxy		CNT- Epoxy		MMT-Epoxy
Rate, mm.min^−1	0.5	2	0.5	2	0.5	2
Bending strength, MPa	886.28	670.39	894.05	697.60	1250.69	977.42
Bending modulus, GPa	1.71	1.540	2.040	3.095	1.518	1.485
Elongation ε, %	2.55	2.13	2.14	2.23	7.58	3.79
Stress, MPa	36.63	27.71	36.95	28.83	58.37	40.40