Research Article
Interrelationships of Pressure-Dependent Hole Fraction and Elongational Viscosity in Polymer Melts
Table 4
Values of parameters of (
7) evaluated for
at different elongational stresses.
| Polymer | σc (kPa) | | | | | | R2 |
| LDPE60 | 500 800 1100 1400 | 7.27 6.74 6.57 6.54 | 69.62 83.59 87.59 87.68 | 0.136 0.163 0.1711 0.1713 | 0.0027 0.0046 0.0055 0.0057 | 1.31 1.56 1.57 1.45 | 0.99980 0.99969 0.99966 0.99971 |
| LDPE65 | 350 500 800 1100 | 8.41 8.15 7.84 7.77 | 58.14 64.45 74.56 77.07 | 0.115 0.128 0.148 0.152 | 0.00086 0.0011 0.0015 0.0016 | 2.85 1.54 1.31 1.43 | 0.99846 0.99963 0.99975 0.99968 |
| LLDPE | 800 1100 1400 | 8.15 7.46 6.24 | 70.54 84.85 112.06 | 0.189 0.23 0.30 | 0.0011 0.0022 0.0076 | 4.56 3.57 4.97 | 0.99725 0.99797 0.99642 |
| HDPE | 500 800 1100 1400 1700 2000 | 9.89 9.25 8.83 8.53 8.30 8.11 | 33.07 53.52 62.72 67.19 69.22 69.84 | 0.0540 0.0874 0.102 0.110 0.113 0.12 | 0.00023 0.00044 0.00066 0.00089 0.0011 0.0014 | 1.15 0.59 0.70 0.61 0.47 0.59 | 0.99980 0.99992 0.99992 0.99994 0.99996 0.99995 |
| PMMA | 1100 1400 1700 | -4.16 -2.89 -2.28 | 949.92 861.9 815.85 | 1.42 1.28 1.22 | 362.15 101.70 54.98 | 2.73 1.82 1.64 | 0.99840 0.99934 0.99960 |
| PC | 500 800 1100 1400 1700 2000 | 1.93 1.49 1.18 0.96 0.77 0.62 | 510.04 536.48 554.40 567.97 578.90 588.04 | 5.42 5.71 5.90 6.04 6.16 6.25 | 0.729 1.136 1.535 1.927 2.314 2.698 | 2.40 2.78 3.32 3.76 4.30 4.76 | 0.99895 0.99859 0.99810 0.99759 0.99708 0.99659 |
| PP | 350 500 800 | 7.99 6.37 5.33 | 55.21 137.53 170.44 | 0.052 0.13 0.161 | 0.0013 0.0066 0.0188 | 2.34 2.44 2.18 | 0.99885 0.99915 0.99940 |
| PS | 500 800 1100 1400 | 2.93 1.37 0.89 0.77 | 354.33 427.57 448.55 452.19 | 0.226 0.27 0.285 0.287 | 0.237 1.128 1.82 2.068 | 2.70 2.34 1.98 1.93 | 0.99849 0.99896 0.99925 0.99935 |
|
|