Combustion Synthesis of TiC-TiB₂-Based Cermets from Elemental Powders

Table 1

Comparison of mechanical properties between the sample in the present work (A) and that in literature (B) [13].

Sample	Composition	Relative density (%)	HV (kg/mm^2)	TRS (MPa)
A	TiC-TiB2-Ni	96.95	1950	330
	(52.5/17.5/30) vol.%
B	TiC-TiN-WC-Mo-Ni-C	99.98	1750	1521
	(40/10/15/14/20/1) wt.%