Optimization of Dry Sliding Wear Performance of Ceramic Whisker Filled Epoxy Composites Using Taguchi Approach
Table 3
Test conditions with output results using L 27 orthogonal array.
| SI. no | Sliding velocity (m/s) | Normal load (N) | Filler content (%) | Sliding distance (m) | Specific wear rate (mm3/N-km) | / ratio (db) |
| 1 | 0.50 | 10 | 5 | 500 | 0.132890 | 17.5301 | 2 | 0.50 | 10 | 10 | 1000 | 0.113821 | 18.8755 | 3 | 0.50 | 10 | 15 | 1500 | 0.074015 | 22.6136 | 4 | 0.50 | 20 | 5 | 1000 | 0.161960 | 15.8118 | 5 | 0.50 | 20 | 10 | 1500 | 0.132791 | 17.5366 | 6 | 0.50 | 20 | 15 | 500 | 0.150674 | 16.4392 | 7 | 0.50 | 30 | 5 | 1500 | 0.118125 | 18.5532 | 8 | 0.50 | 30 | 10 | 500 | 0.130081 | 17.7157 | 9 | 0.50 | 30 | 15 | 1000 | 0.100449 | 19.9611 | 10 | 0.75 | 10 | 5 | 1000 | 0.132890 | 17.5301 | 11 | 0.75 | 10 | 10 | 1500 | 0.113821 | 18.8755 | 12 | 0.75 | 10 | 15 | 500 | 0.095163 | 20.4307 | 13 | 0.75 | 20 | 5 | 1500 | 0.157807 | 16.0375 | 14 | 0.75 | 20 | 10 | 500 | 0.170732 | 15.3537 | 15 | 0.75 | 20 | 15 | 1000 | 0.138779 | 17.1535 | 16 | 0.75 | 30 | 5 | 500 | 0.149502 | 16.5071 | 17 | 0.75 | 30 | 10 | 1000 | 0.121951 | 18.2763 | 18 | 0.75 | 30 | 15 | 1500 | 0.102212 | 19.8100 | 19 | 1.00 | 10 | 5 | 1500 | 0.132890 | 17.5301 | 20 | 1.00 | 10 | 10 | 500 | 0.130081 | 17.7157 | 21 | 1.00 | 10 | 15 | 1000 | 0.111023 | 19.0917 | 22 | 1.00 | 20 | 5 | 500 | 0.224252 | 12.9853 | 23 | 1.00 | 20 | 10 | 1000 | 0.150407 | 16.4547 | 24 | 1.00 | 20 | 15 | 1500 | 0.132170 | 17.5773 | 25 | 1.00 | 30 | 5 | 1000 | 0.171650 | 15.3071 | 26 | 1.00 | 30 | 10 | 1500 | 0.130081 | 17.7157 | 27 | 1.00 | 30 | 15 | 500 | 0.126883 | 17.9319 |
|
|