Wear Resistance of (Diamond-Ni)-Ti6Al4V Gradient Materials Prepared by Combined Selective Laser Melting and Spark Plasma Sintering Techniques
Table 1
Composition of samples and SPS sintering conditions.
| ||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
- Preheating was performed at 260°C, 10 MPa and 6 Min. Sintering was done at 860°C for samples No. 1-6 and 1000°C for No. 7. - D=diamond, TA= Ti6Al4V titanium alloy powder, and L is added in case of Ti6Al4V lattice. - For No. 5 and No. 6, the average composition is stated due to gradient configuration. |