Hydroxyapatite Coating of Titanium Implants Using Hydroprocessing and Evaluation of Their Osteoconductivity

Figure 5

Surface and/or cross-sectional views of the samples with surface roughness. (a)–(c) bead-sintered porous samples (as sintered), (d)-(e) bead-sintered porous samples coated with HAp (thermal substrate method, 0.7 mM CaCl2 + 0.3 mM Ca(H2PO4)2, pH 7, 100°C, 15 min.).