Carbon Nanotubes Reinforced Composites for Biomedical Applications

Wang, Wei; Zhu, Yuhe; Liao, Susan; Li, Jiajia

doi:https://doi.org/10.1155/2014/518609

BioMed Research International

On this page

Abstract Introduction Conclusions Acknowledgments References Copyright Related Articles

Special Issue

Scaffolds Reinforced by Fibers or Tubes for Tissue Repair

View this Special Issue

Review Article | Open Access

Volume 2014 | Article ID 518609 | https://doi.org/10.1155/2014/518609

Carbon Nanotubes Reinforced Composites for Biomedical Applications

Wei Wang,¹Yuhe Zhu,¹Susan Liao,²and Jiajia Li¹

Academic Editor: Xiaoming Li

Received28 Dec 2013

Accepted17 Jan 2014

Published24 Feb 2014

Abstract

This review paper reported carbon nanotubes reinforced composites for biomedical applications. Several studies have found enhancement in the mechanical properties of CNTs-based reinforced composites by the addition of CNTs. CNTs reinforced composites have been intensively investigated for many aspects of life, especially being made for biomedical applications. The review introduced fabrication of CNTs reinforced composites (CNTs reinforced metal matrix composites, CNTs reinforced polymer matrix composites, and CNTs reinforced ceramic matrix composites), their mechanical properties, cell experiments in vitro, and biocompatibility tests in vivo.

1. Introduction

Carbon is an important element to various sciences, from physics, chemistry, and materials science to life science, but conventional carbon formulation in the micron scale may not be the optimal implant material [1]. Then the nanomaterials such as the carbon nanotubes (CNTs), with unique electrical, mechanical, and surface properties, have captured the attention and aroused the interest of many scientists, since CNTs were discovered by Iijima in 1991 and up to now appear well suited as a biomaterial [2–7]. CNTs are substances with cylindrical structure of about 1 nm diameter and 1–10 m length, consisting of only carbon atoms. In general, CNTs contain single-wall carbon nanotubes (SWCNTs) and multiwall carbon nanotubes (MWCNTs). SWCNTs are viewed as rolled-up structures of single sheets of graphene and individual carbon structures approximately 1 nm in diameter and up to a millimeter or more in length, and MWCNTs are similar to hollow graphite fibers, except that they have a much higher degree of structural perfection, which are having a diameter of 10–200 nm [8–11]. Lu and Tsai investigated the load transfer efficiency in double-walled carbon nanotubes (DWCNTs, a hollow cylindrical structure, which contains two concentric graphene layers) using multiscale finite element modeling, and the results showed that increasing of CNTs’ length can effectively improve the load transfer efficiency in the outermost layers, while the DWCNTs with incremental covalent bonds exhibit increasing load transfer efficiency in the inner layer. Besides, compared with SWCNTs, the DWCNTs still possess the less capacity of load transfer efficiency [12]. For MWCNTs, the outer graphene layers as well as the inner layers may be responsible for sustaining the applied load, and the load carrying capacity from the outermost layer to interior layers in MWCNTs associated with different interatomistic properties are waiting to be investigated thoroughly [12].

Treacy et al. measured the elastic modulus of MWCNTs to be 1TPa, on the same level of diamond. Compared with steel, the mechanical strength is 100 times higher of steel, but the density is only one sixth of the steel [13, 14]. Wang et al. studied the axial strength of MWCNTs and reported elastic modulus values ranging from 200 to 400 GPa, the bending modulus is to 14 GPa, and compression strength is about 100 GPa. The high deformation of CNTs allows it to break when tensile strength reaches 18% [15]. Iijima et al. investigated bending strength of CNTs, and their experimental results and theoretical studies have demonstrated that CNTs have extremely high tensile strengths, as high as 100 GPa [16, 17]. Depending on the outstanding quality of the CNTs, it is possible to use CNTs for composites reinforcement. It is also believed that the incorporation of CNTs into matrix materials should lead to composites with unique properties.

Compared with conventional carbon, CNTs are stronger and more flexible and have a higher tensile strength to weight ratio [18]. Since CNTs have a density even smaller than graphite due to the tube structure, and with sufficient high strength and excellent thermal and chemical stability, the CNTs material may be used as a structural material in the biomedical field [4, 19–24]. At present, CNTs are used as carriers for drug delivery and gene therapy, and CNTs have been shown effective to reinforce scaffolds for tissue engineering and regenerative medicine [25–30]. Since CNTs have pores and the pores of SWCNTs and MWCNTs were, respectively, less than 1 nm and 4–30 nm in diameter [31, 32], SWNTs and MWNTs might be available for tissue regeneration. Besides, CNTs have been used as supports for enzyme immobilization to improve biocatalyst performances such as activity, stability, and reusability [33]. CNTs can be easily separated by simple filtration [34] and enzymes can be adsorbed [35, 36] or covalently attached [37, 38] on surface of SWCNTs and MWCNTs. The study of Prlainovic showed that lipase can be successfully adsorbed on the surface of unmodified MWCNTs, and immobilized preparations were characterized, with FT-IR spectroscopy, AFM, and cyclic voltammetry [39]. As filler materials, CNTs are used to improve the properties of polymer composites [40].

To date, various composite materials have been prepared by incorporating SWCNTs or MWCNTs into a metal matrix, a ceramic matrix, or a polymer matrix (including SiC ceramic, SiN ceramic, quartz, Al₂O₃, and mental ceramic) [41–50]. And CNTs reinforced polymer matrix composites and CNTs reinforced ceramic matrix composites may be used as a structural material in the bone cement, bone filling material, and tissue engineering scaffolds [45–50]. Webster et al. fabricated polyurethane/CNTs composite, and the composite material possessed better electrical conductivity and mechanical properties, which can be used in neural tissue and bone [51, 52]. Deng et al. studied the use of MWCNT/chitosan (CHI) scaffolds, composed of MWCNTs (up to 89 wt%) and CHI and with a well-defined microchannel porous structure, as biocompatible and biodegradable supports for cell growth [53].

This review addresses the different synthetic methods, mechanical properties, and biocompatibility of CNTs-based reinforced composites, which may indicate that CNTs-based reinforced composites appear suited as biomaterials and may become useful scaffold materials for tissue engineering.

2. Fabrication of CNTs and CNTs-Based Reinforced Composites

2.1. Fabrication of CNTs

CNTs are generally prepared using five main synthesis methods containing ARC discharge, laser ablation, chemical vapor deposition (CVD), catalyst chemical vapor deposition (CCVD), and template-directed synthesis [54, 55]. Although arc discharge is a common method for CNTs synthesis, it is difficult to control the morphology of CNTs, such as length, diameter, and number of layers. Compared with arc-discharge and laser-ablation methods, CVD is most widely used for its low set-up cost, high production yield, and ease of scale-up [56]. CCVD is the most flexible and economic method for the production of CNTs; however, since many parameters influence the producing process, it is still very complex for precisely controlled growth of CNTs [54]. In the study of Disfani, MWCNTs produced by the catalytic carbon vapor deposition (CCVD) process were then functionalized, which were designated as CNTs-COOH, CNTs-OH, and CNTs-NH2. And different functionalized CNTs, as well as nonfunctionalized CNTs, were incorporated into a phenoxy resin via a melt mixing process [57].

2.2. Fabrication of CNTs-Based Reinforced Composites

2.2.1. Fabrication of CNTs Reinforced Metal Matrix Composites

CNTs reinforced the strength, hardness, abrasion, and wear properties and thermal of stability of metal, and CNTs reinforced metal matrix composites are prepared through a variety of processing techniques, such as powder metallurgy, the melt casting, spray forming, electrochemical deposition, and other novel techniques. At present, CNTs as reinforcement in Fe-matrix, Cu-matrix, Mg-matrix, and Ni-matrix composite materials have been successfully fabricated [58–62]. Kuzumaki et al. produced CNTs reinforced aluminum (Al) composites by hot-press and hot-extrusion methods [63]. CNTs-Fe-Al₂O₃ composites have been prepared by hot pressing [64, 65].

2.2.2. Fabrication of CNTs Reinforced Polymer Matrix Composites

The common fabricating methods of CNTs/polymer composites are solution mixing, melt blending, in situ polymerization, and sol-gel method [66]. Uniform dispersion of CNTs in polymer is a fundamental challenge and several factors that influence the dispersion of CNTs in a polymer matrix have to be considered in the preparation process of CNTs/polymer composites. In recent years, many polymers, such as epoxy [67–69], PMMA [70–73], PVA [74], PVC [75], PP [76], PE [77, 78], PA12 [79], and PS [80, 81], have been employed as matrices to prepare CNTs/polymer composites.

2.2.3. Fabrication of CNTs Reinforced Ceramic Matrix Composites

Ceramic materials possess high temperature resistance, corrosion resistance, and better biocompatibility compared with metal and polymer. The poor mechanical properties of ceramic with regard to its brittleness and low fracture toughness restrict its use in load bearing applications [82–85]. Therefore, CNTs with excellent physical and chemical properties are added to enhance the mechanical properties of the ceramic matrix. The fabricating methods of CNTs/ceramic composites include hot pressing process (HP), hot isostatic pressing-sintering (Sinter-HIP), spark plasma sintering (SPS), microwave sintering, and high-temperature extrusion molding according to the sintering process [86, 87]. SPS method is a newly developed technique used widely since 1990 [88]. During recent years, various ceramics, composites, cermets, and other materials, including Al, Ti, and functionally graded materials (FGM), have been successfully compacted by SPS [88–96]. Compared with other sintering methods, SPS method has several advantages. The SPS method can break surface oxide layer on particles and heat them up instantly by electric spark discharges under compressive pressure. In this way, it is possible to obtain fully dense samples at relatively low sintering temperature and pressure in a very short holding time [56, 95, 97]. Besides, by rapid temperature rise, grain growth of the raw material is kept to a minimum, thus making it possible to maintain the nanotube structure in the sintered bulk CNTs. Wang et al. successfully fabricated CNTs-based composites including MWCNTs/5, 20, 25% polycarbosilane (PCS), 100% MWCNTs, and MWCNTs/40% hydroxyapatite (HA) composites by using the SPS method under different sintering conditions. In addition, Yao et al. fabricated CNTs/alumina reinforced composite by a combined process of pressureless sintering and atmosphere hot-pressing sintering [96]. Ogihara et al. synthesized the CNTs/alumina composite using pressureless sintering under vacuum and hot isostatic pressing [97].

3. Mechanical Properties and Biocompatibility of CNTs-Based Reinforced Composites

3.1. Microstructure

CNTs have recently gained substantial interest for their potential applications in tissue engineering due to their large ratio of surface area to volume and unique microstructure. From the TEM micrographs, MWCNTs starting powders had external and internal diameters of 20–80 nm and 10–50 nm, and the 100% MWCNTs monolith basically maintained the nanosized tube microstructure and the bamboo microstructures following SPS treatment, as indicated by the hollow arrow in Figures 1(a) and 1(b) [98].

(a)

(b)

For the phenoxy/MWCNTs nanocomposites, optical microscopic images were shown as in Figure 2, from which we can see the state of CNTs dispersion in phenoxy matrix for different functionalized and nonfunctionalized MWCNTs, and compared with the other composites, the agglomerates are much bigger for CNTs-COOH (Figure 2(a)) [57]. TEM images of phenoxy/MWCNTs nanocomposites were shown as in Figure 3. The size of aggregates was in the scale of 200 nm, and the size of CNTs aggregates follows the following trend: CNT-COOH>pure-CNT>CNT-OH>CNT-NH [57].

(a)

(b)

(c)

(d)

(a)

(b)

(c)

(d)

In the sintering process of MWCNTs/5, 20, and 25% PCS, nanosized SiC particles pyrolyzed from PCS during sintering worked as the binder for MWCNTs, while HA was selected as binder to consolidate MWCNTs, which has been extensively used for maxillofacial surgery, orthopedics, and implant fabrication and is one of the most compatible biomaterials owing to its similar chemical composition and crystal structure to apatite in human hard tissue such as bone and tooth [84, 85, 99]. However, the poor mechanical properties of HA with regard to its brittleness and low fracture toughness restrict its use in load bearing applications (orthopedic/dental implant) [86, 87].

3.2. Mechanical Properties

It has been well proved that the mechanical property of matrix could be largely enhanced by the addition of CNTs [100, 101].

3.2.1. Mechanical Properties of CNTs Reinforced Metal Matrix Composites

For AZ31/CNTs composite, the maximal tensile strength and the elongation of the AZ31/CNTs composites are enhanced by 41.3% and 119.4%, respectively, and the elastic modulus and microhardness are also raised by 67.8% and 66.9%, respectively, when compared with those of the as-cast AZ31 Mg alloys [102]. Kim et al. were the first to report Cu-CNTs reinforced composites by SPS. Further rolling was performed on the composite to deform and align the CNT rich regions resulting in improved properties. SPS of Cu-CNTs nanocomposite powder, produced by molecular level mixing process, helps further improve density and mechanical properties. Enhancement in mechanical strength by 129% with addition of 5 vol% CNTs had been demonstrated [103].

3.2.2. Mechanical Properties of CNTs Reinforced Polymer Matrix Composites

In previous study, carboxyl-functionalized MWCNTs were used as fillers in a polyamide 6 (PA6) matrix in order to change the effect of the material [104, 105]. Sun et al. reported that the addition of CNTs improved the storage modulus E′ and loss modulus E′′ of the PA6/CNTs composite [104]. Zomer Volpato et al. synthesized MWCNTs/PA6 composite, and incorporation of up to 2 wt% CNTs in CNTs/PA6 laminates improved the flexural stress of the laminates up to 36%, which should form hydrogen bonds between the polymer and filler or form amide bond between the free amines on the polymer and the CNTs carboxyl groups [105].

To improve the physiochemical properties of polyurethane (PU), CNTs are incorporated to add functionalities of material. For instance, Amr et al. reported that Young’s modulus of CNTs/polystyrene (PS) nanocomposites was increased by 22% [106]; Jung et al. reported that the transparent PU film was incorporated with functionalized MWCNTs and found 2-fold and 10-fold increases in tensile strength and modulus, respectively, for MWCNTs/PU composite film [107]. According to the result of Tijing, the incorporation of MWCNTs increased the tensile strength and modulus of the composite nanofibers by 69% and 140%, respectively, and 62% and 78%, respectively, for composite films, and the MWCNTs/PU composites showed an improved thermal degradation behavior [108].

3.2.3. Mechanical Properties of CNTs Reinforced Ceramic Matrix Composites

Yao et al. reported that the mechanical properties of the CNTs/alumina reinforced composite can be obviously improved due to the addition of the CNTs. As the increase of mass fraction of carbon nanotubes, the tensile strength and Brinell hardness of the composite are elevated and achieve the maximum of 245 MPa and 106.66 n/mm², respectively, when the mass fraction of CNTs increases to 2.0 wt% [96]. Ogihara et al. synthesized the CNTs/alumina composite by direct growth of CNTs on alumina by chemical vapor deposition (CVD) and the as-grown nanocomposites were densified by SPS, and the mechanical strength was enhanced as follows: Young’s modulus, 383 GPa; Vickers hardness, 19.9 GPa; Bending strength, 578 MPa [97].

For Zirconia-MWCNTs composites, the addition of MWCNTs aims to avoid the slow crack propagation and to enhance the toughness of the ceramic material used for prostheses. The sample of Zirconia MWCNTs shows higher density, lower grain size, improved toughness, and enhanced hardness, which suggested the good behavior of MWCNTs as strengthening agents for zirconia [109].

For MWCNTs/PCS composites, it is found that PCS content and sintering pressure improved the bulk density and Vickers hardness of sintered MWCNTs, and the value of mechanical properties was highest for the MWCNTs/20% PCS. The bulk density, Young’s modulus, and compressive strength of the MWCNTs/20% PCS material had the highest value of 2.13 g/cm³, 27 GPa, and 298 MPa, which was higher than that of human bone. However, the bulk density, Young’s modulus, and compressive strength of 100% MWCNTs monolith were 1.95 g/cm³, 20 GPa, and 249 MPa, which were very closer to those of bone (1.9 g/cm³, 19 GPa, and 150 MPa) and lower than those of other traditional implant materials: Ti (4.51 g/cm³, 120 GPa, and 500 MPa) and HA (3.15 g/cm³, 35 GPa, and 600 MPa) [98, 110–113]. The results showed that the 100% MWCNTs monolith could match the mechanical properties of human compact bone, which might be more suitable for implant materials than HA and Ti.

3.3. Biocompatibility

At present, carbon nanotubes have been extensively studied for use in biomedical applications, and biomaterials using CNTs are expected to be developed for clinical use [114–119]. Some studies showed that nanophase biomaterials had higher biocompatibility than similar micron-sized materials [5, 120]. Many studies in vivo and in vitro have investigated the biocompatibility of CNTs for biomedical applications. There are controversies on CNTs cytotoxicity, and CNTs might have adverse effects, which is ascribed to their physicochemical properties, such as structure, surface area, extent of oxidation, producing method, and concentration [121]. The toxicity of CNTs on the respiratory system is investigated. Lam et al. studied toxicity of CNTs by bronchial injection test, and the results of studies showed that 0.5 mg of CNTs can cause the death of part of mice, another part of the lungs in mice is characterized by damage granuloma [122]. In contrast, Miyawaki et al. investigated in vitro and in vivo the toxicities of carbon nanohorns (CNHs). The CNHs were found to be a nonirritant and a nondermal sensitizer through skin primary and conjunctival irritation tests and skin sensitization test. The acute peroral toxicity of CNHs was found to be quite low; the lethal dosage for rats was more than 2000 mg/kg of body weight. Intratracheal instillation tests revealed that CNHs rarely damaged rat lung tissue for a 90-day test period, although black pigmentation due to accumulated nanohorns was observed. Yet the present results suggest that CNHs have low acute toxicities [123].

Used in the scaffold, CNTs could promote cell adhesion, and MWNTs could decrease osteoclast number to inhibit bone resorption [124, 125]. When it comes to osteoblasts, CNTs did not have cytotoxicity to osteoblasts and did not have harmful effects on osteoblast differentiation or mineralization [126–128]. In addition, nonfunctionalized SWCNTs had little toxicity to cell such as decreasing the viability and number of cells [129]. It is reported that there was no acute toxicity or adverse reaction for functionalized CNTs; however, the severe tissue deposition and inflammatory response were observed for pristine CNTs. Tang et al. modified the CNTs with macromolecules (polyethylene glycol PEG), and the results indicated that the synthesized CNTs are very biocompatible, exhibiting no differences from normal control groups, and in other words, shorter pristine and polymer functionalized MWCNTs have a significant potential for biomedical applications as efficient carriers for diagnostic, therapeutic, or cell-specific targeting molecules [130]. Ahn et al. investigated the incorporation of MWCNTs into calcium phosphate cements (CPC) and evaluated the bioactive nature of CPC-MWCNTs hybrid the osteogenic differentiation capacity as bone grafting materials, using proliferation and differentiation of MC3T3-E1 cells, the result of which showed that CPC-MWCNTs hybrid which promoted the osteogenic differentiation of osteoblasts could serve well as bone repairing graft material [131]. Zomer Volpato et al. synthesized PA6/MWCNT and investigated the effect of the addition of CNTs on the cell-material interactions and found that the proliferation and activation of MG63 cell line osteoblasts were enhanced due to surface modification caused by the filler addition compared to the purely PA6 networks [105]. The result of Ogihara et al. about cell attachment of CNTs/alumina composite indicated that CNTs/alumina composite had more favorable cell attachment properties, and CNTs at the surface of the implant did not inhibit attachment [97].

Meanwhile the subcutaneous tissue reactions and bone tissue reactions were evaluated for the alumina ceramic and CNTs/alumina composite, and found that inflammatory cells were observed around the composites after 1 week, however, severe inflammatory reactions were not observed (Figures 4(a) and 4(b)) [97]. And after 4 weeks, thin fibrous capsules attached to alumina ceramic had been formed, and the inflammatory reaction had disappeared. Similar phenomenon was observed on the CNTs/alumina composite (Figures 4(c) and 4(d)) [97].

(a)

(b)

(c)

(d)

Yokoyama et al. investigated the biological behavior of hat-stacked carbon nanofibers (H-CNFs) in the subcutaneous tissue of rats, and the results showed that H-CNFs were englobed by fibrous connective tissue with little inflammation [27]. But Muller et al. found that CNTs have the potential to cause serious inflammatory and fibrotic reactions by studying rats exposed to respirable CNTs particles [132]. Colvin reported that the pulmonary toxicity of CNTs was not obvious as granulomas which were not commonly observed in rat lungs instilled with CNTs [133]. Additionally, the study of Kumar et al. has revealed that the chemical state of the surface of CNTs may strongly influence tissue response [134]. The influence of catalytic particles, like Fe and Ni, applied during the synthesis of CNTs on the toxicity of CNTs has been reported [30].

The inflammation of MWCNTs powders is most serious in the soft tissue, which may be due to that the dispersed powder easily caused body response. At 1 week after the implantation in the soft tissue of rats, MWCNTs powders were surrounded by granulation tissue with many macrophages and foreign body giant cells (Figure 5(a)) [110], which was consistent with the study of Warheit et al., who have demonstrated that pulmonary exposures to CNTs in rats produced multifocal granulomas that consisted of macrophage-like multinucleate, [135]. However, no severe inflammatory response was observed around MWCNTs/PCS composites with different percentage of PCS and 100% MWCNTs monolith. For the response in subcutaneous tissue, there was a difference dependent on the content of PCS in the early implant stage; the degree of inflammation was influenced by SiC pyrolyzed from PCS. At 1 week after surgery, inflammatory response around MWCNTs/5% PCS (Figure 5(c)) was milder than that around MWCNTs/25% PCS (Figure 5(e)) [110]. MWCNTs/20% PCS was covered by relatively thick fibrous connective tissue including many cells with large cytoplasm like fibroblasts, fibroblasts with spindle-shaped cytoplasm, and some inflammatory round cells (Figure 5(d)) [111], and an inflammatory reaction around the 100% MWCNTs monolith was observed at 1 week after implantation in subcutaneous tissue (Figure 5(b)) [98]. But at 4 weeks after implantation, the MWCNTs/20% PCS and 100% MWCNTs monolith were covered by loose fibrous connective tissue, and inflammation around materials was slight in comparison to that at 1 week (Figures 6(a) and 6(b)) [98, 111]. The inflammatory reaction after one-week implantation is normal for the short period that immediately follows an implantation treatment.

(a)

(b)

(c)

(d)

(e)

(a)

(b)

The images of bone tissue reactions after alumina ceramic or CNTs/alumina composite implanted in rabbit femurs were shown as Figure 7 [97]. At 12 weeks, new bone was found around the composites and the fibrous capsule between the composites and the bone was rarely observed (Figures 7(a), 7(b), 7(e), and 7(f)). At 24 weeks, the entire circumference of the specimen had attached to the bone tissue without gaps, and composites were completely incorporated into the bone and the bone defect was repaired (Figures 7(c), 7(d), 7(g), and 7(h)). These results showed that the bone tissue compatibility of CNT/alumina composite is comparable with that of alumina ceramic.

(a)

(b)

(c)

(d)

(e)

(f)

(g)

(h)

For the response in bone tissue, after implantation for 4 weeks in the femur, part of the newly formed bone attached to MWCNTs/20% PCS directly (Figure 8(a)), lamellar newly formed bone was observed around the 100% MWCNTs implant (Figure 8(b)), and a large of newly formed bone was observed around the MWCNTs/40% HA composites as shown in Figure 8(c), and the newly formed bone was attached to the implant directly [98, 111, 112]. The MWCNTs/PCS composite had very little prophlogistic effect and possessed osteoconductivity. Similar in vitro results were described by Elias et al. who reported that carbon fiber compacts improved the growth of osteoblasts compared to conventional carbon fiber [120]. However, the osteoconductivity was influenced by the PCS content, and the amount of the newly formed bone was least in MWCNTs/20% PCS and most in MWCNTs/40% HA. HA was added for improving the biocompatibility of MWCNTs materials. HA is widely accepted coating for orthopedic implants since 1980 due to its excellent biocompatibility and bioactivity properties [133, 136]. And many composites containing HA were fabricated and show good biocompatibility [137, 138]. MWCNTs/HA composites possessed better osseointegration than pure MWCNTs as we expected.

(a)

(b)

(c)

4. Conclusions and Perspectives

Nanoscale substances like CNTs could be potential applied in almost all the walks of life: media, entertainment, communication, transport, health, and environment, especially in the nanobiomedical field [53]. CNTs, with a range of unique properties, appear suited as biomaterials and may become useful scaffold materials for tissue engineering. Reinforcing scaffolds with CNTs has been suggested to be an effective means of developing engineering materials for tissue regeneration. These reinforced scaffolds have been largely applied for not only hard tissue but also soft tissue repair. However, their safety and effectiveness as biomaterials are still unclear. More and more interests were emerged in CNT-based composites, including the synthesis of the composites and their mechanical properties, cell experiments in vitro, and biocompatibility in vivo. From previous studies, we could find that there were many methods for composing the variable CNTs-based composites under different synthetic conditions. Those composites with adjustable mechanical properties could be used for different usages, such as tissue engineering, delivery of genes and drugs, scaffold, implant, or as filler in other composites to improve their mechanical properties. Besides, we found that the mechanical property of 100% MWCNTs monolith was most close to that of human bone. Moreover, in the animal experiments, no severe inflammatory response such as necrosis and no toxicity for soft tissue and bone regeneration were observed around most CNTs-based composites. The weak inflammatory reaction in short term after implantation was normal for the short period that immediately followed an implantation treatment, and the inflammation could be reduced with the extension of experiment time. The MWCNTs/40% HA composites possessed better osseointegration than other composites.

Although modified CNTs might not represent certain original structure and properties of CNTs, it is still possible for the modified CNTs-based composites to further improve their biocompatibility and effectively reinforce their mechanical properties. Above all, although there is still a lot of works to do, the CNTs-based reinforced composites will be not only applicable as artificial bone implant materials, but also for other biomedical applications potentially rewards opportunities to develop the next generation of engineered biomaterials in the future, such as tissue engineering, cell therapy, drug delivery, and diagnostic device.

Conflict of Interests

The authors declare that there is no conflict of interests regarding the publication of this paper.

Acknowledgments

The authors acknowledge the financial support from the Liaoning Provincial Department of Education Sciences Research Grant for Research on Advanced Medical Technology (L2011131). The authors acknowledge the graduate students in the Department of Prosthodontics, School of Stomatology, China Medical University for their kind help.

References

J. Mortier and M. Engelhardt, “Foreign body reaction to a carbon fiber implant in the knee: case report and literature survey,” Zeitschrift für Orthopädie und ihre Grenzgebiete, vol. 138, no. 5, pp. 390–394, 2000.
View at: Publisher Site | Google Scholar
S. Iijima, “Helical microtubules of graphitic carbon,” Nature, vol. 354, no. 6348, pp. 56–58, 1991.
View at: Google Scholar
X. Li, X. Liu, J. Huang, Y. Fan, and F.-Z. Cui, “Biomedical investigation of CNT based coatings,” Surface and Coatings Technology, vol. 206, no. 4, pp. 759–766, 2011.
View at: Publisher Site | Google Scholar
I. Firkowska, M. Olek, N. Pazos-Peréz, J. Rojas-Chapana, and M. Giersig, “Highly ordered MWNT-based matrixes: topography at the nanoscale conceived for tissue engineering,” Langmuir, vol. 22, no. 12, pp. 5427–5434, 2006.
View at: Publisher Site | Google Scholar
X. M. Li, Q. Feng, X. Liu, W. Dong, and F. Cui, “The use of nanoscaled fibers or tubes to improve biocompatibility and bioactivity of biomedical materials,” Journal of Nanomaterials, vol. 3, pp. 1–16, 2013.
View at: Google Scholar
N. W. S. Kam, T. C. Jessop, P. A. Wender, and H. Dai, “Nanotube molecular transporters: internalization of carbon nanotube-protein conjugates into mammalian cells,” Journal of the American Chemical Society, vol. 126, no. 22, pp. 6850–6851, 2004.
View at: Publisher Site | Google Scholar
N. W. S. Kam, Z. Liu, and H. Dai, “Functionalization of carbon nanotubes via cleavable disulfide bonds for efficient intracellular delivery of siRNA and potent gene silencing,” Journal of the American Chemical Society, vol. 127, no. 36, pp. 12492–12493, 2005.
View at: Publisher Site | Google Scholar
T. W. Ebbesen, “Carbon nanotubes: prepartion and properties,” in From Carbon Fibers to Nanotubes, M. Endo, R. Saito, M. S. Dresselhaus, and G. Dresselhaus, Eds., pp. 42–49, 1997.
View at: Google Scholar
P. M. Ajayan, “Nanotubes from Carbon,” Chemical Reviews, vol. 99, no. 7, pp. 1787–1799, 1999.
View at: Google Scholar
K. P. De Jong and J. W. Geus, “Carbon nanofibers: catalytic synthesis and applications,” Catalysis Reviews, vol. 42, no. 4, pp. 481–510, 2000.
View at: Google Scholar
M. Ono-Ogasawara and T. Myojo, “Characteristics of multi-walled carbon nanotubes and background aerosols by carbon analysis, particle size and oxidation temperature,” Advanced Powder Technology, vol. 24, no. 1, pp. 263–269, 2012.
View at: Google Scholar
T. C. Lu and J. L. Tsai, “Characterizing load transfer efficiency in double-walled carbon nanotubes using multiscale finite element modeling,” Composites B, vol. 44, no. 1, pp. 394–402, 2013.
View at: Google Scholar
M. M. J. Treacy, T. W. Ebbesen, and J. M. Gibson, “Exceptionally high Young's modulus observed for individual carbon nanotubes,” Nature, vol. 381, no. 6584, pp. 678–680, 1996.
View at: Google Scholar
E. W. Wong, P. E. Sheehan, and C. M. Lieber, “Nanobeamme mechanics: elasticity, strength, and toughness of nanorods and nanotubes,” Science, vol. 277, no. 5334, pp. 1971–1975, 1997.
View at: Google Scholar
S. Iijima, C. Brabec, A. Maiti, and J. Bernholc, “Structural flexibility of carbon nanotubes,” Journal of Chemical Physics, vol. 104, no. 5, pp. 2089–2092, 1996.
View at: Google Scholar
N. Yu, Z. H. Zhang, and S. Y. He, “Fracture toughness and fatigue life of MWCNT/Epoxycomposites,” Science and Engineering A, vol. 494, no. 1, pp. 380–384, 2008.
View at: Google Scholar
S. G. Prolongo, M. Burón, M. R. Gude, R. Chaos-Morán, M. Campo, and A. Ureña, “Effects of dispersion techniques of carbon nanofibers on the thermo-physical properties of epoxy nanocomposites,” Composites Science and Technology, vol. 68, no. 13, pp. 2722–2730, 2008.
View at: Publisher Site | Google Scholar
P. M. Ajayan, “Organics, polymers and biological materials,” in Handbook of Nanostructured Materials and Nanotechnology, H. S. Nalwa, Ed., p. 375, Academic Press, San Diego, Calif, USA, 2000.
View at: Google Scholar
M. Uo, K. Tamura, Y. Sato et al., “The cytotoxicity of metal-encapsulating carbon nanocapsules,” Small, vol. 1, no. 8-9, pp. 816–819, 2005.
View at: Publisher Site | Google Scholar
T. Akasaka and F. Watari, “Nano-architecture on carbon nanotube surface by biomimetic coating,” Chemistry Letters, vol. 34, no. 6, pp. 826–827, 2005.
View at: Publisher Site | Google Scholar
R. A. MacDonald, B. F. Laurenzi, G. Viswanathan, P. M. Ajayan, and J. P. Stegemann, “Collagen-carbon nanotube composite materials as scaffolds in tissue engineering,” Journal of Biomedical Materials Research A, vol. 74, no. 3, pp. 489–496, 2005.
View at: Publisher Site | Google Scholar
K. Kiura, Y. Sato, M. Yasuda et al., “Activation of human monocytes and mouse splenocytes by single-walled carbon nanotubes,” Journal of Biomedical Nanotechnology, vol. 1, no. 3, pp. 359–364, 2005.
View at: Google Scholar
X. Li, H. Gao, M. Uo et al., “Maturation of osteoblast-like SaoS2 induced by carbon nanotubes,” Biomedical Materials, vol. 4, no. 1, Article ID 015005, 2009.
View at: Publisher Site | Google Scholar
X. M. Li, X. H. Liu, G. P. Zhang et al., “Repairing 25 mm bone defect using fibres reinforced scaffolds as well as autograft bone,” Bone, vol. 43, article S94, 2008.
View at: Google Scholar
T. Akasaka, F. Watari, Y. Sato, and K. Tohji, “Apatite formation on carbon nanotubes,” Materials Science and Engineering C, vol. 26, no. 4, pp. 675–678, 2006.
View at: Publisher Site | Google Scholar
Y. Sato, A. Yokoyama, K.-I. Shibata et al., “Influence of length on cytotoxicity of multi-walled carbon nanotubes against human acute monocytic leukemia cell line THP-1 in vitro and subcutaneous tissue of rats in vivo,” Molecular BioSystems, vol. 1, no. 2, pp. 176–182, 2005.
View at: Publisher Site | Google Scholar
A. Yokoyama, Y. Sato, Y. Nodasaka et al., “Biological behavior of hat-stacked carbon nanofibers in the subcutaneous tissue in rats,” Nano Letters, vol. 5, no. 1, pp. 157–161, 2005.
View at: Publisher Site | Google Scholar
A. Bianco, K. Kostarelos, and M. Prato, “Applications of carbon nanotubes in drug delivery,” Current Opinion in Chemical Biology, vol. 9, no. 6, pp. 674–679, 2005.
View at: Publisher Site | Google Scholar
D. Cui, C. S. Ozkan, S. Ravindran, Y. Kong, and H. Gao, “Encapsulation of pt-labelled DNA molecules inside carbon nanotubes,” Mechanics & Chemistry of Biosystems, vol. 1, no. 2, pp. 113–121, 2004.
View at: Google Scholar
B. S. Harrison and A. Atala, “Carbon nanotube applications for tissue engineering,” Biomaterials, vol. 28, no. 2, pp. 344–353, 2007.
View at: Publisher Site | Google Scholar
A. S. Ferlauto, D. Z. De Florio, F. C. Fonseca et al., “Chemical vapor deposition of multi-walled carbon nanotubes from nickel/yttria-stabilized zirconia catalysts,” Applied Physics A, vol. 84, no. 3, pp. 271–276, 2006.
View at: Publisher Site | Google Scholar
M. Jagtoyen, J. Pardue, T. Rantell, and F. Derbyshire, “Porosity of carbon nanotubes,” Porosity of Carbon Nanotubes, vol. 17, pp. 289–293, 2000.
View at: Google Scholar
Y. Gao and I. Kyratzis, “Covalent immobilization of proteins on carbon nanotubes using the cross-linker 1-ethyl-3-(3-dimethylaminopropyl)carbodiimide: a critical assessment,” Bioconjugate Chemistry, vol. 19, no. 10, pp. 1945–1950, 2008.
View at: Publisher Site | Google Scholar
P. Asuri, S. S. Karajanagi, E. Sellitto, D.-Y. Kim, R. S. Kane, and J. S. Dordick, “Water-soluble carbon nanotube-enzyme conjugates as functional biocatalytic formulations,” Biotechnology and Bioengineering, vol. 95, no. 5, pp. 804–811, 2006.
View at: Publisher Site | Google Scholar
N. R. Palwai, D. E. Martyn, L. F. F. Neves, Y. Tan, D. E. Resasco, and R. G. Harrison, “Retention of biological activity and near-infrared absorbance upon adsorption of horseradish peroxidase on single-walled carbon nanotubes,” Nanotechnology, vol. 18, no. 23, Article ID 235601, 2007.
View at: Publisher Site | Google Scholar
S. Shah, K. Solanki, and M. N. Gupta, “Enhancement of lipase activity in non-aqueous media upon immobilization on multi-walled carbon nanotubes,” Chemistry Central Journal, vol. 1, no. 1, article 30, pp. 1–6, 2007.
View at: Publisher Site | Google Scholar
K. Jiang, L. S. Schadler, R. W. Siegel, X. Zhang, H. Zhang, and M. Terrones, “Protein immobilization on carbon nanotubes via a two-step process of diimide-activated amidation,” Journal of Materials Chemistry, vol. 14, no. 30, pp. 37–39, 2004.
View at: Publisher Site | Google Scholar
W. Huang, S. Taylor, K. Fu et al., “Attaching proteins to carbon nanotubes via Diimide-Activated amidation,” Nano Letters, vol. 2, no. 4, pp. 311–314, 2002.
View at: Publisher Site | Google Scholar
N. Z. Prlainovic, D. I. Bezbradica, Z. D. Knezevic-Jugovic et al., “Adsorption of lipase from Candida rugosa on multi walled carbon nanotubes,” Journal of Industrial and Engineering Chemistry, vol. 19, pp. 279–285, 2013.
View at: Google Scholar
G. V. Salmoria, R. A. Paggi, A. Lago, and V. E. Beal, “Microstructural and mechanical characterization of PA12/MWCNTs nanocomposite manufactured by selective laser sintering,” Polymer Testing, vol. 30, no. 6, pp. 611–615, 2011.
View at: Publisher Site | Google Scholar
X. Li, X. Liu, W. Dong et al., “In vitro evaluation of porous poly(L-lactic acid) scaffold reinforced by chitin fibers,” Journal of Biomedical Materials Research B, vol. 90, no. 2, pp. 503–509, 2009.
View at: Publisher Site | Google Scholar
W. X. Chen, J. P. Tu, L. Y. Wang, H. Y. Gan, Z. D. Xu, and X. B. Zhang, “Tribological application of carbon nanotubes in a metal-based composite coating and composites,” Carbon, vol. 41, no. 2, pp. 215–222, 2003.
View at: Publisher Site | Google Scholar
J. P. Tu, Y. Z. Yang, L. Y. Wang, X. C. Ma, and X. B. Zhang, “Tribological properties of carbon-nanotube-reinforced copper composites,” Tribology Letters, vol. 10, no. 4, pp. 225–228, 2001.
View at: Publisher Site | Google Scholar
S. R. Dong, J. P. Tu, and X. B. Zhang, “An investigation of the sliding wear behavior of Cu-matrix composite reinforced by carbon nanotubes,” Materials Science and Engineering A, vol. 313, no. 1-2, pp. 83–87, 2001.
View at: Publisher Site | Google Scholar
L. Zhao and L. Gao, “Novel in situ synthesis of MWNTs-hydroxyapatite composites,” Carbon, vol. 42, no. 2, pp. 423–426, 2004.
View at: Publisher Site | Google Scholar
Z. Xia, L. Riester, W. A. Curtin et al., “Direct observation of toughening mechanisms in carbon nanotube ceramic matrix composites,” Acta Materialia, vol. 52, no. 4, pp. 931–944, 2004.
View at: Publisher Site | Google Scholar
A. B. Dalton, S. Collins, E. Muñoz et al., “Super-tough carbon-nanotube fibres,” Nature, vol. 423, no. 6941 article 703, 2003.
View at: Publisher Site | Google Scholar
S. Kumar, H. Doshi, M. Srinivasarao, J. O. Park, and D. A. Schiraldi, “Fibers from polypropylene/nano carbon fiber composites,” Polymer, vol. 43, no. 5, pp. 1701–1703, 2002.
View at: Google Scholar
X. M. Li, L. Wang, Y. B. Fan, Q. L. Feng, and F. Z. Cui, “Biocompatibility and toxicity of nanoparticles and nanotubes,” Journal of Nanomaterials, vol. 2012, Article ID 548389, 19 pages, 2012.
View at: Publisher Site | Google Scholar
L. Valentini, J. Biagiotti, J. M. Kenny, and S. Santucci, “Morphological characterization of single-walled carbon nanotubes-PP composites,” Composites Science and Technology, vol. 63, no. 8, pp. 1149–1153, 2003.
View at: Publisher Site | Google Scholar
T. J. Webster, M. C. Waid, J. L. McKenzie, R. L. Price, and J. U. Ejiofor, “Nano-biotechnology: carbon nanofibres as improved neural and orthopaedic implants,” Nanotechnology, vol. 15, no. 1, pp. 48–54, 2004.
View at: Publisher Site | Google Scholar
R. L. Price, K. M. Haberstroh, and T. J. Webster, “Improved osteoblast viability in the presence of smaller nanometre dimensioned carbon fibres,” Nanotechnology, vol. 15, no. 8, pp. 892–900, 2004.
View at: Publisher Site | Google Scholar
P. Deng, Z. Xu, and J. Li, “Simultaneous determination of ascorbic acid and rutin in pharmaceutical preparations with electrochemical method based on multi-walled carbon nanotubes-chitosan composite film modified electrode,” Journal of Pharmaceutical and Biomedical Analysis, vol. 76, pp. 234–242, 2013.
View at: Google Scholar
H. Golnabi, “Carbon nanotube research developments in terms of published papers and patents, synthesis and production,” Scientia Iranica, vol. 19, pp. 2012–2022, 2012.
View at: Google Scholar
Y. Zhu, W. Wang, X. Jia, T. Akasaka, S. Liao, and F. Watari, “Deposition of TiC film on titanium for abrasion resistant implant material by ion-enhanced triode plasma CVD,” Applied Surface Science, vol. 262, pp. 156–158, 2012.
View at: Publisher Site | Google Scholar
M. Kumar and Y. Ando, “Chemical vapor deposition of carbon nanotubes: a review on growth mechanism and mass production,” Journal of Nanoscience and Nanotechnology, vol. 10, no. 6, pp. 3739–3758, 2010.
View at: Publisher Site | Google Scholar
M. N. Disfani and S. H. Jafari, “Assessment of intertube interactions in different functionalized multiwalled carbon nanotubes incorporated in a phenoxy resin,” Polymer Engineering and Science, vol. 53, no. 1, pp. 168–175, 2013.
View at: Google Scholar
H. Kwon, M. Estili, K. Takagi, T. Miyazaki, and A. Kawasaki, “Combination of hot extrusion and spark plasma sintering for producing carbon nanotube reinforced aluminum matrix composites,” Carbon, vol. 47, no. 3, pp. 570–577, 2009.
View at: Publisher Site | Google Scholar
X. Zeng, G. Zhou, Q. Xu, Y. Xiong, C. Luo, and J. Wu, “A new technique for dispersion of carbon nanotube in a metal melt,” Materials Science and Engineering A, vol. 527, no. 20, pp. 5335–5340, 2010.
View at: Publisher Site | Google Scholar
S. R. Bakshi, V. Singh, S. Seal, and A. Agarwal, “Aluminum composite reinforced with multiwalled carbon nanotubes from plasma spraying of spray dried powders,” Surface and Coatings Technology, vol. 203, no. 10-11, pp. 1544–1554, 2009.
View at: Publisher Site | Google Scholar
G. Han, J. Yuan, G. Shi, and F. Wei, “Electrodeposition of polypyrrole/multiwalled carbon nanotube composite films,” Thin Solid Films, vol. 474, no. 1-2, pp. 64–69, 2005.
View at: Publisher Site | Google Scholar
S. R. Bakshi and A. Agarwal, “An analysis of the factors affecting strengthening in carbon nanotube reinforced aluminum composites,” Carbon, vol. 49, no. 2, pp. 533–544, 2011.
View at: Publisher Site | Google Scholar
T. Kuzumaki, K. Miyazawa, H. Ichinose, and K. Ito, “Processing of carbon nanotube reinforced aluminum composite,” Journal of Materials Research, vol. 13, no. 9, pp. 2445–2449, 1998.
View at: Google Scholar
A. Peigney, C. Laurent, O. Dumortier, and A. Rousset, “Carbon nanotubes-Fe-alumina nanocomposites. Part I: influence of the Fe content on the synthesis of powders,” Journal of the European Ceramic Society, vol. 18, no. 14, pp. 1995–1104, 1998.
View at: Google Scholar
C. Laurent, A. Peigney, O. Dumortier, and A. Rousset, “Carbon nanotubes-Fe-Alumina nanocomposites. Part II: microstructure and mechanical properties of the hot-Pressed composites,” Journal of the European Ceramic Society, vol. 18, no. 14, pp. 2005–2013, 1998.
View at: Google Scholar
S. B. Jagtap and D. Ratna, “Preparation and characterization of rubbery epoxy/multiwall carbon nanotubes composites using amino acid salt assisted dispersion technique,” Express Polymer Letter, vol. 7, no. 4, pp. 329–339, 2013.
View at: Google Scholar
J. Sandler, M. S. P. Shaffer, T. Prasse, W. Bauhofer, K. Schulte, and A. H. Windle, “Development of a dispersion process for carbon nanotubes in an epoxy matrix and the resulting electrical properties,” Polymer, vol. 40, no. 21, pp. 5967–5971, 1999.
View at: Google Scholar
L. S. Schadler, S. C. Giannaris, and P. M. Ajayan, “Load transfer in carbon nanotube epoxy composites,” Applied Physics Letters, vol. 73, no. 26, pp. 3842–3844, 1998.
View at: Publisher Site | Google Scholar
F. H. Gojny, J. Nastalczyk, Z. Roslaniec, and K. Schulte, “Surface modified multi-walled carbon nanotubes in CNT/epoxy-composites,” Chemical Physics Letters, vol. 370, no. 5-6, pp. 820–824, 2003.
View at: Publisher Site | Google Scholar
Z. Jia, Z. Wang, C. Xu et al., “Study on poly(methyl methacrylate)/carbon nanotube composites,” Materials Science and Engineering A, vol. 271, no. 1-2, pp. 395–400, 1999.
View at: Google Scholar
M. Lamy De La Chapelle, C. Stéphan, T. P. Nguyen et al., “Raman characterization of singlewalled carbon nanotubes and PMMA-nanotubes composites,” Synthetic Metals, vol. 103, no. 1–3, pp. 2510–2512, 1999.
View at: Publisher Site | Google Scholar
X. M. Li, Y. Huang, L. S. Zheng et al., “Effect of substrate stiffness on the functions of rat bone marrow and adipose tissue derived mesenchymal stem cells in vitro,” Journal of Biomedical Materials Research A, 2013.
View at: Publisher Site | Google Scholar
R. Haggenmueller, H. H. Gommans, A. G. Rinzler, J. E. Fischer, and K. I. Winey, “Aligned single-wall carbon nanotubes in composites by melt processing methods,” Chemical Physics Letters, vol. 330, no. 3-4, pp. 219–225, 2000.
View at: Google Scholar
M. S. P. Shaffer and A. H. Windle, “Fabrication and characterization of carbon nanotube/poly (vinyl alcohol) composites,” Advanced Materials, vol. 11, no. 11, pp. 937–941, 1999.
View at: Google Scholar
F. Li, H. M. Cheng, S. Bai, G. Su, and M. S. Dresselhaus, “Tensile strength of single-walled carbon nanotubes directly measured from their macroscopic ropes,” Applied Physics Letters, vol. 77, no. 20, pp. 3161–3163, 2000.
View at: Google Scholar
G. G. Tibbetts and J. J. McHugh, “Mechanical properties of vapor-grown carbon fiber composites with thermoplastic matrices,” Journal of Materials Research, vol. 14, no. 7, pp. 2871–2880, 1999.
View at: Google Scholar
X. Tong, C. Liu, H.-M. Cheng, H. Zhao, F. Yang, and X. Zhang, “Surface modification of single-walled carbon nanotubes with polyethylene via in situ Ziegler-Natta polymerization,” Journal of Applied Polymer Science, vol. 92, no. 6, pp. 3697–3700, 2004.
View at: Publisher Site | Google Scholar
K. Lozano, S. Yang, and R. E. Jones, “Nanofiber toughened polyethylene composites,” Carbon, vol. 42, no. 11, pp. 2329–2331, 2004.
View at: Publisher Site | Google Scholar
J. K. W. Sandler, S. Pegel, M. Cadek et al., “A comparative study of melt spun polyamide-12 fibres reinforced with carbon nanotubes and nanofibres,” Polymer, vol. 45, no. 6, pp. 2001–2015, 2004.
View at: Publisher Site | Google Scholar
D. E. Hill, Y. Lin, A. M. Rao, L. F. Allard, and Y.-P. Sun, “Functionalization of carbon nanotubes with polystyrene,” Macromolecules, vol. 35, no. 25, pp. 9466–9471, 2002.
View at: Publisher Site | Google Scholar
K. Liao and S. Li, “Interfacial characteristics of a carbon nanotube-polystyrene composite system,” Applied Physics Letters, vol. 79, no. 25, pp. 4225–4227, 2001.
View at: Publisher Site | Google Scholar
X. M. Li, L. Wang, Y. B. Fan, Q. L. Feng, F. Z. Cui, and F. Watari, “Nanostructured scaffolds for bone tissue engineering,” Journal of Biomedical Materials Research A, vol. 101, no. 8, pp. 2424–2435, 2013.
View at: Google Scholar
A. A. White, S. M. Best, and I. A. Kinloch, “Hydroxyapatite-carbon nanotube composites for biomedical applications: a review,” International Journal of Applied Ceramic Technology, vol. 4, no. 1, pp. 1–13, 2007.
View at: Publisher Site | Google Scholar
X. Li, H. Liu, X. Niu et al., “Osteogenic differentiation of human adipose-derived stem cells induced by osteoinductive calcium phosphate ceramics,” Journal of Biomedical Materials Research A, vol. 97, no. 1, pp. 10–19, 2011.
View at: Publisher Site | Google Scholar
Q. Wang, S. Ge, and D. Zhang, “Nano-mechanical properties and biotribological behaviors of nanosized HA/partially-stabilized zirconia composites,” Wear, vol. 259, no. 7-12, pp. 952–957, 2005.
View at: Publisher Site | Google Scholar
J.-W. Choi, Y.-M. Kong, H.-E. Kim, and I.-S. Lee, “Reinforcement of hydroxyapatite bioceramic by addition of Ni3Al and Al₂O₃,” Journal of the American Ceramic Society, vol. 81, no. 7, pp. 1743–1748, 1998.
View at: Google Scholar
C. Chang, J. Shi, J. Huang, Z. Hu, and C. Ding, “Effects of power level on characteristics of vacuum plasma sprayed hydroxyapatite coating,” Journal of Thermal Spray Technology, vol. 7, no. 4, pp. 484–488, 1998.
View at: Google Scholar
H. Feng, Q. Meng, Y. Zhou, and D. Jia, “Spark plasma sintering of functionally graded material in the Ti-TiB2-B system,” Materials Science and Engineering A, vol. 397, no. 1-2, pp. 92–97, 2005.
View at: Publisher Site | Google Scholar
T. Takeuchi, M. Tabuchi, H. Kageyama, and Y. Suyama, “Preparation of dense BaTiO₃ ceramics with submicrometer grains by spark plasma sintering,” Journal of the American Ceramic Society, vol. 82, no. 4, pp. 939–943, 1999.
View at: Google Scholar
Y. Zhou, K. Hirao, M. Toriyama, and H. Tanaka, “Very rapid densification of nanometer silicon carbide powder by pulse electric current sintering,” Journal of the American Ceramic Society, vol. 83, no. 3, pp. 654–656, 2000.
View at: Google Scholar
M. Nygren and Z. Shen, “On the preparation of bio-, nano- and structural ceramics and composites by spark plasma sintering,” Solid State Sciences, vol. 5, no. 1, pp. 125–131, 2003.
View at: Publisher Site | Google Scholar
F. Watari, A. Yokoyama, M. Omori et al., “Biocompatibility of materials and development to functionally graded implant for bio-medical application,” Composites Science and Technology, vol. 64, no. 6, pp. 893–908, 2004.
View at: Publisher Site | Google Scholar
H. Kondo, A. Yokoyama, M. Omori et al., “Fabrication of titanium nitride/apatite functionally graded implants by spark plasma sintering,” Materials Transactions, vol. 45, no. 11, pp. 3156–3162, 2004.
View at: Google Scholar
S. Hoshii, A. Kojima, and M. Goto, “Rapid baking of graphite powders by the spark plasma sintering method,” Carbon, vol. 38, no. 13, pp. 1896–1899, 2000.
View at: Publisher Site | Google Scholar
H. Conrad, “Electroplasticity in metals and ceramics,” Materials Science and Engineering A, vol. 287, no. 2, pp. 276–287, 2000.
View at: Google Scholar
H. Yao, Y. Jin, M. H. Chen, H. Wu, N. Liu, and Q. W. Li, “Preparation and mechanical properties of carbon nanotubes reinfored Aluminum composite,” Materials Review, vol. 26, no. 18, pp. 111–115, 2012.
View at: Google Scholar
N. Ogihara, Y. Usui, K. Aoki et al., “Biocompatibility and bone tissue compatibility of alumina ceramics reinforced with carbon nanotubes,” Nanomedicine, vol. 7, no. 7, pp. 981–993, 2012.
View at: Google Scholar
W. Wang, A. Yokoyama, S. Liao et al., “Preparation and characteristics of a binderless carbon nanotube monolith and its biocompatibility,” Materials Science and Engineering C, vol. 28, no. 7, pp. 1082–1086, 2008.
View at: Publisher Site | Google Scholar
W. A. Curtin and B. W. Sheldon, “CNT-reinforced ceramics and metals,” Materials Today, vol. 7, no. 11, pp. 44–49, 2004.
View at: Publisher Site | Google Scholar
X. M. Li, Y. Yang, Y. Fan, Q. Feng, F. Cui, and F. Watari, “Biocomposites reinforced by fibers or tubes as scaffolds for tissue engineering or regenerative medicine,” Journal of Biomedical Materials Research A, 2013.
View at: Publisher Site | Google Scholar
X. Li, H. Gao, M. Uo et al., “Effect of carbon nanotubes on cellular functions in vitro,” Journal of Biomedical Materials Research A, vol. 91, no. 1, pp. 132–139, 2009.
View at: Publisher Site | Google Scholar
Q. Xu, X.-S. Zeng, and G.-H. Zhou, “Mechanical properties of CNTs/AZ31 composites prepared by adding CNTs block with plunger,” Chinese Journal of Nonferrous Metals, vol. 20, no. 2, pp. 189–194, 2010.
View at: Google Scholar
S. R. Bakshi, D. Lahiri, and A. Agarwal, “Carbon nanotube reinforced metal matrix composites: a review,” International Materials Reviews, vol. 55, no. 1, pp. 41–64, 2010.
View at: Publisher Site | Google Scholar
L. Sun, J. T. Yang, Y. Q. Shi, and M. Q. Zhong, “Dynamic mechanical properties and analysis of toughening mechanism of PA6/CNTs nano-meter composite,” China Plastics Industry, S1, 2007.
View at: Google Scholar
F. Zomer Volpato, S. L. Fernandes Ramos, A. Motta, and C. Migliaresi, “Physical and in vitro biological evaluation of a PA 6/MWCNT electrospun composite for biomedical applications,” Journal of Bioactive and Compatible Polymers, vol. 26, no. 1, pp. 35–47, 2011.
View at: Publisher Site | Google Scholar
I. T. Amr, A. Al-Amer, T. P. Selvin et al., “Effect of acid treated carbon nanotubes on mechanical, rheological and thermal properties of polystyrene nanocomposites,” Composites B, vol. 42, no. 6, pp. 1554–1561, 2011.
View at: Publisher Site | Google Scholar
Y. C. Jung, H. H. Kim, Y. A. Kim et al., “Optically active multi-walled carbon nanotubes for transparent, conductive memory-shape polyurethane film,” Macromolecules, vol. 43, no. 14, pp. 6106–6112, 2010.
View at: Publisher Site | Google Scholar
L. D. Tijing, C.-H. Park, W. L. Choi et al., “Characterization and mechanical performance comparison of multiwalled carbon nanotube/polyurethane composites fabricated by electrospinning and solution casting,” Composites B, vol. 44, no. 1, pp. 613–619, 2013.
View at: Publisher Site | Google Scholar
N. Garmendia, I. Santacruz, R. Moreno, and I. Obieta, “Zirconia-MWCNT nanocomposites for biomedical applications obtained by colloidal processing,” Journal of Materials Science, vol. 21, no. 5, pp. 1445–1451, 2010.
View at: Publisher Site | Google Scholar
W. Wang, M. Omori, F. Watari, and A. Yokoyama, “Novel bulk carbon nanotube materials for implant by spark plasma sintering,” Dental Materials Journal, vol. 24, no. 4, pp. 478–486, 2005.
View at: Google Scholar
W. Wang, F. Watari, M. Omori et al., “Mechanical properties and biological behavior of carbon nanotube/polycarbosilane composites for implant materials,” Journal of Biomedical Materials Research B, vol. 82, no. 1, pp. 223–230, 2007.
View at: Publisher Site | Google Scholar
W. Wang, Y. Zhu, F. Watari et al., “Carbon nanotubes/hydroxyapatite nanocomposites fabricated by spark plasma sintering for bonegraft applications,” Applied Surface Science, vol. 262, pp. 194–199, 2012.
View at: Publisher Site | Google Scholar
H. Aoki, Marvelous Biomaterials: Apatite, Ishiyaku Press, Tokyo, Japan, 1999.
X. Li, Y. Fan, and F. Watari, “Current investigations into carbon nanotubes for biomedical application,” Biomedical Materials, vol. 5, no. 2, Article ID 022001, 2010.
View at: Publisher Site | Google Scholar
Y. Usui, K. Aoki, N. Narita et al., “Carbon nanotubes with high bone-tissue compatibility and bone-formation acceleration effects,” Small, vol. 4, no. 2, pp. 240–246, 2008.
View at: Publisher Site | Google Scholar
N. Aoki, A. Yokoyama, Y. Nodasaka et al., “Strikingly extended morphology of cells grown on carbon nanotubes,” Chemistry Letters, vol. 35, no. 5, pp. 508–509, 2006.
View at: Publisher Site | Google Scholar
X. Li, H. Liu, X. Niu et al., “The use of carbon nanotubes to induce osteogenic differentiation of human adipose-derived MSCs in vitro and ectopic bone formation in vivo,” Biomaterials, vol. 33, no. 19, pp. 4818–4827, 2012.
View at: Publisher Site | Google Scholar
K.-H. Im, S.-B. Lee, K.-M. Kim, and Y.-K. Lee, “Improvement of bonding strength to titanium surface by sol-gel derived hybrid coating of hydroxyapatite and titania by sol-gel process,” Surface and Coatings Technology, vol. 202, no. 4–7, pp. 1135–1138, 2007.
View at: Publisher Site | Google Scholar
T. J. Webster, C. Ergun, R. H. Doremus, R. W. Siegel, and R. Bizios, “Specific proteins mediate enhanced osteoblast adhesion on nanophase ceramics,” Journal of Biomedical Materials Research, vol. 51, no. 3, pp. 475–483, 2000.
View at: Google Scholar
K. L. Elias, R. L. Price, and T. J. Webster, “Enhanced functions of osteoblasts on nanometer diameter carbon fibers,” Biomaterials, vol. 23, no. 15, pp. 3279–3287, 2002.
View at: Publisher Site | Google Scholar
A. A. Bhirde, S. Patel, A. A. Sousa et al., “Distribution and clearance of PEG-single-walled carbon nanotube cancer drug delivery vehicles in mice,” Nanomedicine, vol. 5, no. 10, pp. 1535–1546, 2010.
View at: Publisher Site | Google Scholar
C.-W. Lam, J. T. James, R. McCluskey, and R. L. Hunter, “Pulmonary toxicity of single-wall carbon nanotubes in mice 7 and 90 days after intractracheal instillation,” Toxicological Sciences, vol. 77, no. 1, pp. 126–134, 2004.
View at: Publisher Site | Google Scholar
J. Miyawaki, M. Yudasaka, T. Azami, Y. Kubo, and S. Iijima, “Toxicity of single-walled carbon nanohorns,” ACS Nano, vol. 2, no. 2, pp. 213–226, 2008.
View at: Publisher Site | Google Scholar
A. Abarrategi, M. C. Gutiérrez, C. Moreno-Vicente et al., “Multiwall carbon nanotube scaffolds for tissue engineering purposes,” Biomaterials, vol. 29, no. 1, pp. 94–102, 2008.
View at: Publisher Site | Google Scholar
F. M. Tonelli, A. K. Santos, K. N. Gomes et al., “Carbon nanotube interaction with extracellular matrix proteins producing scaffolds for tissue engineering,” International Journal of Nanomedicine, vol. 7, pp. 4511–4529, 2012.
View at: Google Scholar
R. Verdejo, G. Jell, L. Safinia, A. Bismarck, M. M. Stevens, and M. S. P. Shaffer, “Reactive polyurethane carbon nanotube foams and their interactions with osteoblasts,” Journal of Biomedical Materials Research A, vol. 88, no. 1, pp. 65–73, 2009.
View at: Publisher Site | Google Scholar
X. Li, C. A. van Blitterswijk, Q. Feng, F. Cui, and F. Watari, “The effect of calcium phosphate microstructure on bone-related cells in vitro,” Biomaterials, vol. 29, no. 23, pp. 3306–3316, 2008.
View at: Publisher Site | Google Scholar
X. Liu, X. Li, Y. Fan et al., “Repairing goat tibia segmental bone defect using scaffold cultured with mesenchymal stem cells,” Journal of Biomedical Materials Research B, vol. 94, no. 1, pp. 44–52, 2010.
View at: Publisher Site | Google Scholar
S. Garibaldi, C. Brunelli, V. Bavastrello, G. Ghigliotti, and C. Nicolini, “Carbon nanotube biocompatibility with cardiac muscle cells,” Nanotechnology, vol. 17, no. 2, pp. 391–397, 2006.
View at: Publisher Site | Google Scholar
S. Tang, Y. Tang, L. Zhong et al., “Short- and long-term toxicities of multi-walled carbon nanotubes in vivo and in vitro,” Journal of Applied Toxicology, vol. 32, no. 11, pp. 900–912, 2012.
View at: Google Scholar
G. Ahn, D. W. Seol, S. G. Pyo, and D. Lee, “Calcium phosphate cement-multi-walled carbon nanotube hybrid material (CPC-MWCNT hybrid) enhances osteogenic differentiation,” Tissue Engineering and Regenerative Medicine, vol. 8, no. 4, pp. 390–397, 2011.
View at: Google Scholar
J. Muller, F. Huaux, and D. Lison, “Respiratory toxicity of carbon nanotubes: how worried should we be?” Carbon, vol. 44, no. 6, pp. 1048–1056, 2006.
View at: Publisher Site | Google Scholar
V. L. Colvin, “The potential environmental impact of engineered nanomaterials,” Nature Biotechnology, vol. 21, no. 10, pp. 1166–1170, 2003.
View at: Publisher Site | Google Scholar
Z. Evis and R. H. Doremus, “Coatings of hydroxyapatite: nanosize alpha alumina composites on Ti-6Al-4V,” Materials Letters, vol. 59, no. 29-30, pp. 3824–3827, 2005.
View at: Publisher Site | Google Scholar
D. B. Warheit, B. R. Laurence, K. L. Reed, D. H. Roach, G. A. M. Reynolds, and T. R. Webb, “Comparative pulmonary toxicity assessment of single-wall carbon nanotubes in rats,” Toxicological Sciences, vol. 77, no. 1, pp. 117–125, 2004.
View at: Publisher Site | Google Scholar
Y. Zhang, T. Fu, Y. Han, Q. Wang, Y. Zhao, and K. Xu, “In vitro and in vivo tests of hydrothermally synthesised hydroxyapatite coating,” Biomolecular Engineering, vol. 19, no. 2-6, pp. 57–61, 2002.
View at: Publisher Site | Google Scholar
X. Li, Q. Feng, X. Liu, W. Dong, and F. Cui, “Collagen-based implants reinforced by chitin fibres in a goat shank bone defect model,” Biomaterials, vol. 27, no. 9, pp. 1917–1923, 2006.
View at: Publisher Site | Google Scholar
Z. Evis and R. H. Doremus, “Hot-pressed hydroxylapatite/monoclinic zirconia composites with improved mechanical properties,” Journal of Materials Science, vol. 42, no. 7, pp. 2426–2431, 2007.
View at: Publisher Site | Google Scholar

Copyright

Copyright © 2014 Wei Wang et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

PDF Download Citation

Download other formats

Order printed copies

Views

7697

Downloads

3052

Citations