UV-fs-LA-ICP-MS Analysis of CO2-Rich Fluid Inclusions in a Frozen State: Example from the Dahu Au-Mo Deposit, Xiaoqinling Region, Central China
Table 1
Element concentrations (ppm) in solid-free fluid inclusion assemblages (FIA) from Dahu stage I and stage III quartz.
(a) |
| | FIA | | Li | SD () | B | SD () | Na | SD () | Al | SD () | K | SD () | Ca | SD () | Mn | SD () |
| | Stage I | | Sample: DH-505-8 | | A1 | 4 | 20 | 3 (2) | 264 | 71 (4) | 21694 | 4257 (4) | NM | NM | 8417 | 1716 (4) | NM | NM | 30 | - (1) | | A2 | 2 | 88 | 19 (2) | 424 | 79 (2) | 26733 | 747 (2) | NM | NM | 7155 | 291 (2) | NM | NM | 81 | - (1) | | A3 | 3 | 235 | - (1) | 502 | 28 (3) | 27928 | 2604 (3) | NM | NM | 10086 | 1407 (3) | NM | NM | 158 | - (1) | | A4 | 2 | 31 | 10 (2) | 177 | 2 (2) | 17649 | 4808 (2) | NM | NM | 4406 | 197 (2) | NM | NM | 18 | - (1) | | A5 | 6 | 33 | 16 (4) | 172 | 52 (6) | 17875 | 2001 (6) | <2 | - (0) | 6398 | 643 (6) | <167 | - (0) | 10 | 3 (3) | | A6 | 4 | 25 | 11 (3) | 156 | 13 (4) | 15746 | 1586 (4) | NM | NM | 5887 | 567 (4) | NM | NM | <6 | - (0) | | A7 | 6 | 30 | 15 (6) | 217 | 38 (6) | 21879 | 2657 (6) | NM | NM | 6491 | 1313 (6) | NM | NM | 14 | 8 (4) | | A9 | 7 | 27 | 9 (4) | 126 | 62 (7) | 19029 | 2031 (7) | 112 | - (1) | 5439 | 616 (7) | <20 | - (0) | 22 | 7 (4) | | A10 | 4 | 19 | 2 (2) | 149 | 16 (4) | 14842 | 1980 (4) | 243 | - (1) | 6839 | 954 (4) | <47 | - (0) | 6 | - (1) | | A11 | 1 | 72 | - (1) | 251 | - (1) | 21121 | - (1) | NM | NM | 3286 | - (1) | NM | NM | <3 | - (0) | | A12 | 1 | <10 | - (0) | 169 | - (1) | 22913 | - (1) | NM | NM | 4787 | - (1) | NM | NM | 24 | - (1) | | A13 | 1 | <20 | - (0) | 357 | - (1) | 19377 | - (1) | NM | NM | 5047 | - (1) | NM | NM | <12 | - (0) | | A14 | 1 | 23 | - (1) | 164 | - (1) | 18603 | - (1) | NM | NM | 5227 | - (1) | NM | NM | 9 | - (1) | | A15 | 1 | 74 | - (1) | 145 | - (1) | 17100 | - (1) | NM | NM | 5307 | - (1) | NM | NM | <8 | - (0) |
| | Stage I | | Sample: LS-540-3B | | B1 | 4 | 531 | 273 (4) | 71 | 8 (4) | 18078 | 993 (4) | 32 | 15 | 11304 | 519 (4) | <11 | - (0) | 12 | 2 (2) | | B2 | 1 | <0.8 | - (0) | 123 | - (1) | 20609 | - (1) | <0.07 | - (0) | 10980 | - (1) | <5 | - (0) | <0.3 | - (0) |
| | Stage I | | Sample: LS-540-3C | | C1 | 4 | 84 | 6 (2) | 167 | 28 (4) | 43914 | 10113 (4) | <0.8 | - (0) | 14165 | 4390 (4) | <59 | - (0) | 25 | - (1) |
| | Stage III | | Sample: 470-F7-13D | | D1 | 6 | 47 | 4 (6) | 370 | 45 (6) | 34485 | 1309 (6) | NM | NM | 14635 | 1543 (6) | NM | NM | 25 | 12 (2) | | D2 | 7 | 44 | 7 (7) | 337 | 36 (7) | 32528 | 3648 (7) | NM | NM | 12387 | 1705 (7) | NM | NM | 28 | 1 (3) | | D3 | 13 | 45 | 12 (12) | 283 | 57 (13) | 34755 | 1408 (13) | 128 | 112 (5) | 15105 | 1089 (13) | <23 | - (0) | 11 | 12 (5) | | D4 | 8 | 47 | 6 (7) | 254 | 53 (8) | 33922 | 3565 (8) | 145 | 68 (2) | 14449 | 2761 (8) | <23 | - (0) | 3.2 | 1 (3) | | D5 | 2 | 49 | 10 (2) | 321 | 9 (2) | 34761 | 1250 (2) | NM | NM | 12905 | 570 (2) | NM | NM | 23 | - (1) | | D6 | 1 | 57 | - (1) | 339 | - (1) | 34265 | - (1) | NM | NM | 16592 | - (1) | NM | NM | <4 | - (0) |
| | Stage III | | Sample: 470-F7-13A | | E1 | 4 | 31 | 10 (4) | 130 | 77 (4) | 31373 | 3173 (4) | NM | NM | 9869 | 4386 (4) | NM | NM | 44 | - (1) | | E2 | 7 | 44 | 7 (7) | 527 | 238 (7) | 29782 | 2370 (7) | NM | NM | 12155 | 1476 (7) | NM | NM | 19 | - (1) | | E3 | 1 | 38 | - (1) | 149 | - (1) | 24203 | - (1) | NM | NM | 10355 | - (1) | NM | NM | 24 | - (1) |
|
|
(b) |
| | FIA | N | Fe | SD () | Cu | SD | Zn | SD | Rb | SD | Sr | SD | Mo | SD | Ag | SD |
| | Stage I | | Sample: DH-505-8 | | A1 | 4 | <88 | - (0) | 56 | - (1) | <7 | - (0) | 83 | 20 (4) | 16 | 5 (4) | <0.8 | - (0) | <0.6 | - (0) | | A2 | 2 | <95 | - (0) | <3 | - (0) | 63 | 9 (2) | 53 | 4 (2) | 37 | 17 (2) | <0.9 | - (0) | <0.8 | - (0) | | A3 | 3 | <114 | - (0) | <4 | - (0) | 173 | - (1) | 69 | 16 (3) | 91 | 6 (3) | <1 | - (0) | <1 | - (0) | | A4 | 2 | <53 | - (0) | <2 | - (0) | <4 | - (0) | 41 | 2 (2) | 7 | 1 (2) | <0.4 | - (0) | <0.5 | - (0) | | A5 | 6 | <40 | - (0) | 7 | - (1) | <3 | - (0) | 61 | 11 (6) | 15 | 12 (6) | <0.3 | - (0) | <0.3 | - (0) | | A6 | 4 | <70 | - (0) | 5 | - (1) | <5 | - (0) | 42 | 14 (4) | 8 | 4 (4) | <0.7 | - (0) | <0.6 | - (0) | | A7 | 6 | <53 | - (0) | <2 | - (0) | 15 | - (1) | 54 | 8 (6) | 10 | 3 (6) | <0.5 | - (0) | <0.5 | - (0) | | A9 | 7 | <32 | - (0) | <1 | - (0) | 8 | - (1) | 37 | 5 (7) | 11 | 5 (7) | <0.3 | - (0) | <0.3 | - (0) | | A10 | 4 | <55 | - (0) | <2 | - (0) | <4 | - (0) | 31 | 2 (4) | 8 | 3 (4) | <0.4 | - (0) | <0.5 | - (0) | | A11 | 1 | <33 | - (0) | <1 | - (0) | <2 | - (0) | 21 | - (1) | 4 | - (1) | <0.3 | - (0) | <0.3 | - (0) | | A12 | 1 | <64 | - (0) | <2 | - (0) | <4 | - (0) | 34 | - (1) | 9 | - (1) | <0.5 | - (0) | <0.6 | - (0) | | A13 | 1 | <139 | - (0) | <5 | - (0) | <10 | - (0) | 36 | - (1) | 21 | - (1) | <1 | - (0) | <1 | - (0) | | A14 | 1 | <45 | - (0) | <2 | - (0) | <3 | - (0) | 46 | - (1) | 11 | - (1) | <0.4 | - (0) | <0.4 | - (0) | | A15 | 1 | <95 | - (0) | <4 | - (0) | <7 | - (0) | 41 | - (1) | 13 | - (1) | <0.9 | - (0) | <0.8 | - (0) |
| | Stage I | | Sample: LS-540-3B | | B1 | 4 | <5 | - (0) | <0.6 | - (0) | <0.2 | - (0) | 35 | 2 (4) | 5 | 1 (4) | <0.03 | - (0) | <0.04 | - (0) | | B2 | 1 | <2 | - (0) | <0.2 | - (0) | <0.07 | - (0) | 70 | - (1) | 15 | - (1) | <0.01 | - (0) | <0.02 | - (0) |
| | Stage I | | Sample: LS-540-3C | | C1 | 4 | <8 | - (0) | 13 | - (1) | <0.3 | - (0) | 71 | 16 (4) | 14 | 5 (3) | <0.05 | - (0) | <0.07 | - (0) |
| | Stage III | | Sample: 470-F7-13D | | D1 | 6 | <54 | - (0) | <1 | - (0) | 58 | 28 (6) | 52 | 3 (6) | 73 | 18 (6) | <0.3 | - (0) | <0.4 | - (0) | | D2 | 7 | 104 | - (1) | 6 | - (1) | 39 | 12 (7) | 58 | 11 (7) | 76 | 14 (7) | <0.3 | - (0) | <0.3 | - (0) | | D3 | 13 | 51 | - (1) | <0.6 | - (0) | 55 | 21 (13) | 48 | 6 (13) | 62 | 39 (13) | <0.1 | - (0) | 0.4 | 0.3 (4) | | D4 | 8 | <28 | - (0) | <0.7 | - (0) | 34 | 15 (7) | 50 | 10 (8) | 40 | 11 (8) | <0.1 | - (0) | 0.4 | - (1) | | D5 | 2 | <64 | - (0) | <2 | - (0) | 52 | 7 (2) | 64 | 5 (2) | 72 | 0.1 (2) | <0.4 | - (0) | <0.5 | - (0) | | D6 | 1 | <32 | - (0) | <0.8 | - (0) | 38 | - (1) | 50 | - (1) | 60 | - (1) | <0.1 | - (0) | <0.2 | - (0) |
| | Stage III | | Sample: 470-F7-13A | | E1 | 4 | <63 | - (0) | 179 | - (1) | 13 | 3 (4) | 28 | 6 (4) | 33 | 16 (4) | <0.4 | - (0) | <0.5 | - (0) | | E2 | 7 | <98 | - (0) | <3 | - (0) | 52 | 34 (7) | 50 | 7 (7) | 38 | 25 (7) | <0.6 | - (0) | <0.8 | - (0) | | E3 | 1 | <60 | - (0) | <2 | - (1) | 21 | - (1) | 36 | - (1) | 20 | - (1) | <0.3 | - (0) | <0.4 | - (0) |
|
|
(c) |
| | FIA | | Te | SD | Cs | SD | Ba | SD | Au | SD | Pb | SD | Bi | SD |
| | Stage I | | Sample: DH-505-8 | | A1 | 4 | <5 | - (0) | 26 | 8 (4) | <1 | - (0) | <1 | - (0) | 5 | 5 (3) | <0.2 | - (0) | | A2 | 2 | <5 | - (0) | 43 | 2 (2) | 9 | 5 (2) | <1 | - (0) | 14 | 15 (2) | <0.1 | - (0) | | A3 | 3 | <6 | - (0) | 46 | 13 (3) | 44 | - (1) | <1 | - (0) | 31 | 16 (2) | <0.2 | - (0) | | A4 | 2 | <3 | - (0) | 12 | 0.1 (2) | <0.7 | - (0) | <0.6 | - (0) | 0.7 | - (1) | <0.1 | - (0) | | A5 | 6 | <2 | - (0) | 16 | 4 (6) | 1 | - (1) | <0.5 | - (0) | 2 | 1 (5) | <0.07 | - (0) | | A6 | 4 | <4 | - (0) | 11 | 3 (4) | <0.9 | - (0) | <0.8 | - (0) | 1 | 1 (2) | <0.1 | - (0) | | A7 | 6 | <3 | - (0) | 15 | 2 (6) | 1 | 1 (3) | <0.6 | - (0) | 2 | 1 (5) | <0.1 | - (0) | | A9 | 7 | <2 | - (0) | 13 | 3 (7) | <0.4 | - (0) | 1 | - (1) | 2 | 2 (4) | <0.06 | - (0) | | A10 | 4 | <3 | - (0) | 11 | 1 (4) | 3 | - (1) | <0.7 | - (0) | 0.4 | 0.03 (2) | <0.08 | - (0) | | A11 | 1 | <2 | - (0) | 9 | - (1) | <0.5 | - (0) | <0.4 | - (0) | <0.1 | - (1) | <0.1 | - (0) | | A12 | 1 | <3 | - (0) | 13 | - (1) | 3 | - (1) | <0.8 | - (0) | 1 | - (0) | <0.1 | - (0) | | A13 | 1 | <7 | - (0) | 27 | - (1) | <2 | - (0) | <2 | - (0) | <0.3 | - (1) | <0.2 | - (0) | | A14 | 1 | <3 | - (0) | 14 | - (1) | 0.9 | - (1) | <0.5 | - (0) | 1 | - (0) | <0.1 | - (0) | | A15 | 1 | <5 | - (0) | 11 | - (1) | <1 | - (0) | <1 | - (0) | <0.2 | - (1) | <0.1 | - (0) |
| | Stage I | | Sample: LS-540-3B | | B1 | 4 | <0.2 | - (0) | 7 | 1 (4) | <0.03 | - (0) | <0.05 | - (0) | <0.02 | - (0) | <0.007 | - (0) | | B2 | 1 | <0.06 | - (0) | 14 | - (1) | <0.006 | - (0) | <0.02 | - (0) | <0.005 | - (0) | <0.003 | - (0) |
| | Stage I | | Sample: LS-540-3C | | C1 | 4 | <0.2 | - (0) | 13 | 3 (4) | 34 | - (1) | <0.09 | - (0) | 8 | - (1) | <0.006 | - (0) |
| | Stage III | | Sample: 470-F7-13D | | D1 | 6 | <2.3 | - (0) | 6 | 1 (6) | 8 | 6 (6) | <0.3 | - (0) | 90 | 28 (6) | <0.1 | - (0) | | D2 | 7 | <2.0 | - (0) | 8 | 3 (7) | 10 | 7 (7) | <0.3 | - (0) | 120 | 83 (7) | <0.1 | - (0) | | D3 | 13 | <1 | - (0) | 5 | 1 (13) | 10 | 12 (10) | <0.2 | - (0) | 100 | 21 (13) | <0.04 | - (0) | | D4 | 8 | <1 | - (0) | 6 | 1 (8) | 4 | 1 (5) | <0.2 | - (0) | 68 | 43 (8) | <0.04 | - (0) | | D5 | 2 | <2.8 | - (0) | 7 | 2 (2) | 6 | 4 (2) | <0.4 | - (0) | 100 | 37 (2) | <0.1 | - (0) | | D6 | 1 | <1.4 | - (0) | 5 | - (1) | 7 | - (1) | <0.2 | - (0) | 88 | - (1) | <0.1 | - (0) |
| | Stage III | | Sample: 470-F7-13A | | E1 | 4 | <3 | - (0) | 5 | 1 (4) | 2 | 1 (4) | <0.4 | - (0) | 22 | 10 (4) | <0.1 | - (0) | | E2 | 7 | <4 | - (0) | 13 | 4 (7) | 5 | 3 (6) | <0.5 | - (0) | 39 | 16 (7) | <0.1 | - (0) | | E3 | 1 | <3 | - (0) | 8 | - (1) | 3 | - (1) | <0.3 | - (0) | 19 | - (1) | <0.1 | - (0) |
|
|
= number of analyzed inclusions, = number of significant concentrations, NM = not measured, and SD = standard deviation. |